防止氟化铝母液脱硅工艺中铝、氟消耗方法研究

在氟化铝母液中添加氯化铝等可溶性铝盐,可有效地阻止钠,氟,铝间冰晶石固体物质的形成,从而达到防止氟化铝脱硅工艺中铝,氟的损耗,确保氟硅酸钠的产品质量,同时提高母液利用的经济效益。     

热塑性聚酰亚胺的热膨胀系数研究

利用静态热机械分析仪（TMA）测定了热塑性聚酰亚胺（TPI）注塑件的热膨胀系数α，考察了TPI的各向异性、尺寸稳定性以及添加不同填料对α的影响。结果表明：TPI存在着各向异性，且流向面的α最低。在正常的使用范围内，试样经历一个升降温循环后尺寸基本没发生变化。经消除热历史后，材料的α降低；类似地，热处理也能使。减小。在主链相同的TPI树脂中，加入玻纤、碳纤维等高强度、高热稳定性的填料有助于降低TPI的α。     

压挤成形--固化法制备0-3型压电复合材料的性能研究

详细地叙述了室温压挤成形———固化工艺制备 0 -3型压电复合材料工艺 ,使用XRD、SEM和HP42 94测试并分析了样品的结构和性能 ,并与压电陶瓷性能参数进行了对比 ;同时用这种工艺制备可以获得介电损耗小、机电耦合系数为 2 5 .11%、压电应变常数为 3 2PC N和机电品质因数可达到 3 0 2的 0— 3型压电复合材料。     

Chemical and experiential basis for rejection ofTropaeolum majus byPieris rapae larvae

Rejection of nasturtium,Tropaeolum majus, by cabbage-reared larvae ofPieris rapae has been explained by the presence of feeding deterrents in the nastrutium foliage. Sensitivity to the deterrents develops as neonate larvae feed on cabbage. The most prominent deterrent compound, which is present in nasturtium at a concentration of 40 mg/100 g fresh leaves, was identified as chlorogenic acid. When neonate larvae were fed on a cabbage leaf treated with high concentrations of deterrent-containing extracts of nasturtium foliage, they remained insensitive to the deterrents, so they accepted nasturtium when transferred as second instars. When neonate larvae were reared on a cabbage leaf treated with 0.1 mg chlorogenic acid, ca. 35% of the second instars accepted nasturtium. Similar dietary exposure of neonates to the subunits of chlorogenic acid, caffeic acid and quinic, acid resulted in much less or no effect on the rejection behavior of second instars. The results suggest that the combined effects of specific chemical constituents of nasturtium can explain the rejection of this plant by larvae ofP. rapae, but if larvae are continuously exposed to these compounds immediately after hatching, they apparently become habituated to the feeding deterrents. The lack of activity of the subunits of chlorogenic acid suggests that specific structural features are necessary for a dietary constituent to cause such habituation or suppression of sensitivity development.     

1—苯基—5—巯基四氮唑和苯并三氮唑在胶态银和硫化银上的阳极抑制效应

为了研究抑制剂对银核和硫化银核的不同作用，本工作考察了1－苯基－5－巯基四氮唑（PMT）和苯并三氮唑（BTA)作为抑制剂在银核和硫化银核上物理显影的阳极抑制和解抑制效应。实验结果表明：1）PMT和BTA对Ag核和银离子过量时制得的硫化银核，Ag2S(Ag)，的显影催化活性都有不同程度的抑制作用，而对硫离子过量时制得的硫化银核，Ag2S(S)，无明显的抑制作用，这可能是由于过量硫离子在硫化银核上的吸附要强于这两种抑制剂；2）S2O3^2-或I^-离子的存在对BTA在Ag核上有解抑制作用，不仅可恢复甚至提高Ag核的显影催化活性，而对Ag2S核的抑制作用无明显影响；3）与BTA不同，S2O3^2-或I^-离子对PMT在Ag核上没有解抑制作用，对Ag2S(Ag)核的抑制作用还稍有增强，而对Ag2S(S)核稍有减弱；4）银溶胶中的表面增强拉曼谱（SERS）测量证实：BTA在Ag核上的吸附导致Ag核显影催化活性的下降，加入S2O3^2-或I^-离子后致使BTA的SERS信号消失则意味着BTA在银核表面的脱附。以上这些结果说明阳极抑制机理在抑制效应中有重要作用。     

日本钢管福山焦化厂简介

介绍了福山焦化厂备煤、炼焦和化产回收系统的工艺及设备情况,并对煤调湿及干熄焦部分作了详述。     

Investigation on the early and late stage phase-separation dynamics of poly(methyl methacrylate)/poly(α-methyl styrene-co-acrylonitrile) blends through rheological and scattering functions

The phase-separation behavior of poly(methyl methacrylate)/poly(α-methyl styrene-co-acrylonitrile) (PMMA/α-MSAN) blends with two different compositions was studied by time-resolved small angle light scattering (SALS) in the spinodal decomposition (SD) regime from 160 to 210 °C. The rheological function (WLF-like equation) was introduced into the processing of light scattering data. It was found that the WLF-like equation was applicable to describe the temperature dependence of apparent diffusion coefficient D_app and the relaxation time τ of normalized scattering intensity (I(t)−I(0))/(I_m−I(0)) at the early stage of SD, as well as the relaxation time τ of maximum scattering intensity I_m and characteristic scattering vector q_m with I_m at the late stage of SD for PMMA/α-MSAN blends with two different compositions. This is in consistence with the phase-separation behavior of PMMA/SAN reported in our previous paper.     

双核酞菁钴磺酸铵用于催化裂化汽油的脱臭

采用尿素法合成了双核酞菁钴磺酸铵;通过正交实验及单因素实验,考察了双核酞菁钴磺酸铵在液-液催化氧化法中对催化裂化汽油脱臭的最佳工艺条件:碱液质量分数为10%,催化剂加入量为1 0g·L-1,反应温度为40℃,反应时间为3min;与磺化酞菁钴和美国进口脱臭催化剂ARI100-EXL的脱硫醇效果进行了比较,结果表明双核酞菁钴磺酸铵对汽油的脱臭效果明显优越于磺化酞菁钴催化剂,与进口催化剂的脱臭效果基本相当。     

Synthesis, characterization and thermal properties of hexaarmed star-shaped poly(ε-caprolactone)-b-poly(d,l-lactide-co-glycolide) initiated with hydroxyl-terminated cyclotriphosphazene

Hexakis[p-(hydroxymethyl)phenoxy]cyclotriphosphazene was prepared by the reaction of hexachlorocycltriphosphaneze with the sodium salt of 4-hydroxybenzaldehyde and subsequent reduction of aldehyde groups to alcohol groups by using sodium borohydride. Hexaarmed star-shaped hydroxyl-terminated poly(ε-caprolactone) (PCL) were successfully synthesized via ring-opening polymerization of ε-caprolactone (CL) with the above hydroxyl-terminated cyclotriphosphazene initiator and stannous octoate catalyst in bulk. The number-average molecular weight of PCL linearly increased with the molar ratio of monomer to initiator. The star-shaped PCL with hydroxy end groups could be used as a macroinitiator for block copolymerization with d,l-lactide (d,l-LA) and glycolide (GA) using stannous octoate catalyst. IR, ¹H NMR and GPC analysis showed the star-block copolymers were successfully synthesized and the molecular weights and the unit composition of the star-shaped block copolymers were controlled by the molar ratios of d,l-LA and GA monomers to CL. The copolymer presented a two-phase structure, namely, PCL crystalline and d,l-LAGA amorphous domains, which made the copolymer different from linear PCL and star-shaped PCL in crystallinity and thermal behaviors.     

扫描仪面框注塑件翘曲变形的模拟分析

以扫描仪面框薄壁件注塑成型为例，应用Moldflow软件分析了模具温度、熔体温度、浇口位置和保压参数对翘曲变形的影响规律，提出了减小翘曲变形的工艺措施，分析结果与生产实际吻合。