Optical and Microstructural Characterisations of Pulsed rf Magnetron Sputtered Alumina Thin Film

Alumina thin films were deposited on fused quartz and SS304 substrate by pulsed rf magnetron sputtering with both direct and reactive methods. The films were characterised by energy dispersive X-ray spectroscopy, X-ray diffraction, scanning electron microscopy, field emission scanning electron microscopy and atomic force microscopy to reveal the microstructure, surface morphology and topography of thin films. Transmittance and reflectance of alumina thin film were evaluated after deposition on the quartz substrate. Transmittance of the quartz remains almost un-altered when alumina was deposited by the reactive sputtering. A marginal decrease of ~4% in the transmittance of quartz was, however, observed after deposition of alumina by direct sputtering. Infrared emittance of the substrate also remains almost constant after deposition of thin alumina film. Further, as-deposited alumina on SS304 obtained by both direct and reactive sputtering process was amorphous in nature. However, after annealing crystalline peaks were observed.     

Evaluation of embeddable potential sensor for corrosion monitoring in concrete structures

Embeddable potential sensor based on MnO₂ was assembled and characterised in concrete. The stability, reversibility, polarisability and impedance characteristics have been studied with respect to known reference. The corrosion performance of reinforced steel with respect to MnO₂ sensor was monitored by different electrochemical techniques. Reversibility of MnO₂ sensor indicated that difference of ±5 mV between the forward and reverse scan indicates the better reversibility characteristics in concrete. The rebar potentials (E_R) of steel with respect to MnO₂ are −315 and −525 mV for passive and active conditions of rebar in concrete. The corrosion current from potentiodynamic polarisation and R_ct from a.c. impedance technique clearly differentiated the behaviour of steel embedded in chloride contaminated concrete (active condition) from uncontaminated concrete (passive condition) with respect to MnO₂ sensor. All these studies revealed that corrosion monitoring of steel in concrete using embedded MnO₂ as a better potential sensor for steel in concrete. In addition it is easy to fabricate for amenable miniaturisation, varied configuration as demanded for corrosion monitoring in concrete structures.     

A thermodynamic framework for the modeling of crystallizable shape memory polymers

Shape memory polymers are a relatively new class of materials that have the ability to retain a temporary shape, which can be reset to the original shape with the use of a suitable trigger, typically an increase in temperature. The temporary shapes can be very complex and the deformations involved large. These materials are finding use in a large variety of important applications; hence the need to model their behavior. In this paper, we develop constitutive equations to model the thermo-mechanical behavior of crystallizable shape memory polymers. Crystallizable shape memory polymers are called crystallizable because the temporary shape is fixed by a crystalline phase, while return to the original shape is due to the transition of this crystalline phase. The modeling is carried out using a framework that was developed recently for studying crystallization in polymers and is based on the theory of multiple natural configurations. In this paper we formulate constitutive equations for the original amorphous phase and the semi-crystalline phase that is formed after the onset of crystallization. In addition we model the transition of the crystalline phase to capture the return of the polymer to its original shape. These models for shape memory effects in polymers have been developed within a full thermodynamic framework, extending our previous work in which the models were developed within a mechanical setting [G. Barot, I.J. Rao, Constitutive modeling of the mechanics associated with crystallizable shape memory polymers, ZAMP 57 (4) (2006) 652-681]. The model is applied to the problem of inflation and extension of a hollow cylinder. The results are consistent with what has been observed in experiments.     

A General Method for the Synthesis of 5H‐Benzo[b]‐, Carbazolo[2,3‐b]‐ and Indolo[2,3‐b]carbazole Derivatives via Copper(II) Triflate‐Catalyzed Heteroannulation

A straightforward approach for the construction of 5H‐benzo[b]‐, carbazolo[2,3‐b]‐ and indolo[2,3‐b]carbazole derivatives has been developed by using copper(II) triflate‐catalyzed heteroannulation.     

Application of harmonic analysis in measuring the corrosion rate of rebar in concrete

The corrosion rate (CR) of rebar embedded in cement mortar, concrete and cement extract is determined using harmonic analysis technique (HA). Simultaneously using other electrochemical techniques such as impedance spectroscopy (EIS) and Tafel extrapolation (TET), the CR was determined and compared with the weight loss method. CR obtained from HA is comparable to that of EIS provided that the Stern–Geary constant (B value) obtained from HA is used in the calculation. In concrete, comparable corrosion rates are obtained between TET and HA only under active condition of the rebar whereas under passive state, the corrosion current (i_corr) by TET is 10 times lower than that of HA. A good agreement is obtained between the HA and weight loss method. The outcome of the result suggests that HA is capable of providing a higher degree of accuracy than that of EIS and TET in the determination of i_corr in the medium like rebar in concrete having very low rate of corrosion.     

用超声波研究不同温度下4-氨基丁酸在硫酸柳丁氨醇水溶液中的性质(英文)

Ultrasonic speeds of 4-aminobutyric acid in 0.0041,0.0125 and 0.0207 mol·kg-1 aqueous salbutamol sulphate(SBS) solutions are measured at 308.15,313.15 and 318.15 K.Isentropic compressibility kS,change in isentropic compressibility△k S,relative change in isentropic compressibility( 0 S S △k /k) ,apparent molal compressibility kφ,limiting apparent molal compressibility k0 φ,transfer limiting apparent molal compressibility k0 φ,hydration number nH,pair and triplet interaction parameters kAS,kASS are estimated.The above parameters are used to interpret the solute-solute and solute-solvent interactions of 4-aminobutyric acid in the aqueous salbutamol sulphate solutions.     

A RHEOMETER FOR MEASURING THE PROPERTIES OF GRANULAR MATERIALS

A great many technological applications such as pneumatic handling of grains and minerals, drying of particles, gasification of solid fuels, require an understanding of the properties of granular solids. Material parameters which can describe the common phenomena exhibited by these granular materials, such as dilatancy, cohesion, adhesion, frictional resistance, etc. need to be incorporated in the model and methods devised for measuring and quantifying them. Reliable experiments are required to measure the properties of these materials. However, this branch of rheology has not been as well studied as the rheology of fluids due to the difficulties inherent to grannular materials in that they exhibit both solid-like and fluid-like properties. Here, we discuss the development of an instrument which can evaluate the material properties of grannular solids. Experimental investigations verify the commonly exhibited phenomena by these materials and estimate the various forces which are generated due to the flow of these materials, thereby enabling their characterization.     

Effects of thermal annealing on the electrical and structural properties of Pt/Mo Schottky contacts on n-type GaN

Thermal annealing temperature effects on the electrical and structural properties of platinum/molybdenum (Pt/Mo) Schottky contacts on n-type GaN have been investigated by current–voltage (I–V), capacitance–voltage (C–V), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) techniques. As-deposited Pt/Mo/n-GaN Schottky diode exhibits barrier height of 0.75 eV (I–V) and 0.82 eV (C–V). Upon annealing at 400 and 500 °C, the barrier height slightly increased to 0.77 eV (I–V) and 0.92 eV (C–V) and 0.82 eV (I–V) and 0.97 eV (C–V), respectively. A maximum barrier height of 0.83 eV (I–V) and 0.99 eV (C–V) is obtained on the Pt/Mo contacts annealed at 600 °C. X-ray photoelectron spectroscopy results shows that the Ga 2p core-level shift towards the low-energy side for the contact annealed at 600 °C as compared to the as-deposited one. Based on the results of XPS and XRD studies, the formation of gallide phases at Pt/Mo/n-GaN interface could be the reason for the increase of Schottky barrier heights upon annealing at elevated temperatures. The atomic force microscopy (AFM) results showed that the Pt/Mo contact does not seriously suffer from thermal degradation during annealing even at 600 °C (RMS roughness of 5.41 nm). These results make Pt/Mo Schottky contacts attractive for high temperature device applications.     

Thermally stable and low-resistance W/Ti/Au contacts to n-type GaN

We report on the formation of thermally stable and low-resistance Ti/Au-based ohmic contacts to n-type GaN (4.0 × 10¹⁸ cm⁻³) by using a W barrier layer. It is shown that the electrical characteristic of the sample is considerably improved upon annealing at 900 °C for 1 min in a N₂ ambient. The contacts produce the specific contact resistance as low as 6.7 × 10⁻⁶ Ω cm² after annealing. The Norde and current–voltage methods are used to determine the effective Schottky barrier heights (SBHs). It is shown that annealing results in a reduction in the SBHs as compared to that of the as-deposited sample. Auger electron spectroscopy (AES), scanning transmission electron microscopy (STEM) and X-ray diffraction (XRD) examinations show that nitride and gallide phases are formed at the contact/GaN interface. Based on the AES, STEM and XRD results, a possible ohmic formation mechanism is described and discussed.     

Improvement of tea leaves fermentation with Aspergillus spp. pectinase

The pectinase enzymes isolated from Aspergillus spp., A. indicus, A. flavus and A. niveus were used for fermentation of tea leaves. The enzymes were purified and characterized. The effect of both crude enzyme preparation and purified pectinase enzymes on the improvement of tea leaf fermentation were determined in terms of theaflavin, thearubigin, high polymerized substances, total liquor colour, dry matter content and total soluble solids of the tea produced. The crude enzyme preparations obtained from ethanol precipitation were found to be more effective in improving tea leaf fermentation than the purified pectinase enzymes.