Dependence of dielectric properties on BT particle size in EP/BT composites

The polymer-ceramic composites of epoxy resin (EP) and barium titanate (BT) were prepared.BT powders of different BT particle sizes from 100 nm to 1 μm were used in the preparation.The dielectric properties, such as dielectric constant, dielectric loss and electrical breakdown strength, of the EP/BT composites were studied.The morphology of the composites was characterized by the means of scanning electron microscopy (SEM).The results show that the dielectric constant of the composites is much higher than the epoxy matrix at frequency range from 1 kHz to 10 MHz, and it is also obviously dependent on the size of BT particles.The electrical breakdown strength of the composites decreases with the increase of the BT content.The dependence of electrical breakdown strength on BT particle sizes was also discussed.     

单片机控制的电阻钎焊系统

在电阻钎焊基本原理的基础上，介绍了利用AVR单片机设计开发的电阻钎焊控制系统，分析了单片机的软硬件结合。 时给出了利用热电偶放大和数字转换器MAX6675采集和处理温度信号的基本连接电路并分析了其优点。     

LD7铝合金热变形行为的实验研究

在G1eeble-1500热模拟试验机上对LD7铝合金试样在变形程度为60％，变形温度为360～480℃、变形速率为0．0l～1s^-1的条件下进行等温压缩试验，然后对其进行固溶处理。根据试验结果分析热变形参数对合金流动应力和固溶之后显微组织的影响，可以得到如下结论：LD7铝合金是动态回复型合金，合金的流动应力随温度的升高而降低，随应变速率的升高而升高；合金的晶粒尺寸随温度的升高而增大，随变形程度和变形速率的增大而减小。     

异形坯连铸坯壳应力与鼓肚变形分析

坯壳应力引起的鼓肚变形是影响铸坯质量的重要因素,为防止过大的鼓肚变形,依据湍动能理论、热流传递理论和粘弹性理论,建立了异形坯三维热-力耦合模型,开发了鼓肚分析软件,从而避免了漏钢事故的发生.该模型将温度场和应力场的计算相互耦合,交替进行.结果表明:异形坯截面最危险点位于腹板中部,其次为翼板中点,在两者相结合的圆角部,由于凝固坯壳比较薄,其应力值也比较大;当坯壳厚度小于20 mm时,两点的鼓肚变形量将分别超过其极限变形量,铸坯出结晶器时必然发生漏钢事故.该模型通过预测坯壳应力和鼓肚变形量为现场安全生产提供了理论依据.     

Impact toughness of tungsten films deposited on martensite stainless steel

Tungsten films were deposited on stainless steel Charpy specimens by magnetron sputtering followed by electron beam heat treatment. Charpy impact tests and scanning electron microscopy were used to investigate the ductile-brittle transition behavior of the specimens. With decreasing test temperature the fracture mode was transformed from ductile to brittle for both kinds of specimens with and without W films. The data of the crack initiation energy, crack propagation energy, impact absorbing energy, fracture time and deflection as well as the fracture morphologies at test temperature of-70 ℃ show that W films can improve the impact toughness of stainless steel.     

直齿圆柱齿轮温挤压成形的数值模拟

用优化后的凹模结构对直齿圆柱齿轮的温挤压成形进行了数值模拟 ,结果表明 ,以入模角为 180°、挤压筒内径等于直齿轮齿顶圆直径 ,且在齿根圆处不倒角为特点的凹模形式对齿形成形效果良好 ,此种凹模形式能够解决齿形角隅充不满的难题 ,非常适合直齿圆柱齿轮的挤压精密成形     

新型手机用PCB板焊点的失效分析

采用多种宏微观分析手段,对新型手机用PCB板的失效焊点(BGA)与散落焊珠的组分进行了系统的表征分析.结果表明,表面贴装技术(SMT)回流焊工艺参数控制不当是主要的失效起因;焊膏质量不佳及回流焊工艺与其不匹配是导致焊点焊块失效的另一重要原因.针对上述问题,就回流焊工艺参数的调整以及焊膏质量的改善提出了具体建议,以确保该PCB板的结构完整性和安全可靠性.     

镁热还原法制备超微细无定形硼粉

以B2O3为原料,Mg粉为还原剂,通过自蔓延镁热还原反应获得还原产物,经过对还原产物的盐酸溶浸后,制备出超微细无定形硼粉.研究镁热还原工艺对产物的影响,利用激光粒度分析仪测定无定形硼粉的粒径,用静态表面吸附仪测定77.3 K下硼粉的氮吸附等温曲线,通过XRD和SEM分别对还原产物和无定形硼粉的物相及形貌进行分析.结果表明在B2O3-Mg体系中,影响硼粉纯度的杂质主要是反应过程中生成的酸不溶物MgBx、BxO、Mg2SiO4、FeBx及较难溶物xMgO.B2O3等,在镁热还原过程中应尽量抑制该类化合物的生成.通过优化制备工艺,在w(B2O3)/w(Mg)为3.0的条件下,制备出硼含量为94.6%、比表面积8.2 m2/g、等效粒径0.36 μm的形貌不规则的超微细硼粉.     

激光焊接齿科CoCr-NiCr异种合金组织结构研究

选用齿科烤瓷用NiCr合金和支架用CoCr合金,利用脉冲Nd-YAG激光,在不同电压下进行焊接,考察焊件力学性能,优选电压条件,研究此条件下焊件熔焊区及其附近区域化学成分、显微组织变化规律.结果表明,适合齿科临床应用焊接电压为280V,此条件下可以得到显微组织致密、细小的熔焊区,熔焊区与两侧母材呈冶金结合,主要成分为Ni元素,以固溶体和化合物形式存在;Co、Cr元素部分溶入固溶体,部分与Mo、Be形成化合物.焊接中冶金过程充分,无新相生成.双向侧吹氩气可以对熔焊区起到良好的保护作用,无氧化物形成.