Preliminary<Emphasis Type="Italic">in vitro</Emphasis> and<Emphasis Type="Italic">in vivo</Emphasis> characterizations of a sol-gel derived bioactive glass-ceramic system

This study investigates quantitatively and qualitatively the sol-gel derived bioactive glass-ceramic system (BGS)—apatite-wollastonite (AW) type granules in the size range of 0.5–1 mm, as an effective graft material for bone augmentation and restoration. Scanning electron micrographs (SEM) of the sintered granules revealed the rough material surface with micropores in the range 10–30 μm. X-ray diffraction (XRD) pattern of the granules revealed the presence of crystalline phases of the hydroxyapatite and wollastonite, and the functional groups of the silicate and phosphates were identified by Fourier transform infrared spectroscopy (FT-IR). Thein vitro cell culture studies with L929 mouse fibroblast cell line showed very few cells adhered on the BGS disc after 24 h. This could be due to the highly reactive surface of the disc concomitant with the crystallization but not due to the cytotoxicity of the material, since the cellular viability (MTT assay) with the material was 80‰ Cytotoxicity and cytocompatibility studies proved that the material was non-toxic and biocompatible. After 12 weeks of implantation of the BGS granules in the tibia bone of New Zealand white rabbits, the granules were found to be well osteointegrated, as observed in the radiographs. Angiogram with barium sulphate and Indian ink after 12 weeks showed the presence of microcapillaries in the vicinity of the implant site implicating high vascularity. Gross observation of the implant site did not show any inflammation or necrosis. SEM of the implanted site after 24 weeks revealed good osteointegration of the material with the newly formed bone and host bone. New bone was also observed within the material, which was degrading. Histological evaluation of the bone healing with the BGS granules in the tibial defect at all time intervals was without inflammation or fibrous tissue encapsulation. After 2 weeks the new bone was observed as a trabeculae network around the granules, and by 6 weeks the defect was completely closed with immature woven bone. By 12 weeks mature woven bone was observed, and new immature woven bone was seen within the cracks of the granules. After 24 weeks the defect was completely healed with lamellar bone and the size of the granules decreased. Histomorphometrically the area percentage of new bone formed was 67.77% after 12 weeks and 63.37% after 24 weeks. Less bone formation after 24 weeks was due to an increased implant surface area contributed by the material degradation and active bone remodeling. The osteostimulative and osteoconductive potential of the BGS granules was established by tetracycline labelling of the mineralizing areas by 2 and 6 weeks. This sol-gel derived BGS granules proved to be bioactive and resorbable which in turn encouraged active bone formation.     

Residual Stress Simulation of Injection Molding

In this study, distribution and history of residual stresses in plaque-like geometries are simulated based on linear thermoviscoelastic model, which helps to understand the mechanics and evolution of the residual stresses in the injection molding process. The numerical calculation of direction, combined with the specified boundary conditions. Results show that the stress variation across the thickness exhibits a high surface tensile value changing to a compressive peak value close to the surface, with the core region experiencing a parabolic tensile peak. Residual stress distribution throughout the thickness is almost same along the flowpath and the final residual stresses value near the gate is lower than the value near the end of flowpath.     

Kinetics of chlorination of tantalum pentoxide in mixture with sucrose carbon by chlorine gas

The mechanism and kinetics of β-Ta₂O₅ chlorination, mixed with sucrose carbon, have been studied by a thermogravimetric technique. The investigated temperature range was 500 °C to 850 °C. The reactants and reaction residues were analyzed by scanning electronic microscopy (SEM), X-ray diffraction (XRD), and Brunauer-Emmett-Teller method for surface area (BET). The effect of various experimental parameters was studied, such as carbon percentage, temperature, chlorine partial pressure, and flow, use of the multiple sample method, and carbon previous oxidation. The carbon percentage and previous treatment have an effect on the system reactivity. The temperature has a marked effect on the reaction rate. In the 500 °C to 600 °C temperature interval, the apparent activation energy is 144 kJ/mol of oxide, while at higher temperatures, the activation energy decreases. With high chorine partial pressures, the order of reaction is near zero. The kinetic contractile plate model, X=kt, considering carbon oxidation as the controlling stage, is the one with the best fit to the experimental data. A probable mechanism for the carbochlorination of β-Ta₂O₅ is proposed: (1) activation of chlorine on the carbon surface, (2) chlorination of Ta₂O₅, (3) oxidation of carbon, and (4) recrystallization of β-Ta₂O₅.     

Complete oxidation of methane at low temperature over Pt and Pd catalysts for the abatement of lean-burn natural gas fuelled vehicles emissions: influence of water and sulphur containing compounds

The catalytic activity of fresh Pd and Pt catalysts supported on γ-alumina in the complete oxidation of CH₄ traces under lean-burn conditions was studied in the presence or the absence of water or H₂S. Steam-aged catalysts were also studied in order to simulate long-term ageing in real lean-burn natural gas fuelled vehicles (NGVs) exhaust conditions. Without water or H₂S added to the feed, Pd catalysts exhibit a superior catalytic activity in methane oxidation compared to Pt ones, whatever the catalysts were fresh or aged. The addition of 10 vol.% water vapour to the feed strongly affects the activity of the fresh Pd catalyst, thus being only slightly more efficient than the fresh Pt one. H₂S has a strong poisoning effect on the catalytic activity of Pd catalysts, while Pt catalysts are more resistant. The fresh H₂S-poisoned Pd/Al₂O₃ catalyst was studied by TPD in O₂/He. Poisoning species decompose above 873 K as SO₂ and O₂ in relative concentrations consistent with the decomposition of surface sulphate species. However, a treatment in O₂/He at temperatures as high as 923 K does not allow the complete regeneration of the catalytic activity of H₂S-poisoned Pd/Al₂O₃. A mechanism involving the poisoning of PdO by sulphate species is proposed. Different diffusion processes by which these sulphate species can migrate back and forth between PdO and the support, depending on the experimental conditions, are suggested.     

The evolution of government housing policy: The case of new south Wales 1901–41

This paper sets out the development of four main threads of housing policy in New South Wales from the latter part of the 19th century through the first 40 years of the 20th century. Following a discussion of the social and political circumstances and debate surrounding government policy regarding landlord/tenant relations, housing quality and supply, and owner occupancy, it concludes that policy evolution is irregular and a product of the exigencies of the political process. It also suggests that although government policy did little to improve the housing situation for the underprivileged, there was nevertheless a growing acceptance by both Labor and conservative parties of the increased need for government intervention in the housing market.