Studies on structural,dielectric and electrical properties of Dy<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Bi<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>FeO<Subscript>3</Subscript> solid solutions

The polycrystalline samples of Dy _x Bi_1−x FeO₃ (x = 1, 0.8, 0.6, 0.4 and 0.2) were synthesized by standard solid state reaction technique. The samples synthesized were characterized by X-ray diffraction (XRD) technique. Further the samples were characterized by infrared (IR) spectroscopic technique. The dielectric measurements were carried out as a function of frequency in the range 100 Hz to 1 MHz at room temperature. Also the dielectric measurements were carried out as a function of temperature at certain fixed frequencies. The ac and dc resistivity measurements were carried out using two probe method. Also temperature dependence of ac and dc resistivity was noted. These measurements suggest polaron conduction in the samples. Finally, the data from XRD, IR, dielectric measurements were correlated.     

Dielectric behavior of Cu–GeO<Subscript>2</Subscript> cermet thin films

Capacitance and dielectric loss measurements were carried out using an Al/Cu–GeO₂/Al sandwich structure for 0 to 10 vol% Cu films, 120–400 nm thick, deposited at 0.4–1.5 nm/s in the frequency and temperature range 1–10⁶ Hz and 90–573 K, respectively. The variation of capacitance and dielectric loss with frequency and temperature follows the Goswami and Goswami model. Capacitance decreases slowly with increasing thickness and also varies with the change in deposition rate of the cermet film.     

The effect of interfacial energy and phase fraction on the particle shape and the dihedral angles in two-phase small particles containing a cusp-oriented interface; computational model

The equilibrium shape and dihedral angles at the solid–liquid–vapor tri-junctions of two-phase alloy small particles containing a cusp-oriented interface were modeled as a function of phase fraction, surface energy and the interfacial energy. The calculation was applied to different combinations of surface and/or interfacial energies to demonstrate the various possible particle shapes and dihedral angles that result for two-phase particles. The dihedral angles at the tri-junction vary with the phase fraction, due to the coupling between the relative amounts of each phase, interfacial energy relative to the two surface energies and the equilibrium conditions at the tri-junction. These features can be used to find the ratio of the interfacial energy to the surface energies of two-phase particles for any state of matter.     

The hydration of slag,part 1: reaction models for alkali-activated slag

Reaction models are proposed to quantify the hydration products and to determine the composition of C–S–H from alkali-activated slags (AAS). Products of the slag hydration are first summarized from observations in literature. The main hydration products include C–S–H, hydrotalcite, hydrogarnet, AFm phases (C₄AH₁₃ and C₂ASH₈) and ettringite. Then, three stoichiometric reaction models are established correlating the mineral composition of slag (the glass part) with the hydration products. Using the proposed models, quantities of hydration products and composition of C–S–H are determined. The models are validated with a number of experimental investigations reported in literature, yielding good agreement, i.e., these models can successfully predict the hydration reaction of AAS. The models are furthermore applied to calculate the retained water in the hydration products of AAS in different hydration states and a general hydration equation of AAS is derived. As an illustration to one of the model applications, chemical shrinkage of the AAS cement paste in different hydration states are predicted. The chemical shrinkage of AAS is shown to be remarkably higher than OPC. Furthermore, phase distribution in the hardened AAS paste and the porosity are calculated.     

Factors affecting prior austenite grain size in low alloy steel

The effect of varying normalising and hardening temperatures on the prior austenite grain size in a low alloy Cr–Mo–Ni–V steel has been examined. An initial relative insensitivity of grain size to increasing austenitising temperature was observed followed by a sudden growth of grains at approximately 1000 °C. A detailed study of the precipitates in the steel showed the presence of a bimodal size distribution of vanadium carbides. The grain size increase is attributed to a decrease in volume fraction and an increase in size of V₄C₃ particles with increasing temperature.     

Identification of microstructural zones and thermal cycles in a weldment of modified 9Cr-1Mo steel

This paper presents the results of a study on the microstructural and microchemical variations in a multipass Gas Tungsten Arc weld (GTAW) of modified 9Cr-1Mo steel. The changes brought about in the steel due to the heating and cooling cycles during welding and the subsequent effects due to reheating effects during multipass welding are described. Detailed analytical transmission electron microscopy has been carried to study the type and composition of the primary and secondary phases in this steel. The systematic changes in microstructural parameters such as Prior Austenite Grain Size, martensite lath size, number density, size and microchemistry of carbides, have been understood based on the different transformations that the steel undergoes during the heating and cooling process. Based on the observed microstructure, an attempt has been made to identify distinct microstructural zones and possible thermal cycles experienced by different regions of the weldment.     

Review on the fracture processes in nanocrystalline materials

An overview of experimental study, computer simulations and theoretical models of fracture of nanocrystalline materials is presented. The key experimentally detected facts on ductile and brittle fracture processes are discussed. Special attention is paid to computer simulations and theoretical models of nucleation and growth of nanocracks and nanopores in deformed nanocrystalline materials. Also, we discuss mechanisms for fracture suppression in such materials showing good ductility or superplasticity.     

Magnetostriction of binary and ternary Fe–Ga alloys

This article will review the development of the Fe–Ga (Galfenol) alloy system for magnetostriction applications including work on substitutional ternary alloying additions for magnetic property enhancement. A majority of the alloying addition research has focused on substitutional ternary elements in Bridgman grown single crystals with the intent of improving the magnetostrictive capability of the Galfenol system. Single crystals provide the ideal vehicle to assess the effectiveness of the addition on the magnetostrictive properties by eliminating grain boundary effects, orientation variations, and grain-to-grain interactions that occur when polycrystals respond to applied magnetic fields. In almost all cases, ternary additions of transition metal elements have decreased the magnetostriction values from the binary Fe–Ga alloy. Most of the ternary additions are known to stabilize the D0₃ chemical order and could be a primary contribution to the observed reduction in magnetostriction. In contrast, both Sn and Al are found to substitute chemically for Ga. For Sn additions, whose solubility is limited, no reduction in magnetostriction strains are observed when compared to the equivalent binary alloy composition. Aluminum additions, whose effect on the magnetoelastic coupling on Fe is similar to Ga, result in a rule of mixture relationship. The reviewed research suggests that phase stabilization of the disordered bcc structure is a key component to increase the magnetostriction of Fe–Ga alloys.     

Effect of preparation technique on the properties of Mo-containing Al-MCM-41

The Al-MCM-41 has been used as support to prepare Mo-containing catalysts. The 12- molybdophosphoric heteropoly acid (HPMo) is used as initial compound. The catalysts are synthesized by two different methods: incipient impregnation with aqueous solution of the acid and mechanochemical synthesis. The samples were tested in the reaction of the thiophene hydrodesulfurization after activation with mixture H₂ + H₂S. The effect of the preparation method of the catalysts on their physicochemical and catalytic properties has been studied. A partial destruction of the loaded compound is observed in mechanochemically treated sample whereas the aggregates are formed from the particles of different size in the impregnated sample. The specific surface area of the sample prepared by mechanical–chemical treatment decreases 2–3 times, while the total pore volume is about four times lower. The HDS activity is higher on the impregnated sample than on the mechanochemically treated one.     

Electrical characterization of carbon nanotube Y-junctions: a foundation for new nanoelectronics

A review on the syntheses and electrical characterization of Y-shaped multi-walled carbon nanotube morphologies is presented. Modified thermal CVD processes, using Ti precursors, are used to grow Y-junctions of different geometries and distribution of catalyst particles. It has been established that novel electrical switching behavior is feasible, where any one of the three branches of the Y-junction can be used for modulating the electrical current flow through the other two branches. Current blocking behavior, leading to perfect rectification, is seen which could be related to the interplay of the carrier lifetime and the transit time. The overall goal is to investigate the possibility of obtaining novel functionality at the nanoscale, which can lead to new device paradigms.