Is the List of Incomplete Open Cubes Complete?

Variations of Incomplete Open Cubes is the major project by the twentieth-century conceptual artist Sol LeWitt. In this paper we interpret the enumerative component of the project as embeddings of graphs. This formulation permits use of an algorithm to check the completeness of the list of the structures produced by the artist. Our conclusion is that the artist found the correct number of structures (that is, 122), but that his list contains a mistake in the presentation of a pair of incomplete cubes, a discovery that appears not to have been noted before.     

Super-oleophilicity Co-doping Co2+/F-/TiO2 one-dimensional nanotubes for photocatalytic denitrification of light oil

In this study, a simple hydrothermal synthesis method was adapted for the preparation of Co-doping Co²⁺/F^-/TiO₂ nanotubes photocatalyst, and the micro-nano structure of catalysts prepared by biomimetic technology which makes the catalyst have super-oleophilicity property. Co²⁺/F^-/TiO₂ revealed improved photocatalytic performance for denitrification of light oil compared to single TiO₂ photocatalysts. The enhance of photocatalytic activity can be attributed to narrowing the band gap, increasing the light response wavelength and exposing more highly active crystal surfaces due to synergistic effects of Co²⁺ and F^? in the photocatalyst.     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.     

黄浦江下游吴淞口站低潮位重现期研究

黄浦江为感潮河流,低潮位重现期的确定对黄浦江航道的设计具有重要意义。为了准确估计黄浦江低潮位的重现期,以黄浦江下游吴淞口站年最低潮位序列为例,在对样本进行三性审查的基础上,分别采用传统的数理统计方法和时变矩方法进行水文频率分析。结果表明:吴淞口站年最低潮位序列在1996年发生了变异;还现修正后的序列服从位置参数线性时变的GEV模型,低潮位存在缓慢的上升趋势;一致性条件下百年一遇低潮位约为0.261 m,在非一致性条件下其重现期增大为150 a。非一致性条件下的重现期增大说明黄浦江现有的航道设计标准偏安全,航道通航保证率提高。     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.