近年来,基于特殊润湿性理论制备表面具有微纳米粗糙结构的多孔材料成为油水分离领域研究的重点。为了满足不同环境下对不同形式油-水乳状液高效高通量分离的需求,该研究利用纳米SiO2颗粒对聚丙烯（PP）纤维棉有针对性地亲（疏）水改性,构建了系列不同润湿性和粗糙度的PP纤维棉,探究了不同孔隙度和表面能的PP纤维棉对W/O及O/W型乳状液的分离性能,结果表明,经过亲（疏）水改性后的PP纤维棉对水/正己烷和水/甲苯乳状液的分离效率都高于99.5%,通量高于700 L/(m2·h),并针对不同形式油-水乳状液阐释其相应的分离机制,为后续油-水乳状液分离材料的科学设计和可控制备提供了理论依据。     

Highly Uniform and Stable Transparent Electromagnetic Interference Shielding Film Based on Silver Nanowire–PEDOT:PSS Composite for High Power Microwave Shielding

Electromagnetic interference (EMI) shielding materials, especially ones with excellent shielding effectiveness (SE), high optical transmittance, long-term stability as well as high uniformity, are urgently desired to meet the requirements of many applications. Herein, an extremely transparent, stable and uniform silver nanowire (Ag NW)–poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) composite film as an EMI shielding material is prepared, which possess excellent shielding capability to both small signal and high power microwaves (HPM). The composite film exhibits SE of 30.5 dB in the frequency range of 1–12 GHz (small signal) and simultaneously has an optical transmittance of 91.0%. The SE continuously increases to 41.4 dB, while the optical transmittance still maintains at 81.1%. The composite film is very uniform, and its SE is almost unchanged even when exposed in air for a year. The SE of this composite film under the excitation of HPM is also thoroughly investigated. The HPM SE is much larger than that of small signal. As the power density of HPM is increased, the SE firstly remains unchanged, then continuously increases, and finally saturates. The SE exceeds 50 dB with the excitation power density of 40 W. More interestingly, the SE is saturated at a fixed HPM power density.     

Importance of Low-Temperature Melt-Mixing on the Construction of Stereocomplex Crystallites with Superior Nucleation Efficiency in Asymmetric Poly(l-lactide)/Poly(d-lactide) Blends

The nucleation efficiency (NE) of stereocomplex crystallites (SCs) formed in asymmetric poly(L-lactide)/poly(D-lactide) (PLLA/PDLA) blends is generally unsatisfactory because the competition between stereocomplexation and chain mixing involved in the melt-mixing process can cause low formation efficiency and even severe aggregation of SCs. Herein, it is attempted to achieve high-efficient formation of finely dispersed SCs particles by designing a unique melt-mixing procedure, where the mixing of PLLA with 0.75 wt% PDLA is first performed at elevated temperatures (far above the melting temperature of SCs) to allow the homogeneous mixing of PLLA/PDLA chains and then at a low temperature (slightly above that of homocrystallites) to permit the full stereocomplexation of the premixed chains. It is found that the SCs formed in the blends exhibit unexpectedly low NEs (e.g., 54.5%), much inferior to that (73.6%) in the counterpart without undergoing premixing. This is because the introduction of premixing leads to a remarkable deterioration in the amount of SCs particles formed, despite decreased particle size, highlighting that the direct mixing at low temperatures of 170–180 °C (about 20–30 °C lower than that used in common melt-processing of PLA) is more effective for the construction of SCs with superior NE. The mechanisms for these striking findings are discussed.     

Effect and Evolution of Oxide Film in the HDH-Ti Powder Surface on Densification Behavior During Sintering

Metallurgical and Materials Transactions A - In this work, we used hydride-dehydride Ti (HDH-Ti) powders (with the oxygen levels of 0.17 and 0.51 wt pct, respectively) combined with microstructural...     

地聚合物混凝土配比及力学性能研究

混凝土是巷道支护过程中的重要建筑材料,然而混凝土在巷道施工中常常出现质量问题,为了不影响正常生产,需要对其进行修补。地聚合物混凝土凝结时间快,早期强度高,界面结合能力强,耐高温性和抗冻性强,耐腐蚀性良好,具有用作修补材料的潜力。以粉煤灰和矿粉为原料,Na₂SiO₃溶液和NaOH为碱激发剂制备地聚合物胶砂,研究不同的碱激发剂模数（1.0、1.2、1.4）和掺量（10%、15%、20%）对不同龄期胶砂力学性能的影响。结果表明：当碱激发剂模数为1.2,碱掺量为15%时,胶砂强度达到最大值。设计正交试验,研究了不同水胶比（0.45、0.50、0.55）、粉煤灰掺量（30%、50%、70%）和砂率（30%、35%、40%）对不同龄期地聚合物混凝土的工作性能和力学性能的影响。结果表明：粉煤灰掺量对抗压强度影响最为显著,水胶比次之,而砂率对强度发展几乎没有影响。最优的配合比为水胶比为0.50,粉煤灰掺量为50%,砂率为35%。     

纳米Ti（CN）基金属陶瓷烧结过程中的结构和相变

用分段真空烧结、X射线衍射和背散射扫描电镜研究了纳米Ti（CN）基金属陶瓷在烧结过程中的结构和相成分的演变。结果表明：纳米Ti（CN）基金属陶瓷在900℃以后，Mo2C和TaC开始由于扩散，与Ti（CN）发生固溶反应，在1200℃以前，Mo2C和TaC固溶反应结束，两相均消失。WC在1100℃以后，开始由于扩散，与Ti（CN）发生固溶反应，在1250℃以前消失。在1250℃以后，合金中只有Ti（CN）和Ni（Ni＋Co）两相存在。纳米Ti（CN）粉末与M（M=Mo，W．Ta）反应形成富M的（Ti，M）（CN）固溶体为核，贫M的（Ti，M）（CN）固溶体为环的“亮芯黑环”环形结构，在1350℃即可获得致密的合金。     

一种并行工程信息集成框架的构建

本文针对现有的并行工程信息集成框架对并行工程只提供消极支持的问题展开讨论，通过技术域，支撑域，管理域三个域的建立与分析，特别是对ＣＦ积极支持方法进行探讨，提出一种推拉式的建模思想，实现对并行设计的监督和控制。并依此思想建立了一个ＣＥ信息集成框架。     

Mo的替代对FeNbBCu软磁纳米晶合金磁谱的影响

本文研究了Fe82Nb7-xMoxB10Cu1(x=0,1,3,5）系列纲伙晶软磁合金中Mo的含量对磁导率谱（频率范围1kHz-1MHz)的影响，并用畴壁钉扎理论进行了解释，在磁谱中观测到随着Mo含量的增加，弛豫频率线性地上升，μ′随外加磁场幅度变化曲线表明其原因在于Mo的替代导致了钉扎场的增强。     

一种计算孕育衰退时间的数学模型

确定孕育衰退时间对于正确制定工艺措施、提高铸件质量具有重要意义。以异质形核理论为基础,建立了孕育剂扩散衰退模型,得到了计算衰退时间的表达式。结果表明:孕育衰退时间与孕育剂中有效形核相的溶质扩散系数成反比,与有效形核相的半径及该相中的溶质浓度等参数有关。最后对该模型进行了验证,结果表明该模型与相关试验结果基本符合。