Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

Establishment of a color tolerance for yarn-dyed fabrics from different color-depth yarns

Yarn-dyed fabric is often woven from warp and weft yarns in the same color depth to ensure a uniform color appearance. The difference in color depth between warp and weft tends to result in the uneven color of the yarn-dyed fabric. This article aims to establish a color tolerance for yarn-dyed fabric that can be woven with a qualified color appearance but from the warp and weft yarns in different color depths. A total of 27 yarn-dyed fabric samples in three color series (red, yellow, and blue) were evaluated by using the yarn-dyed fabric from warp and weft yarns in the same color depth of 2% (on weight of fabric, owf) as the standard. Visual assessment and instrumental measurement of color were carried out to establish the color tolerance ellipse that was defined as CMC (Color Measurement Committee) color differences (2:1) of no more than 1.00. It was found that the color strengths (K/S) and color differences (ΔE_CMC(2:1)) of these fabric samples for each color series had linear relationships with the color depths of warp and weft yarns. The color tolerance ellipses indicated that, even though the warp and weft yarns had an apparent color difference, they could be woven in fabrics with relatively uniform color appearance and meet the requirements for yarn-dyed fabric. This work provided valuable insight into the production of qualified yarn-dyed fabrics from unqualified dyed yarns.     

Porous Co3O4 column as a high-performance Lithium anode material

Journal of Porous Materials - Co3O4 has been widely investigated as a promising candidate anode material for lithium-ion batteries. We report on the porous Co3O4 column synthesized via a simple...     

The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

High energy storage and ultrafast discharge in NaNbO3-based lead-free dielectric capacitors via a relaxor strategy

Dielectric capacitors with decent energy storage and fast charge-discharge performances are essential in advanced pulsed power systems. In this study, novel ceramics (1-x)NaNbO₃-xBi(Ni_2/3Nb_1/3)O₃(xBNN, x = 0.05, 0.1, 0.15 and 0.20) with high energy storage capability, large power density and ultrafast discharge speed were designed and prepared. The impedance analysis proves that the introducing an appropriate amount of Bi(Ni_0·5Nb_0.5)O₃ boosts the insulation ability, thus obtaining a high breakdown strength (E_b) of 440 kV/cm in xBNN ceramics. A high energy storage density (W_total) of 4.09 J/cm³, recoverable energy storage density (W_rec) of 3.31 J/cm³, and efficiency (η) of 80.9% were attained in the 0.15BNN ceramics. Furthermore, frequency and temperature stability (fluctuations of W_rec ≤ 0.4% over 5–100 Hz and W_rec ≤ 12.3% over 20–120 °C) were also observed. The 0.15BNN ceramics exhibited a large power density (19 MW/cm³) and ultrafast discharge time (~37 ns) over the range of ambient temperature to 120 °C. These enhanced performances may be attributed to the improved breakdown strength and relaxor behavior through the incorporation of BNN. In conclusion, these findings indicate that 0.15BNN ceramics may serve as promising materials for pulsed power systems.     

Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Optical and electrical properties of ITO film on flexible fluorphlogopite substrate

Indium Tin Oxide (ITO) films were prepared, at room temperature, on a fluorphlogopite substrate using magnetron sputtering technology. At various temperatures of 500 °C, 600 °C, 700 °C, 800 °C, and 900 °C, the samples were (had) annealed for 2 h (a 2-h duration). The results showed improvement in the crystalline performance of ITO film at selected annealing temperatures, with a significant reduction in resistivity at 800 °C. The lowest resistivity is 4.08 × 10^?4 Ω-cm, which is nearly an order of magnitude lower than the unannealed sample. All samples have an average light transmittance above 85% in the visible light range (400–800 nm), and with increasing annealing temperature, the average light transmittance tends to decrease. Besides, at the sensitive wavelength of 550 nm, the light transmittance is as high as 93.74%. The sheet resistance testing of the sample was through the number of bending times, which revealed that with the increase of the number of bending, the sheet resistance increases. However, after 1200 bending times, the change rate of the sheet resistance remains below 5%. Thus, the ITO film prepared on the flexible fluorphlogopite substrate revealed excellent optical and electrical properties, good flexibility, and improved stability after high-temperature annealing, which guarantees successful application in flexible electronic devices.     

Surface Reconstruction Engineering with Synergistic Effect of Mixed-Salt Passivation Treatment toward Efficient and Stable Perovskite Solar Cells

Surface passivation treatment is a widely used strategy to resolve trap-mediated nonradiative recombination toward high-efficiency metal-halide perovskite photovoltaics. However, a lack of passivation with mixture treatment has been investigated, as well as an in-depth understanding of its passivation mechanism. Here, a systematic study on a mixed-salt passivation strategy of formamidinium bromide (FABr) coupled with different F-substituted alkyl lengths of ammonium iodide is demonstrated. It is obtained better device performance with decreasing chain length of the F-substituted alkyl ammonium iodide in the presence of FABr. Moreover, they unraveled a synergistic passivation mechanism of the mixed-salt treatment through surface reconstruction engineering, where FABr dominates the reformation of the perovskite surface via reacting with the excess PbI₂. Meanwhile, ammonium iodide passivates the perovskite grain boundaries both on the surface and top perovskite bulk through penetration. This synergistic passivation engineer results in a high-quality perovskite surface with fewer defects and suppressed ion migration, leading to a champion efficiency of 23.5% with mixed-salt treatment. In addition, the introduction of the moisture resisted F-substituted groups presents a more hydrophobic perovskite surface, thus enabling the decorated devices with excellent long-term stability under a high humid atmosphere as well as operational conditions.     

“电工学”国家级一流课程建设与实践

根据新时代新工科人才需求特点和电工学课程特点,分析非电专业学生的电类实践需求,提出构建电工学课程为核心的电工电子实践创新能力培养新体系。通过优化教学内容、开展教学模式和考核模式改革、构建教学资源体系和进行教师队伍建设,使我校电工学课程教学质量提升、学生工程实践和创新能力提高、学生满意度增加、一流课程建设成效显著。