Relation between crystal structure and lattice oxygen content of sintered reaction-bonded silicon nitride

When reaction-bonded silicon nitride containing MgO/Y₂O₃ additives is sintered at three different temperatures to form sintered reaction-bonded silicon nitride (SRBSN), the thermal conductivity increases with sintering temperature. The β-Si₃N₄ (silicon nitride) crystals of SRBSN ceramics were synthesized and characterized to investigate the relation between the crystal structure and the lattice oxygen content. The hot-gas extraction measurement result and the crystal structure obtained using Rietveld analysis suggested that the unit cell size of the β-Si₃N₄ crystal increases with the decrease in the lattice oxygen content. This result is reasonable considering that the lattice oxygen with the smaller covalent radius substitutes nitrogen with the larger one in the β-Si₃N₄ crystals. The lattice oxygen content decreased with increasing sintering temperature which also correlated with increase in thermal conductivity. Moreover, it is noteworthy from the viewpoint that it may be possible to apply the lattice constant analysis for the nondestructive and simple measurement of the lattice oxygen content that deteriorates the thermal conductivity of the β-Si₃N₄ ceramics.     

Negative ion etching of Al−Si−Cu by employing a magnetic filter in halogen plasmas

Al etching was studied employing negative ions generated in downstream Cl₂ plasma. The Al etch rate by the alternate irradiation of positive and negative ions was two times higher than that by usual positive ions. In order to etch the Al film practically on an insulator covered electrode coupled with RF power, reduction of the negative self bias voltage (Vdc) was examined using a magnetic filter which traps electrons. The reason for the high etching reactivity is that the dominant negative ions F in SF₆ and Cl⁻ in Cl₂ plasmas are atomically very similar to the radicals. Addition of SF₆ and H₂ to a Cl₂/BCl₃ mixture reduced Vdc significantly. However, fluorine and hydrogen atoms inhibited Al etching in spite of sufficient ion energy.     

Evolution of patinas on copper exposed in a suburban area

Copper plates were exposed under sheltered outdoor conditions for up to one year, starting in September 2001 in Musashino City, Tokyo, a suburban area. Following various periods of exposure, the patinas on the plates were characterized to investigate their evolution by using X-ray fluorescence analysis, X-ray diffraction, field emission scanning electron microscopy, and glow discharge optical emission spectroscopy. The difference in the roles of sulfur and chlorine in the early stages of copper patination were identified by analyzing the depth profiles of these two elements. Sulfur was found on top of the patina as cupric sulfates such as posnjakite (Cu₄SO₄(OH)₆ · H₂O) or brochantite (Cu₄SO₄(OH)₆). Brochantite appeared only after 12 months of exposure. In contrast, chlorine was found on the surface after only one month of exposure. It gradually penetrated the patina as the exposure period lengthened, forming copper chloride complexes. Chloride ions accumulated at the patina/copper interface, forming nantokite (CuCl), which promoted corrosion.     

Differences between corrosion products formed on copper exposed in Tokyo in summer and winter

We analyzed the copper corrosion products that formed during a month in summer and a month in winter at three sites in Tokyo using several analytical techniques. The X-ray diffraction patterns revealed that cuprite Cu₂O and posnjakite Cu₄SO₄(OH)₆·H₂O formed on copper exposed in summer. By contrast, only cuprite was found in winter exposed copper. The X-ray fluorescence results indicated that the amounts of sulfur and chlorine on the copper plates exposed in summer were much greater than those in winter. This could be explained by the change in particulate sulfate and sea salt concentrations. Depth profiling analysis by Auger electron spectroscopy revealed that the oxide layer formed in summer was thicker than that in winter. This difference in oxide layer thickness could have been due to the differences in temperature, relative humidity, and the amount of sulfur and chlorine on the copper plate.     

Microstructure Control of Thermally Sprayed Co-Based Self-Fluxing Alloy Coatings by Diffusion Treatment

This article describes microstructure control aimed for wear-resistance improvement of Co-based (Co-Cr-W-B-Si) self-fluxing alloy coating by diffusion treatment. The diffusion treatments of thermally sprayed Co-based self-fluxing alloy coating on steel substrate were carried out at 1370-1450 K for 600-6000 s under an Ar gas atmosphere. Microstructural variations of the coating and the interface between the substrate and the coating were investigated in detail. A proper diffusion treatment precipitates two kinds of fine compounds in Co-based matrix. X-ray diffractometer (XRD) and electron probe microanalyzer (EPMA) analysis revealed these precipitates to be a chromium boride dissolving cobalt and a tungsten boride containing cobalt and chromium. The size of each precipitate became larger with increasing treatment temperature and time. A coating with the proper size borides showed a superior wear-resistance. This article is an invited paper selected from presentations at the 2007 International Thermal Spray Conference and has been expanded from the original presentation. It is simultaneously published in Global Coating Solutions, Proceedings of the 2007 International Thermal Spray Conference, Beijing, China, May 14-16, 2007, Basil R. Marple, Margaret M. Hyland, Yuk-Chiu Lau, Chang-Jiu Li, Rogerio S. Lima, and Ghislain Montavon, Ed., ASM International, Materials Park, OH, 2007.     

Repeatedly foldable AMOLED display

In this study, a 5.9‐inch foldable active‐matrix organic light emitting diode (AMOLED) display was developed. A folding test was performed repeatedly. The display survived the folding test (100,000 folds) with a curvature radius of 2 mm. To protect an organic light emitting diode (OLED) against moisture, inorganic passivation layers are provided on the upper and lower sides of the flexible display. Using our transfer technology, high density passivation layers can be obtained. The measured water vapor transmission rate of the layer is 7 × 10^?6 g/m²?day or less, which improves OLED reliability. With these techniques, we have developed a book‐type display, which is repeatedly foldable like a book, and a tri‐fold display including a display area, which is foldable in three.     

Reliability and mechanical durability tests of flexible OLED with ALD coating

To improve the reliability and mechanical durability of a flexible organic light‐emitting diode display, the entire flexible display is coated with an aluminum oxide film by atomic layer deposition (ALD). Because the step coverage of ALD is excellent, the AlO_x film was deposited not only on the front and back surfaces but also on the side surfaces of the display. A high‐temperature and high‐humidity preservation test, repetitive bending tests, and a pencil hardness test were conducted on the flexible display with ALD‐AlO_x coating. The display survived 500 h of a 65°C, 95% preservation test, endured a 100,000‐time repetitive bending test with a curvature radius of 4 mm, and was found to have a pencil hardness of 4H.     

Finger Braille teaching system-teaching of prosody of finger Braille

Finger Braille is one of tactual communication media of deaf-blind people. Deaf-blind people who are skilled in Finger Braille can catch up with speech conversation, because of prosody of Finger Braille. Features of prosody are： （1） characters at the end of clauses are dotted long; （2） characters of voiced sounds and double consonants are dotted shortly. In this paper, we designed three teaching patterns which taught prosody of Finger Braille （dot conditions about duration of dotting）. Teaching pattern 1 indicated a dot pattern with colored solid background. Teaching pattern 2 indicated a dot pattern with colored empty background. Teaching pattern 3 indicated a dot pattern with colored arrow （long or short）. Every teaching pattern includes 6 colors （red, orange, yellow, green, blue and purple）. In the questionnaire, the yellow pattern of teaching pattern 3 was selected as the most visible pattern. In the evaluation experiment, the yellow pattern of teaching pattern 3, the red and purple patterns of teaching pattern 1 （the least visible pattern） and the existing patterns without teaching of dot conditions are compared. As a result, every subject could dot long at the end of clauses and could dot shortly at the voiced sounds and double consonants. The answers of questionnaire indicated that the yellow pattern of teaching pattern 3 was also the most visible and easiest teaching pattern.     

Superconductivity in the tetragonal phase of La1.9Bi0.1CuO4+δ annealed under high oxygen pressure

We have investigated the relation between the crystal structure and superconductivity in La_1.9Bi_0.1CuO₄₊ , in which the phase separation observed in La₂CuO₄₊ is suppressed. A phase diagram in theT– plane is given for La_1.9Bi_0.1CuO₄₊ with excess oxygen. For very small values, the crystal structure is orthorhombic, and an orthorhombic-tetragonal phase transition occurs markedly at 0.03 in the measured temperature range between 13 and 293 K. Superconductivity is observed in the range of 0.04<<0.11. This is clear evidence thathigh-T _c superconductivity also appears in the tetragonal phase.     

Numerical simulation of molding-defect formation during resin transfer molding

The present study investigated a numerical simulation of molding-defect formation during resin transfer molding using boundary element method and line dynamics. The proposed method enables to simulate small molding defects by increasing the node for required position during time evolution; thereby, the method computes high-resolution flow front without being affected by the initial mesh geometry. The method was applied to the radial injection RTM with single inlet, and it was confirmed by comparison with theoretical value based on Darcy’s law that the flow advancement was computed with high accuracy. In addition, the method was also applied to the flow advancement for inclusion problem with cylinder, and four-point injection problem. The simulated flow behavior, void formation, and shrinkage agreed with the results in references. Finally, the method was compared with experiments using two-point injection problem. The computed configuration of the flow front and weld line agreed well with the experimental results.