Luminescence from praseodymium doped AlN thin films deposited by RF magnetron sputtering and the effect of material structure and thermal annealing on the luminescence

Thin films of Praseodymium doped AlN are deposited on silicon (111) substrates at 77 K and 950 K by rf magnetron sputtering method. About 500–1000 nm thick films are grown at 100–200 watts RF power and 5–8 mTorr nitrogen, using a metal target of Al with Pr. X-rays diffraction results show that films deposited at 77 K are amorphous and those deposited at 950 K are crystalline. Cathodoluminescence studies are performed at room temperature and luminescence peaks are observed in a wide range from ultraviolet to infrared region. The most intense peak is obtained in green at 526 nm from amorphous films as a result from ³P₁→³H₅ transition. In crystalline films the intense peak was obtain in red at 648 nm as a result from ³P₀→³F₂ transition. Films are thermally activated at 1300 K for half an hour in a nitrogen atmosphere. Thermal activation enhances the intensity of luminescence. Two peaks at 488 nm and 505 nm merged after thermal activation, giving rise to a single peak at 495 nm.     

Life cycle cost analysis of alternative vehicles and fuels in Thailand

High crude oil prices and pollution problems have drawn attention to alternative vehicle technologies and fuels for the transportation sector. The question is: What are the benefits/costs of these technologies for society? To answer this question in a quantitative way, a web-based model (http://vehiclesandfuels.memebot.com) has been developed to calculate the societal life cycle costs, the consumer life cycle costs and the tax for different vehicle technologies. By comparing these costs it is possible to draw conclusions about the social benefit and the related tax structure. The model should help to guide decisions toward optimality, which refers to maximum social benefit. The model was applied to the case of Thailand. The life cycle cost of 13 different alternative vehicle technologies in Thailand have been calculated and the tax structure analyzed.     

Solving the trade-off between fairness and throughput: Token bucket and leaky bucket-based weighted fair queueing schedulers

In this article, we present two efficient weighted fair queueing (WFQ) scheduling algorithms leaned on the well-known token bucket and leaky bucket shaping/policing algorithms. The performance of the presented algorithms is compared to those of the state-of-the-art WFQ approximations such as weighted round robin (WRR) and the recently proposed bin sort fair queueing (BSFQ). Our simulation results show that the proposed algorithms provide a better fairness at a lower implementation complexity while simultaneously achieving a comparable network utilization.     

Results of a User Study on 2D Hurricane Visualization

We present the results from a user study looking at the ability of observers to mentally integrate wind direction and magnitude over a vector field. The data set chosen for the study is an MM5 (PSU/NCAR Mesoscale Model) simulation of Hurricane Lili over the Gulf of Mexico as it approaches the southeastern United States. Nine observers participated in the study. This study investigates the effect of layering on the observer's ability to determine the magnitude and direction of a vector field. We found a tendency for observers to underestimate the magnitude of the vectors and a counter‐clockwise bias when determining the average direction of a vector field. We completed an additional study with two observers to try to uncover the source of the counter‐clockwise bias. These results have direct implications to atmospheric scientists, but may also be able to be applied to other fields that use 2D vector fields.     

In‐Situ Observation of the Formation of MnS during Solidification of High Sulphur Steels

A Confocal Scanning Laser Microscope equipped with a gold image furnace was used to directly observe the precipitation of MnS during solidification of high sulphur steels under isothermal conditions in the temperature region 1440 to 1480°C on the free surface of the steel melt. For the case of Al‐killed steels, below 1480°C MnS particles were found to precipitate with Fe forming simultaneously around them. This MnS containing structure continued to grow rapidly (264 μm/s) as a surface film. The film gradually changed, as the level of S in the melt decreased, into a eutectic structure (with lamella spacing of 2 μm) as predicted by thermodynamics. In Si‐ killed steels there was significantly lower tendency to form MnS both in terms of time until precipitation occurred and growth rate.     

Studies of elemental distributions within discrete coal macerals: Use of secondary ion mass spectrometry and X-ray photoelectron spectroscopy

Secondary ion mass spectrometry has been used to measure qualitatively the distributions of many trace and minor elements within some well-characterized coal macerals: vitrinite, fusinite and exinite. Complementary information was obtained by using X-ray photoelectron spectroscopy. Within the vitrinite specimens studied, a widely-dispersed largely inorganic aluminosilicate phase was identified, which contained a number of other trace elements. By contrast, within the organic-rich phase of this macerai, titanium was detected in a very even distribution; this suggests that some titanium may be bonded in an organic complex. The fusinite was shown to contain elevated concentrations of calcium, magnesium and fluorine, dispersed over a large portion of the maceral. The high fluorine content could be identified as an organo-fluoro compound using XPS. Exinite was found to contain lower concentrations of most elements, compared to other macerals. The organic composition of this maceral was significantly different from that of surrounding macerals; this could be seen from the enhanced emission of the C₂H₂-secondary ion and images of this ion thus clearly outlined the position of such macerals.     

A site selection model for high technology manufacturing firms in the United States

This article offers a quantitative model for site selection by high technology manufacturing firms. In the past, site selection studies have usually been qualitative in nature, and very subjective. This is an attempt to introduce a more objective quantitative approach. The site selection factors most important to high technology manufacturing firms were identified, ranked and weighted based on a US Joint Economic Committe survey of such firms. The eight most important factors were: the availability of technical and professional workers, labor costs, tax climate, academic institutions, cost of living, transportation for people, and access to markets. Demographic data on these factors were collected and analyzed for 32 developing high technology areas in the United States. By using the quantitative model, a score was developed for each area, allowing them to be ranked as R & D manufacturing environments. This model should prove a useful tool for both regional planners and high-tech companies seeking to relocate.