Solid-state phase equilibria in the Gd–Co–Al ternary system at 1173 K

A portion of the isothermal section (1173 K) of the phase diagram of the Gd–Co–Al ternary system (up to 33.3 at.% Gd) were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDS) techniques. Fourteen single-phase regions (including solid solution regions of the binary compounds), twenty-five two-phase regions and twelve three-phase regions were found to exist at this isothermal section. In the GdCo₂–GdAl₂ system, the existence of the GdCo_0.74Al_1.26 phase is identified and it has a composition range of 30–45 at.% Al, the maximum solid solubility of Al in GdCo₂ is about 15 at.%, and Co in GdAl₂ is about 16 at.%. Besides, the maximum solid solubility of Al in Co, Gd₂Co₁₇ and GdCo₅ is about 6, 17 and 25 at.%, respectively, the maximum solid solubility of Gd in Co, CoAl is below 2 at.% and the solid solubility range is from 47 to 61 at.% Al in CoAl phase. In this work, no new ternary compounds were observed.     

高频燃烧-红外吸收法测定金属铪中 碳含量研究

称取0.5 g金属铪样品置于瓷坩埚中，加入0.3 g纯铁和1.5 g钨锡粒助熔剂，设定高频燃烧红外碳分析功率为80%，吹扫和延迟时间均为10 s，比较水平为2，以钢铁碳标准物质样单点校准设备，绘制校准曲线，并用标准物质验证曲线准确性，建立金属铪中碳含量的测定方法，测量范围为0.001%~0.040%。采用该方法对2个厂家的金属铪中碳含量进行测定，测定结果的相对标准偏差不大于8%，在2个金属铪样品中加入钢铁碳标样进行加标回收试验，回收率在85%~106%之间。     

AlTiB纳米细化剂对ZL101合金力学及阻尼性能的影响

利用原位自生法合成的纳米晶粒细化剂,成功的克服了颗粒团聚,有效的抑制了颗粒的沉降。本试验用其对ZL101合金的细化行为进行了研究。试验结果表明:加入量为0.2%(质量分数)时,纳米晶粒细化剂可有效地细化初晶α-Al,改善共晶硅的形貌及尺寸,细化后铸态α-Al枝晶尺寸由44μm减小至23μm;经T6处理的细化后试样其拉伸断口为韧窝断口,且韧窝明显多于未细化试样;加入细化剂后保温30min,与未细化合金相比,抗拉强度提高了28MPa,屈服强度提高了22MPa,延伸率增加了2.6%;同时细化后合金的阻尼性能较未细化合金有了大幅提高,0.5Hz时细化后室温阻尼性能Q-1=13×10-3,较之细化前Q-1提高了5×10-3。     

连铸轻压下技术的机理比较

轻压下技术对改善连铸坯中心偏析有显著的效果，在生产中得到了广泛的应用。为此分析了两种机械压下技术改善中心偏析的机理，比较两者改善中心偏析的效果，并进一步讨论了轻压下技术在工业应用中要注意的问题。     

电流值对水下电弧法制备洋葱状富勒烯的影响

研究了在不同电流值条件下纯石墨电极水下电弧放电法制备洋葱状富勒烯(OLFs)的过程和工艺.采用场发射扫描电镜,X射线衍射,高分辨透射电镜对产物的微观结构和形貌进行表征.所得产物是直径约为25 nm,外形呈球状并具有一定的空心结构OLFs.研究了放电时的电流值对产物的产量和产率以及对产物石墨化程度的影响,结果表明在20A-50A范围内随着电流强度的增大OLFs的产量和产率都有不同程度的提高.     

CRYSTALLOGRAPHIC ANALYSIS OF THE LATH MARTENSITE TRANSFORMATION IN Fe-Ni-Mn ALLOY

1.IntroductionBased on the concept of an invariant plane strain (IPS), phenomenological theory of martensite transformation (PTMT) is established[1-3]. In this case, an invariant plane is obtained by self-accommoda-tion effect between different martensitic variants, and the formula which reveals this self-accommoda-tion effect can be written as …     

氧气管道内部喷砂除锈喷头改进

介绍管道内喷砂除锈所用喷头的改进及效果。     

面向集群制造的模具多项目生产管理系统研究

分析了集群制造系统下模具生产的多项目并存多主体协商的特征；研究了基于网络计划的模具生产多项目管理技术；利用JAVA的跨平台性，开发了基于网络的模具多项目分布式生产管理系统。     

添加剂硼对纯铁粉末触媒合成金刚石的影响

本义研究了添加剂硼对纯铁粉末触媒合成金刚石的影响。实验中将不同比例的无定形硼粉直接添加到石墨-纯铁粉末体系中并均匀混合，以此方式，将硼掺杂到高温高压合成的金刚石单晶中。实验结果表明，随硼添加比例的不同，合成金刚石的最低压力点也不同；同时，通过不同添加比例的硼合成出金刚石的颜色，可得知该方法对提高金刚石内硼含醚的有效性。实验还发现，当硼添加比例一定时，合成温度对合成金刚石的特性产生了一系列的影响。