Structure and properties of CE/CTBN/EP blends: II. Effect of EP on the mechanical properties and thermostability of the CE/CTBN system

Carboxyl‐terminated butadiene‐acrylonitrile rubber (CTBN) has often been used to improve the toughness of cyanate ester (CE) resin while sacrificing modulus and thermostability. In this paper, the addition of the appropriate amount of epoxy resin (EP) to the CE/CTBN system is shown to not only increase the modulus and thermostability of the blend, but also improve the toughness. The values of impact strength showed a maximum for the CE/CTBN/EP 100/5/5 blend. The temperature of 10 % weight loss (T₁₀) improves from 376 °C for CE/CTBN 100/5 to 407 °C for the CE/CTBN/EP 100/5/2.5 blend. It is proposed that addition of the appropriate amount of EP can decrease the mobility and increase the stability of CTBN via the reaction between the terminal carboxyl group of CTBN and the hydroxyl group of EP. But a very high EP concentration will decrease the crosslinking density of CE, consequently reducing the mechanical properties and thermostability of the blends. Copyright © 2004 Society of Chemical Industry     

Morphology and properties of poly[2‐methoxy‐5‐(2′‐ethyl‐hexyloxy)‐para‐phenylene vinylene]/silica nanoparticle hybrid films

Poly[2‐methoxy‐5‐(2′‐ethyl‐hexyloxy)‐para‐phenylene vinylene] (MEH‐PPV)/silica nanoparticle hybrid films were prepared and characterised. Three kinds of materials were compared: parent MEH‐PPV, MEH‐PPV/silica (hybrid A films), and MEH‐PPV/coupling agent MSMA/silica (hybrid B films), in which MSMA is 3‐(trimethoxysilyl) propyl methacrylate. It was found that the hybrid B films could significantly prevent macrophase separation, as evidenced by scanning electron and fluorescence microscopy. Furthermore, the thermal characteristics of the hybrid films were largely improved in comparison with the parent MEH‐PPV. The UV‐visible absorption spectra suggested that the incorporation of MSMA‐modified silica into MEH‐PPV could confine the polymer chain between nanoparticles and thus increase the conjugation length. The photoluminescence (PL) studies also indicated enhancement of the PL intensity and quantum efficiency by incorporating just 2 wt% of MSMA‐modified silica into MEH‐PPV. However, hybrid A films did not show such enhancement of optoelectronic properties as the hybrid B films. The present study suggests the importance of the interface between the luminescent organic polymers and the inorganic silica on morphology and optoelectronic properties. Copyright © 2004 Society of Chemical Industry     

Criteria for evaluation of the hardening factor of machine parts

V. Ya. Chubar' Zaporozhe Machine Building Institute. Translated from Problemy Prochnosti, No. 3, pp. 62–65, March, 1989.     

High-strain-rate superplasticity of nanocrystalline aluminum alloy 1570

The structure and mechanical properties of nanocrystalline aluminum alloy 1570 obtained by means of severe plastic deformation have been studied. Being tested in a temperature range from 300 to 400°C, the alloy exhibits high-strain-rate superplasticity. At 400°C, the superplasticity is manifested in a very broad range of strain rates, extending from 5 × 10^?3 to 1 s^?1.     

Filled Fibrous Sorbents Modified with Transition Metal Ferro- and Ferricyanides for Recovery of Americium and Rare-Earth Metals

Filled fibrous sorbents modified with transition metal ferro- and ferricyanides capable to recover americium(III) and rare-earth metals(III) from nitric acid solutions were prepared. The most complete and rapid recovery is attained on complex-forming and cation-exchange sorbents (as filled fibrous materials) saturated with nickel ions. The sorbents are characterized by good kinetic properties and can be used for recovery of the above metals.     

Factors of large graphite crucible life

Production methods used to prepare graphite crucibles with high operating properties are considered: use as a filler of good graphitizing acicular coke, vibration molding of the original coke mix, use of production cycles for impregnation with medium temperature coal-tar pitch — firing, firing of compacted billets in metal containers, graphitization of fired billets in graphite cylinders. The last two production methods make it possible to reduce the temperature drop throughout the volume of a billet during heat treatment, and as a consequence to reduce crack development to a minimum as a result of reducing thermal stresses. All of the production methods recommended may be entirely accomplished in existing electrode plants and may be used to increase markedly the quality crucible graphite. It is possible to achieve a quality for these materials at the best world level. Translated from Novye Ogneupory, No. 8, pp. 28–33, August 2008.