叙述了选择混炼型聚氨酯(PU)与分子量适中的Ⅱ型聚氯乙烯(PVC)树脂制备PVC/PU合金的过程,讨论了PVC/PU共混比、填充剂、硫化体系、共混工艺等因素对PVC/PU合金性能的影响。结果表明:选择PVC/PU=60/40(质量比),硫化剂TD15份,白炭黑30份,混炼温度140—160℃,可制得性能优良的PVC/PU合金。动态力学性能实验显示了PVC/PU合金有较好的相容性。     

新型层状表面相锆基固体酸催化酯化反应研究

将所研制的层状表面相锆基固体酸催化剂用于一元、二元醇醋酸酯和其他羧酸酯类产品的合成 ,考察了其催化性能。研究发现 :层状表面相锆基固体酸催化剂对所考察的酯化反应具有很好的普遍适用性 ,但其酯化率与醇的性质和结构密切有关。催化反应动力学研究表明乙酸与丁醇、戊醇、己醇的酯化反应均为二级反应 ,且反应活化能均较低 ,分别为 47 4kJ/mol、2 3 3kJ/mol和 19 8kJ/mo     

环氧树脂-聚丙烯酸酯乳液型复合薄膜粘合剂

本文主要叙述了环氧-丙烯酸酯聚合乳液的合成,以及该乳液粘合剂的配制;讨论了该乳液粘合剂的粘合性能及耐水、耐溶剂性能。     

聚氨酯丙烯酸酯紫外光固化PVC涂料的研制

通过对涂料不同组分的种类及配比进行调节,制备不同配方的PVC清漆。在测试附着力、硬度、耐温、耐水性能的基础上,优化涂料配方,并配制出性能优异的PVC清漆涂料。     

Preparation,characterization, and adsorption properties for metal ions of a novel chelating resin containing sulfoxide and diethylene glycol

A novel chelating resin containing sulfoxide and diethylene glycol, poly{4‐vinylbenzyl‐[2‐2‐(hydroxyethyl)ethoxyl]sulfoxide} (PVESO) was synthesized using chloromethylated polystyrene (PS‐Cl) as material. Its structure was characterized by elemental analysis, infrared spectra, and scanning electron microscopy (SEM). The adsorption capacities of the resin for Hg²⁺, Ag⁺, Cu²⁺, Zn²⁺, and Pb²⁺ at various pH values were determined. The maximum adsorption capacities for Hg²⁺ and Ag⁺ were 1.56 and 0.75 mmol g^?1 respectively. The resin had high selectivity for Hg²⁺ and Ag⁺ over the pH range 1.0–7.0. The adsorption capacities for Hg²⁺ and Ag⁺ under competitive condition were also determined by batch experiment method. In addition, the adsorption kinetics of the resin towards Hg²⁺ at different temperatures was also investigated. The results showed that the adsorption rate was governed by film diffusion at 20°C and 25°C, by particle diffusion at 30°C and 35°C. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 6054–6059, 2006     

浅析呼和浩特市大气SO2发展趋势及防治对策

本文通过对二氧化硫的形成及危害的阐述，以及对我市近几年大气中二氧化硫监测结果的分析，针对发展趋势和存在的问题，根据实际情况提出相应的建议。     

Soap‐free emulsion copolymerization of perfluoroalkyl acrylates in the presence of a reactive surfactant

Soap‐free emulsion copolymerization of perfluoroalkyl acrylate (FA)/methyl methacrylate (MMA)/n‐butyl acrylate (n‐BA) was carried out in the presence of sodium 2‐acrylamide‐2‐methyl propanesulfonate (AMPSNa) as a reactive surfactant and potassium persulfate (KPS) as an initiator. An analysis of the effects of concentration of AMPSNa, KPS, FA as well as polymerization temperature on the kinetic features (rate of polymerization) and colloidal characteristics (mean particle diameter, particle disperse index, particle numbers, and surface charge density) was followed. NMR, FTIR, AFM, and fluorine‐selective electrode analysis were used to characterize the composition and morphology of the FA copolymers. Both AFM analysis and contact angle measurements strongly implied that the fluorinated segments migrated to the outmost surface and created films with lower surface energy. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 2438–2444, 2007     

快速高效隔膜压滤机在鹤壁四矿选煤厂的应用

介绍了快速高效隔膜压滤机的主要性能参数和特点 ;分析了压滤机在煤泥水处理系统中的应用情况和运行结果 ;应用快速高效隔膜压滤机对煤泥水处理系统进行改造后获得了较好的经济及社会效益     

新型聚丙烯接枝物的制备及应用

为制备强韧的共混材料,利用熔融接枝法研制了含有两种接技单体的新型聚丙烯接枝物,讨论了第二单体在接枝过程中的作用,并将其应用于尼龙6/聚丙烯(PA6/PP)共混体系,获得了使分散相粒径更细小、界面更模糊的增容效果。     