Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

Phase and microstructure evolution of Sc2O3–CeO2 –ZrO2ceramics in Na2SO4 + V2O5 molten salts

In this study, the destabilization resistance of Sc₂O₃ and CeO₂ co-stabilized ZrO₂ (SCZ) ceramics was tested in Na₂SO₄ + V₂O₅ molten salts at 750°C–1100 °C. The phase structure and microstructure evolution of the samples during the hot corrosion testing were analyzed with X-ray diffraction (XRD), Raman spectra, scanning electron microscopy (SEM), energy dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). Results showed that the destabilization of SCZ ceramics at 750 °C was the result of the chemical reaction with V₂O₅ to produce m-ZrO₂ and CeVO₄, and little ScVO₄ was detected in the Sc₂O₃-rich SCZ ceramics. The primary corrosion products at 900 °C and 1100 °C were CeO₂ and m-ZrO₂ due to the mineralization effect. The Sc₂O₃-rich SCZ ceramics exhibited excellent degradation resistance and phase stability owing to the enhanced bond strength and the decreased size misfit between Zr⁴⁺ and Sc³⁺. The destabilization mechanism of SCZ ceramic under hot corrosion was also discussed.     

Study on Runoff Control Effect of Different Drainage Schemes in Sponge Airport

Water Resources Management - The low impact development (LID) concept aims to control storm runoff and pollution through decentralized, small-scale source control to bring the development area as...     

Photoregulation of Gene Expression with Ligand-Modified Caged siRNAs through Host/Guest Interaction

Small interfering RNA (siRNA) can effectively silence target genes through Argonate 2 (Ago2)-induced RNA interference (RNAi). It is very important to control siRNA activity in both spatial and temporal modes. Among different masking strategies, photocaging can be used to regulate gene expression through light irradiation with spatiotemporal and dose-dependent resolution. Many different caging strategies and caging groups have been reported for light-activated siRNA gene silencing. Herein, we describe a novel caging strategy that increases the blocking effect of RISC complex formation/process through host/guest (including ligand/receptor) interactions, thereby enhancing the inhibition of caged siRNA activity until light activation. This strategy can be used as a general approach to design caged siRNAs for the photomodulation of gene silencing of exogenous and endogenous genes.     

Motion of a Robot Mower with Directional Control

Russian Engineering Research - The stability of robot-mower motion in a specific direction is considered. The direction is regulated by means of an angular sensor and a programmable controller...     

The surface carboxyl group of carbonaceous microspheres effects on the synthesis and structure of SiOC ceramics

In this study, C/SiOC and C/SiO₂ composites were prepared by using carbonaceous microspheres with different surface functional groups. Carbonaceous microspheres based on hydrothermal reaction of glucose contains hydroxyl group, while the surface carboxyl group increases after NaOH etching. The hydroxyl group increases the oxygen-enriched structural units of SiOC ceramics, and the C spheres are closely enwrapped in SiOC matrix after pyrolysis at 900 °C. However, the interfacial reaction of surface carboxyl with Si–OH results in the formation of cristobalite SiO₂, and C spheres are not only encased inside the SiOC matrix, but also dispersed outside of SiOC ceramics. After removal of C via calcination at 500 °C for 5 h, C/SiOC and C/SiO₂ composites are transformed into amorphous SiO₂ and cristobalite SiO₂, respectively. The thermogravimetric analysis indicates the oxidation resistance of SiOC is superior to that of C and SiO₂.     

Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Spatiotemporal Magnetocaloric Microenvironment for Guiding the Fate of Biodegradable Polymer Implants

The degradation behavior of implants is significantly important for bone repair. However, it is still unprocurable to spatiotemporally regulate the degradation of the implants to match bone ingrowth. In this paper, a magneto-controlled biodegradation model is established to explore the degradation behavior of magnetic scaffolds in a magnetothermal microenvironment generated by an alternating magnetic field (AMF). The results demonstrate that the scaffolds can be heated by magnetic nanoparticles (NPs) under AMF, which dramatically accelerated scaffold degradation. Especially, magnetic NPs modified by oleic acid with a better interface compatibility exhibit a greater heating efficiency to further facilitate the degradation. Furthermore, the molecular dynamics simulations reveal that the enhanced motion correlation between magnetic NPs and polymer matrix can accelerate the energy transfer. As a proof-of-concept, the feasibility of magneto-controlled degradation for implants is demonstrated, and an optimizing strategy for better heating efficiency of nanomaterials is provided, which may have great instructive significance for clinical medicine.