气膜片胀形模结构的改进

分析了气膜片零件胀形质量差的原因，对原模具结构进行了改进，解决了原模具成形后贴模不理想、型面不准确的问题，提高了零件质量。     

超细WC粉末的强化球磨和表面钝化

研究了超细WC球磨破碎和分散机理,通过表面活性剂和聚合物的添加,降低了超细WC的球磨料浆粘度,提高了WC的球磨效率;经过150小时球磨后WC的BET小于100nm,X衍射晶粒度小于30nm。WC表面聚合物包覆的物理改性,其抗氧化能力提高了一倍。     

TiAl/Ti/V/Cu/40Cr钢扩散连接界面组织结构对接头强度的影响

研究了TiAl/Ti/V/Cu/40Cr钢的扩散连接，结果显示：在TiAl/Ti界面处形成了对接头强度有利的Ti3Al TiAl双相层及Ti固溶体层，而Ti/V/Cu/40Cr界面处未出现金属间化合物及其它脆性相，接头最高拉伸强度可达420MPa，接近TiAl母材。     

Investigations in the compaction and sintering of large ceramic parts

In this study, a large ceramic part was successfully compacted and sintered using uniaxial die compaction technique. The effects of die design, compaction pressure, lubrication, sintering procedure and part orientation in the oven on the P/M part quality were investigated and the preferred process conditions were discussed and concluded. The main quality issues encountered were cracking and distortion. A finite element model for the powder compaction process was also developed and validated. Based on the model, the relationship between the cracking location and the density distribution predicted from finite element analysis (FEA) was discussed.     

T91与1Cr18Ni9Ti异种钢焊接

T91钢是国外为提高火力发电机组的效率而研制的一种高合金耐热钢,它是完成超临界发电机组主蒸气参数由566℃向593℃过渡的关键材料.针对马氏体耐热钢(T91)与奥氏体钢(1Cr18Ni9Ti)的物理化学性能,分析了该异种钢的焊接性.通过在湘潭电厂二期工程中具体应用表明,采取适当的焊前预热及焊后热处理的措施,选取合适的焊接材料和焊接工艺参数,能够获得性能优良的焊接接头.     

Direct laser fabrication of thin-walled metal parts under open-loop control

Direct laser fabrication (DLF) is an advanced manufacturing technology, which can build full density metal parts directly from CAD files without using any modules or tools. The investigation on the fabrication of thin-walled parts of nickel alloy using open-loop DLF process is introduced in this paper. The experimental setup consisted of a CO₂ laser, a 3-axis CNC table, a coaxial powder nozzle and a powder recycler. The 3D-CAD file of a thin-walled metal part was converted into the STL file format and imported into software HUST-RP to generate ‘pseudo-random’ scanning paths of laser beam. The influence of process parameters on the build height of thin-walled metal parts was studied by 1–10 layered single-bead stacks of nickel alloy. The result shows that the interference factors which affect the build height of thin-walled metal parts occur randomly during the process. For open-loop DLF process, thin-walled metal parts can achieve much better shape quality if the process parameters are suitable. Multilayer single-bead walls were built up with different scanning velocity to obtain the optimal process parameters of thin-walled parts of nickel alloy. It shows that thin walls of nickel alloy with uniform height can be built up layer by layer in a certain range of specific energy. However, it is difficult to control the build height of complex thin-walled metal parts in an accurate manner just using optimal parameters. A special coaxial powder nozzle was designed in this paper. In a certain range, the deposition thickness of the nozzle is nearly linearly increased with increase in the standoff distance between the powder focusing point of the nozzle and the deposition substrate. By means of the nozzle, a novel method to control the build height of thin-walled metal parts using open-loop DLF process was introduced. The difference in build height of a thin-walled part can be compensated automatically in one or several layers during the process. It is proved that the build height of a thin-walled metal part can be accurately controlled in theory using the nozzle. A complex single-bead part of nickel alloy whose geometry was designed to be the well-known Chinese ‘FU’ was fabricated and explained in this paper. The result shows that the shape quality of the sample is quite good, and actual build height of the sample is 53.54 mm while the designed value is 54 mm.     

热处理对Mg-Li-Zn-Zr系镁合金组织及性能影响

研究了Mg-Li-Zn-Zr镁合金和添加钇、镧错铈混合稀土的Mg-Li-Zn-Zr-Y-LPC镁合金的显微组织和力学性能特点．以及热处理对两种镁锂合金显微组织和力学性能的影响规律。结果表明：铸态Mg-7．13Li-3．92Zn-1Zr合金主要由α-Mg相．θ′相（MgLi2Zn）组成；添加混合稀土后，铸态Mg-8．16Li-4．10Zn-2．86Y-0.59Zr-2．14LPC合金主要由Li、Zn和RE在Mg中的固溶体和Mg-Li-Zn-RE块状化合物共同组成。对铸态Mg-Li-Zn-Zx合金均化处理后，合金的θ′相转变为更为稳定的θ相（MgLiZn），并且均化处理可以明显提高铸态Mg-7．13Li-3．92Zn-1Zt合金的力学性能。另外，氢化处理也可以明显提高铸态Mg-Li-Zn-Y-Zr-LPC合金的力学性能。     

管线钢多丝埋弧焊烧结焊剂焊接工艺性能研究

对管线钢用多丝埋弧焊烧结焊剂主要组分对焊接工艺性能的影响规律进行了试验研究．在此基础上研制出一种基于MgO-CaF2-Al2O3-SiO2-MnO-ZrO2渣系、碱度BⅡw在1．2～1．5之间的新型烧结焊剂。试验表明．该焊剂在多丝埋弧焊时具有良好的焊接工艺性能，焊接接头各项力学性能均能满足X70级管线钢的焊接要求。     

马鞍形板材件多点“三明治”成形实验研究

多点“三明治”成形是一种针对小批量多曲率板材工件制造而提出的新成形方法。用该方法成形时,上模采用聚氨酯模具,下模为型面可调节的多点模具。为了使多点模具型面连续化和消除工件表面的压痕,在成形过程中使用了金属护板和弹性垫板。由于工件板材两侧都和聚氨酯相接触,因此成形后工件的表面质量好。为了研究采用多点“三明治”成形复杂三维曲面工件的成形过程以及成形可能会出现的表面缺陷,文章选用马鞍面作为目标形面进行了实验研究,提出了用于提高工件的贴模程度,通过改变上模形状的分步成形方法,并得到了Q235B板材厚度和可成形马鞍形工件深度之间的关系曲线。     

板料成形数值模拟的关键技术及难点

本文结合国内外板料成形数值模拟的最新研究动态，从关键算法、屈服函数、本构方程、有限元列式、接触问题、破裂准则、回弹计算、起皱分析八个方面叙述了板料成形有限元计算的关键技术及主要难点。