多层膜界面粗糙度的低角X射线衍射研究

对磁控溅射方法制备的Ｗ／Ｓｉ周期多层膜在Ｘ射线衍时仪上进行了低角Ｘ射线衍射实验，并用动力学理论分析了膜层的周期结构和界面粗糙度，在对实验谱线的拟合过程中，考虑了界面的不对称性、周期的随机涨落及系统偏差等因素对衍射强度的影响，并讨论了各个参量对衍射强度影响的程度．     

EFFECT OF INITIAL CRYSTALLIZATION ON MAGNETIZATION OF METALLIC GLASSES(Fe_(1-x)Co_x)_(78)Si_(10)B_(12)

<正> 文献[1]曾对金属玻璃(Fe_(1-x)Co_x),_(78)Si_(10)B_(12)的晶化,作过X射线衍射和透射电镜研究,指出初期晶化相为相应晶态Fe_(1-x)Co_x的室温平衡相.本工作将在验证这一结论的基础上,研究初期晶化对一定磁场强度下磁化强度(定场磁化)的影响。 一、样品和实验方法 成分为(Fe_(1-x)Co_x)_(78)Si_(10)B_(12)(x=0.1,0.5,0.7,1)的合金用单辊快淬法制成截面为～1×0.3mm的金属玻璃窄带,用示差扫描热分析法测定其晶化温度T_(cr)(升温速率10℃/min)分别为505,490,440和420℃.磁性试样在石英管式炉中依次进行退火,退火温度T_a=350-500℃,除了x=0.7的样品在T_a≥450℃退火10min外,T_a≤450℃退火20min,     

奥氏体Fe-Mn合金的低温脆性

奥氏体型合金一般具有优良的低温韧性.本文对奥氏体Fe-Mn合金低温变脆现象进行了研究.实验结果肯定了低温下有冷脆倾向;指出随Mn含量增多,冷脆转变温度增高,呈沿晶脆断;发现Mn沿晶界偏聚,且Mn含量愈高偏析程度愈大;初步分析了晶界Mn富集造成冷脆的因素;未能证实前人提到的可能引起低温变脆的-100℃时面心立方→面心四方相变的存在.     

阴极保护对低合金钢在海水中断裂行为的影响

本文系统地研究了AISI4340,HY100,WELTEN60,AISIA537和A131低合金钢在开路和阴极保护电位下海水中的应力腐蚀开裂(SCC)和腐蚀疲劳(CF)行为.试验结果表明,阴极保护可以使合金钢在海水中不发生SCC的界限强度降低;而对低合金钢在海水中CF裂纹扩展速率的影响则不是单一的,与其强度及SCC的行为密切相关.指出在海洋工程结构中,应尽可能把阴极保护电位控制在规定区域的上限,同时可把海洋平台用钢的强度提高200—300MPa     

高过冷度Zr-Cu-Ni-Al-Hf-Ti块体非晶合金

以Hf和Ti作为替换元素对Zr60Cu20Nil0Al10非晶合金进行了掺杂(替换法)研究．结果表明，掺杂元素含量有一最佳范围，其中，Ti的最佳含量约为2％(原子分数)左右，而Hf的最佳含量为3％．在最佳含量时二者都具有明显的扩大合金过冷温度区间ΔTx的作用．超过最佳掺杂量，会使非晶相变得不稳定，促进某些晶化相的形成，从而降低ΔTx．当采用Hf和Ti两种元素的最佳含量联合掺杂时，稳定非晶相的作用更加明显，并且ΔTx提高的幅度大于两种元素单独掺杂时的效果．ΔTx最大(144℃)的成分为：Zr60Cu20Ni8Al7Hf3Ti2，该合金Tg＝357℃，Tx＝501℃，Trg＝0．59．     

金属-类金属非晶态合金的菱面体单元结构模型与形成能力的关系

进一步发展了非晶态合金菱面体单元结构模型的概念，认为不仅存在（２∶１）菱面体单元结构，而且存在（１∶１）菱面体单元结构和（４∶１）菱面体单元结构。通过计算上述几种结构的金属类金属键与类金属含量的关系曲线，发现其变化趋势和实验得到的非晶态合金形成能力与类金属含量的关系曲线一致，因而所提出的几种菱面体单元结构模型得到实验支持     

Numerical studies on the stress distribution in weldbonded joints with different adhesives

The Effect of elastic modulus and thickness of the adhesives on the stress distribution in weldbonded joints hasbeen studied with three-dimensional elastoplastic finite element method (FEM). Stress distribution curves have beenobtained at the edges of the spot welds and the lap zones in weldbonded joints, which werem made with adhesives ofdifferent elastic modulus or different thickness. Results show that there exists larger stress concentration at the edge of thespot Welds, though the shear stresses in the adhesive layers are smaller for weldbonded joints with low elastic modulus orthick adhesive layers. the stress concentration decreases and the shear stresses in adhesive layers increase with the increaseof the elastic modulus or the decrease of the adhesive thickness. It is concluded that the thiner adhesive layers with higherelastic modulius are preferable in weldbonded joints to cut down the stress concentration.     

Ti对Ml(NiCoMnTi)_5合金相结构和充放电循环性能的影响

研究了微量 Ｔｉ在 Ｍｌ（ＮｉＣｏＭｎＴｉ）５合金中的作用．结果表明,在铸态条件下,Ｔｉ几乎全部以 ＴｉＮｉ３第二相的形式在晶界析出,退火处理后 ＴｉＮｉ３相消失,但 ＳＥＭ和 ＥＤＳ表明 Ｔｉ取代了 ＡＢ５型化合物中 Ａ侧的稀土 Ｍｌ;而不是 Ｂ侧的 Ｎｉ．Ｔｉ在 Ａ侧的取代量以 ５％为宜．此时合金在铸态和退火态的放电容量都在 ３１０ ｍＡ·ｈ／ｇ以上．进一步提高取代量虽然会改善循环稳定性,但大大降低了放电容量．     

机械合金化合成NiAl/HfB_2复合材料的组织与力学性能

球磨Ｎｉ,Ａｌ;Ｈｆ和Ｂ元素粉末反应合成ＮｉＡｌ／ＨｆＢ２复合材料,形成机制归结为机械碰撞诱发的自蔓延反应．采用 热压和热等静压工艺将纳米双相复合粉末压制成较密实的块体材料,进而研究其微观组织与力学性能．结果表明“反应球磨＋热 压”制备的ＮｉＡｌ／ＨｆＢ２复合材料基体晶粒细小,原位生成的弥散相颗粒主要分布于基体晶界,其强化效果显著而对塑性的削弱 作用较小;不同温度下的压缩屈服强度均远高于铸态ＮｉＡｌ,且压缩变形量均超过１０％;高温下材料的屈服强度依赖于应变速率, 用线性回归方法计算出的应力指数ｎ和变形激活能Ｑ高于单相ＮｉＡｌ,与含弥散相比例较高的ＸＤ ＮｉＡｌ－２０％ＴｉＢ２（体积分数） 复合材料相当．     

人工神经网络技术在电阻点焊质量控制中的应用

介绍了９０年代以来国内外关于人工神经网络技术在电阻焊点焊质量控制和无损检测中应用的研究。并对其发展趋势作了分析和展望。