Hydrothermal Corrosion of Alumina Ceramics

The corrosion behavior and strength degradation of alumina ceramics with 99%, 99.9%, and 99.99% Al₂O₃ were studied in water at 300°C and 8.6 MPa for 1 to 10 d. The weight loss in alumina ceramics was mainly attributed to the dissolution of SiO₂ and Na₂O grain-boundary impurities. Intergranular corrosion proceeded in the alumina ceramics by preferential attack at the grain boundaries. The extent of the strength reduction for corroded alumina ceramics was related to the impurity level in the alumina ceramics.     

Identifications of inhibitors of IgE production by human lymphocytes isolated from ‘Cha Chuukanbohon Nou 6’ tea leaves

BACKGROUND: Tea (Camellia sinensis L.) is consumed all over the world and in especially large quantities in Japan and China, where it has been used not only as a daily beverage but also for medicinal purposes for thousands of years. Tea has been found to exhibit various bioregulatory activities, including antiallergic, anticarcinogenic, antimetastatic, antioxidative, antihypertensive, antihypercholesterolemic, anti‐dental caries and antibacterial effects, and to influence intestinal flora. RESULTS: Cha Chuukanbohon Nou 6 is a tea cultivar improved by the National Institute of Vegetable and Tea Science (NIVTS) in Japan. On comparing chemical constituents of 11 varieties of tea leaves by high‐performance liquid chromatography, we found two new major compounds in Cha Chuukanbohon Nou 6. Nuclear magnetic resonance spectroscopy revealed these compounds to be theogallin and 1,2‐di‐O‐galloyl‐4,6‐O‐(S)‐hexahydroxydiphenoyl‐β‐D ‐glucopyranose. The two were similar in chemical structure to strictinin, an inhibitor of immunoglobulin (Ig) production. Thus their effects on the production of Igs by peripheral blood lymphocytes were tested. Both compounds, like strictinin, inhibited IgE production. CONCLUSION: The results suggest Cha Chuukanbohon Nou 6 to be the basis of an antiallergic beverage. Copyright © 2009 Society of Chemical Industry     

TARGET YIELDS AND HYDROGEN CONSUMPTION IN BROWN COAL LIQUEFACTION

A simple mechanistic model for brown coal liquefaction has been developed and used in conjunction with data from PDU operation to examine the factors which contribute to hydrogen consumption. It is found that after allowing for hydrogen generation requirements, the maximum achievable refined product yield from Morwell brown coal ((ssuming a naphtha/middle distillate ratio of 5:6 together with refined product H/C ratios of 1.8 for naphtha and 1.5 for middle distillate) is 46 - 48%, corresponding to a hydrogen consumption of 6.6 - 7.6%. Alternatively, if consideration of hydrogen generation is excluded (as in pilot plant operation), the maximum yield would be around 54%, corresponding to 6.6% net hydrogen consumption. These results suggest that an aim of maximizing product yield by decreasing Cl-C4 gas formation may not be as desirable as at first thought.     

Creation of Ferroelectric, Single-Crystal Architecture in Sm0.5La0.5BGeO5 Glass

Using a novel, selective heating by Nd:YAG laser, a single-crystal architecture is created in a model glass system, Sm_0.5La_0.5BGeO₅, which devitrifies congruently into a ferroelectric phase of the same composition as the parent glass. The Sm³⁺ ions in glass absorb the light and heat the matrix locally resulting in devitrification. Initially, a polycrystalline spot is formed. However, with optimum laser power, scanning speed, and the depth of focus, one of the grains acts as the seed for further growth as a single crystal. By programming the relative displacement of the glass with respect to laser spot, desired single ferroelectric crystal architecture is created. The optical functionalities (guiding of light and second harmonic generation) of the architectures are shown, which demonstrate the viability of this method for constructing active elements in optical integrated circuits. The single-crystal nature of the architecture is confirmed from the electron backscattered diffraction results.     

Transient and steady state crack growth kinetics for stress corrosion cracking of a cold worked 316L stainless steel in oxygenated pure water at different temperatures

The stress corrosion cracking (SCC) growth kinetics for a cold worked 316L stainless steel was continuously monitored in high purity water at different temperatures and dissolved oxygen (DO) levels under a K (or K_max) of 30 MPa m^0.5. The total SCC test time was more than 8000 h to make sure the steady state crack growth rate under each test condition could be reached. Crack growth rate (CGR) increases with increasing temperature in the range 110-288 °C. A typical intergranular-cracking mode is identified. Depending on the previous test condition, especially the temperature, three kinds of crack growth kinetics, i.e., increasing with testing time then becoming steady, being constant during the whole period, or decreasing with test time then becoming steady, are identified and discussed. Time-dependent and testing history-dependent crack growth modes were confirmed in two series of tests in 2 ppm DO and 7.5 ppm DO pure water. The apparent activation energies are calculated and compared with other data in different environments under different applied loading levels for understanding the cracking mechanism.     

Immunohistochemical localization of endothelin-1, endothelin-3 and endothelin receptors in human pheochromocytoma and paraganglioma

Endothelin (ET) and its receptor system have been shown to exert various biological effects on different types of cells in addition to their well-known vasoconstrictor activity. Recently ET-1, ET-3 and the ETB receptor have been shown to play an important role in the development of neural crest-derived cells and, in this context, pheochromocytomas have been reported to harbor ET-1. Endothelin-3 or ET receptor subtypes, however, have not been examined in pheochromocytoma and paraganglioma so far. In the present study the immunohistochemical localization of ET-1/big ET-1, ET-3/big ET-3 and the ETA and ETB receptors were investigated to clarify the biological characteristics of these two tumors using 32 pheochromocytomas and 11 extra-adrenal paragangliomas. Endothelin-1/big ET-1 was detected in 19 pheochromocytomas (59%) and eight paragangliomas (72%), while ET-3/big ET-3 was detected in 10 pheochromocytomas (31%) and three paragangliomas (27%). The ETA receptor was found in 21 pheochromocytomas (66%) and in eight paragangliomas (73%), while the ETB receptor was found in 25 pheochromocytomas (78%) and in eight paragangliomas (73%). Normal adrenomedullary cells lacked each antigen examined. Endothelin-immunoreactive tumor cells were distributed focally or in a manner scattered, while receptor-immunostained tumor cells were distributed with a focal pattern for the ETA receptor and with a focal or diffuse pattern for the ETB receptor. Endothelin and its receptor coexisted in the same tumor in 21 of 28 ET-positive pheochromocytomas and in eight of 10 ET-positive paragangliomas. In addition, seven pheochromocytomas and two paragangliomas revealed positivity of the receptor(s) irrespective of the absence of ET-immunoreactivity. In conclusion, ET and its receptor are frequently and concomitantly expressed in the pheochromocytoma and paraganglioma. From the highly frequent expression of this system or the receptor(s), ET-receptor-mediated signal transduction of these tumors concerning growth and/or cell survival is expected, although definite biological significance of this ligand-receptor system in these tumors awaits further investigation.     

Nondestructive inspection of thermal barrier coating of gas turbine high temperature components

A thermal barrier coating (TBC) is applied to high‐temperature components in gas turbines, and consists of a ceramic topcoat and a metallic bondcoat. Various kinds of TBC degradation and damage occur in high‐temperature components during service, such as topcoat thinning, topcoat delamination, and formation of a thermally grown oxide (TGO) layer below the topcoat, each of which can be examined using a suitable nondestructive inspection technique. Topcoat thinning can be detected by topcoat thickness measurement using terahertz waves, which are electromagnetic waves in the frequency region between optical and radio waves. The measurement resolution is about 10 μm, which is comparable to microscopic observation of the cross section in destructive inspection. Topcoat delamination can be detected by active thermography, in which the topcoat surface is scanned by a heating laser and the surface temperature distribution is measured by a thermal infrared camera. The combination of temperature peak and residual thermal image detection is effective in eliminating false detection. The TGO layer can be detected using photoluminescence, in which the Cr³⁺ ions included as an impurity in Al₂O₃ are detected. Since delamination tends to occur at locations at which the TGO layer has grown, TGO layer detection provides an effective method to select regions where delamination has occurred or is likely to occur. An inspection flow based on these techniques is proposed, which is expected to aid the establishment of condition‐based maintenance strategies of high‐temperature components. © 2016 Institute of Electrical Engineers of Japan. Published by John Wiley & Sons, Inc.     

Lightning occurrence data observed with lightning location systems of electric power companies in Japan: 2009–2013

Nine electric power companies in Japan have been collecting lightning data with lightning location systems. Five years of the lightning data (2009–2013) are summarized and analyzed in this paper. The recent annual number of lightning flashes of which the current is more than 10 kA in Japan is around 1 million. The variations of lightning occurrence characteristics by areas, seasons, and so on, are clarified. Meteorological conditions that may affect lightning occurrence are also discussed. Furthermore, we show that there is a clear correlation between the number of lightning strikes and the outage rate of transmission lines. © 2016 Institute of Electrical Engineers of Japan. Published by John Wiley & Sons, Inc.     

Development and characterization of micro-dispersed lacquer

本文利用一种特制的搅拌装置来制备微分散生漆。研究了在不同的搅拌速率和搅拌时间下所获得的生漆微粒子的直径和性能的关系。粒度分布测定表明,经过60分钟且每分钟240转搅拌处理的生漆,其粒子直径分布最窄,平均为0.194微米。凝胶色谱(GPC)分析显示生漆中的寡聚体增加的同时单体的百分含量减少了,意味着在搅拌的过程中发生了聚合反应。另外,微分散生漆的粘度、干燥成膜时间、膜亮度、膜颜色、膜光泽以及耐紫外线等特性也作了深入的探讨。