Synthesis and characteristics of SiC whiskers with “rosary bead” morphology

SiC whiskers with ″rosary bead″ morphology were synthesized using suitable silicon source and carbon source through solid reaction at the temperature above 1537 K. The diameter and length of the SiC whiskers were about 0.1-1.0 μm and 20-100 μm,respectively. The largest diameter of their enlarged ends of the whiskers was about 0.2-1.0 μm, and it gradually and smoothly decreased to the size of the plain part of the whiskers. The results of X-ray diffraction analysis show that the crystalline structure of the obtained SiC whiskers is β-SiC. It is considered that the SiC whiskers grow via a vapor-solid mechanism.     

Correlations between the Optical Properties and the Microstructure of TiO_2 Thin Films Prepared by Reactive Electron-beam Evaporation

1　IntroductionInrecentyears ,theoreticalandexperimentalinvesti gationsonthetitaniumoxidefilmsareconductedonac countoftheirremarkableproperties .Titaniumdioxidefilmshaveattractedconsiderableattentiontoapplytomi croelectronicdevices ,opticalthin filmdevice…     

EXPERIMENTAL STUDIES OF NEW TECHNOLOGY ON HIGH GLOSSINESS GRANITE SURFACE

On the basis of analysing thecharacter of granite and its polishingtechnology,the authors have manufactureda kind of polishing disk to polish graniteand good results have been obtained.Through studying the polishing process ofgranite in theory and experiment,theauthors think that the high glossinesssurface is the result of grinding ofabrasives and adhering of soft metal.Moreover,orthogonal test is carried outabout the technical parameters for threeetypical kinds of granites and some usefulresults for production are obtained.     

Fabrication and magnetic properties of Sm_3(Fe,Ti)_(29)N_x/α-Fe dual-phase nanocomposite permanent magnetic material

Sm3(Fe,Ti)29Nx/α-Fe dual-phase nanometer magnetic material was fabricated through rapid solidification, crystallization and nitridation of Sm-Fe (Ti) alloy. The effect of combination of rapid solidification and Ti alloy addition on the phase for- mation and microstructure of the Sm-Fe alloy is investigated in this paper. The mi- crostructure of amorphous phase and dual-phase nano-grain crystals before and after crystallization annealing were observed using a high-resolution transmission electron microscope (HREM). The dual-phase nano-grains after annealing were compacted together with a clear interface with the direct exchange-coupling mechanism. Different annealing processes were used to examine the melt-spun alloy. Comparison of the images of SEM showed that annealing at 750 ℃ for 10 min was most suitable to get homogeneous and nano-grains. No obvious kink was de- tected in the second quadrant of the hysteresis loop like a single hard magnet, and strong exchange coupling was found between hard magnets and soft magnets.     

INVESTIGATION ON SELF-PROPAGATING HIGH-TEMPERATURE SYNTHESIS OF TiAl INTERMETALLIC COMPOUND

The self-propagating high-temperature syn-thesis method was used to synthesize the TiAl intermetalliccompound,and two kinds of synthesis modes were studied inthis paper.The results show that the thermal explosion modeis suitable for the synthesis of TiAI,the pre-heating tempera-ture has a great influence on the synthesis.Microstructurestudy show that the density of the sample fabricated by thermal explosion mode is higher than that fabricated by propa-gating mode.     

用moire技术测量平板玻璃折射率

本文描述了使用moire技术测量平板玻璃折射率的理论并进行了实验论证。测量方法简单且快捷。可精确测量任何透明材料的折射率。测量精确度可达10~(-5)。     

聚醚固体电解质锂电池放电性能研究

利用氧亚甲基连接的聚氧乙烯-聚氧丙烯多嵌段共聚物或氧亚甲基连接的聚氧乙烯多嵌段共聚物与高氯酸锂的络合物作电池的电解质,锂片作负极,几种含钒的化合物作正极,组装了全固态二次锂电池.研究了不同正极材料、不同电解质和不同温度对电池短路放电性能的影响以及电池的重复短路放电性能.研究表明,正极材料V_6O_(13)的性能优于Na_(1+x)V_3O_8;电解质(PEO)_n·LiClO_4的性能优于(PEO-PPO)_n·LiClO_4,这与它们的电导率分别为3.2×10~(-3)S·cm~(-1)和2.2×10~(-3)S·cm~(-1)是一致的.     

电离辐射及超氧阴离子基对人血淋巴细胞姐妹染色单体交换的诱发作用

用姐妹染色单体交换(SCE)作为指标,研究了~(60)Coγ射线辐照及NADH-PMS(吩嗪硫酸甲酯)系统中产生的超氧阴离子自由基(0_2~(·-))对胎儿脐血淋巴细胞染色体的损伤作用,及活性氧清除剂SOD和甘露醇的保护作用。结果显示γ射线及0_2~(·-)都能诱发细胞SCE频率显著升高,且存在一定的剂量-效应关系。SOD及甘露醇对0_2~(·-)诱发的损伤有明显的保护作用。     

国内外海绵钛生产工艺现状

海绵钛生产的原则工艺流程为钛精矿→电炉熔炼钛渣→氯化→粗TiCl4精制→还原蒸馏→海绵钛。本文论述了该工艺流程中各海绵钛生产国所采取的独具特色的成熟技术。指出目前海绵钛生产发展的总趋势是：设备大型化、产能规模化、质量高纯化、控制自动化，而今后海绵钛生产的发展方向除研究探索熔盐电解法等新的技术方法外，重点还是对镁法更进一步完善，并探索低成本、连续化生产的途径。     