AN ELECTRON DIFFRACTION ANALYSIS OF PRECIPITATES IN A 13Ni MARAGING STEEL (280kgf/mm~2)

用X射线衍射,选区电子衍射和σ及δ相与马氏体基体之间的取向关系,鉴别了13Ni(280kgf/mm~2)马氏体时效钢的析出物。 13Ni(280kgf/mm~2)马氏体时效钢强化析出物是金属间化合物δ-(Fe,Ni,Co)Mo。锻造状态时效后还析出μ相使韧性恶化。过时效后(例如580℃ 16h空冷)形成逆转变奥氏体。时效状态样品在电子显微镜里加热至743℃时,发现粗大的δ相颗粒和长条状的σ相颗粒。 虽然衍射花样常常可以指标化成δ或σ相,但根据δ/α和σ/α之间取向关系的差别很容易区分δ和σ相。     

Properties and Microstructuresof Three Kinds of Silversheathed Bi-2223 Tapes

ＰｒｏｐｅｒｔｉｅｓａｎｄＭｉｃｒｏｓｔｒｕｃｔｕｒｅｓｏｆＴｈｒｅｅＫｉｎｄｓｏｆＳｉｌｖｅｒｓｈｅａｔｈｅｄＢｉ－２２２３ＴａｐｅｓＺｅｎｇＲｏｎｇ；ＺｈｏｕＹｉｒｕ；ＹｅＢｉｎ；ＺｈｏｕＭｉｎ；ＺｈａｎｇＪｉａｎｇｕｏ（曾荣）（周贻茹）（叶斌）...     

550 MPa级中厚板矫直过程中表面凹坑缺陷的成因与对策

针对550 MPa级高强中厚板在矫直过程中极易出现氧化铁皮压入凹坑缺陷的问题，根据现场矫直工艺，研究了在不同温度下进行热变形时试样表面和横截面的形貌，钢基体与氧化铁皮界面处平直度的变化规律。结果表明，热变形温度为450 ℃时，表面氧化铁皮开始出现裂纹，且随着变形温度的降低，裂纹的数量逐渐增加；此外，氧化铁皮与钢基体之间的界面长度随变形温度的降低而呈直线增加，表明氧化铁皮与钢基体界面平直度随着热变形温度的降低越发粗糙、易脱落而形成凹坑缺陷。为此，应适当提高终轧温度以确保矫直时钢板表面温度大于450 ℃，同时提高钢板的运行速率，防止氧化铁皮在低温变形发生破碎和脱落的同时降低氧化铁皮厚度，从而减小因氧化铁皮脱落而造成凹坑缺陷的发生几率。     

化学冶金因素对埋弧焊焊缝硫磷含量的影响

通过试验和理论分析，探讨了在埋弧焊过程中，熔池中Ｓ，Ｐ的脱去过程，主要是以分别生成硫酸盐和磷酸盐的形式进行的化学冶金反应，并提出了熔池中的硫，磷脱去过程存在一个极限值，而这个极限值与焊剂的碱度和焊剂，焊丝及母材中的硫，磷含量有关。在焊剂碱度ＢＩ≥２．５的高碱度焊剂中，根据焊丝或焊剂中硫含量的不同，熔敷金属中硫的的极限值可低于焊丝中的硫含量或接近焊剂中的硫含量；而磷的极限值为０．０１０％±０．００２     

半固态灰铸铁的制备与显微组织

建立了一种不需搅拌和其它附加处理的半固态灰铸铁制备技术 ,用浇注前合理调整熔体温度或调温 适当快冷的铸造方法 ,并配以合适的凝固冷却速度 ,成功地制备了球状初生奥氏体圆整、尺寸细小、分布均匀的半固态亚共晶灰铸铁 ,得到了最佳工艺条件 ,并用铸铁金相计算机辅助检测系统 ,对初生奥氏体的形状系数和等效直径进行了测量与统计分析 ,定量描述了半固态组织的特性     

Model of intense pulsed ion beam and simulation study of energy deposited on target

Gaussian type models have been established according to the real detected voltage of magnetically insulated ion diode and intense pulsed ion beam density near the focus of the diode. The energy deposition of Al target irradiated by intense pulsed ion beam has been simulated by Monte Carlo method based on these models. The results of energy depositions of the irradiation of single energy ions and the Gaussian distribution IPIB have been obtained. Especially cases of ion beam irradiating Al target at different angles on one dimension and two dimensions are discussed. The evolution processes of the energy deposition of ions in target have been simulated during a pulse. In addition, incident angles of H⁺ ions and C⁺ ions ranging from 20 to 40° have been researched. We obtained the conclusions that C⁺ ions of the beam affect the physical properties of near surface region, but H⁺ ions affect the deeper layer. The energy of intense pulsed ion beam mainly deposits on target surface, so melting and evaporation begin both from target surface.     

北美和欧洲消失模铸造发展现状

2001-2002年美国和德国相继召开了3个有关消失模铸造研讨会，共交流45篇报告。报告归纳出北美和欧洲在消失模铸造研究上有3大热点：开展消除铝合金消失模铸造缺陷的研究；完善发泡模具及白区制模技术；探索消失模铸造模拟和快速原型制造技术。介绍了国外消失模铸造企业现状，指出我国消失模铸造与世界先进消失模技术的3大差距。     

DZG-10焦化汽油加氢精制催化剂的开发和工业应用

介绍了DZG-10焦化汽油加氢精制催化剂的开发过程和工业应用。通过对载体的改性，提高了大孔所占比例,将催化剂外形改为齿球形，增大了催化剂的外表面积，提高了催化剂的活性和机械强度。从连续平稳运转26个月情况来看，催化剂床层压差较低，说明催化剂床层结垢、结焦和催化剂破损情况不明显。开发的DZG-10催化剂是一种优良的纯焦化汽油加氢精制催化剂，具有较好的应用前景。     

兰香草挥发油化学成分的研究

采用常压水蒸气蒸馏法提取了兰香草挥发油,得油率为 0.35 ~ 0.52%。其相对密度(20℃/4℃)0.9980 ~0.9900,折射率(20℃)1.4608,比旋光度+0.51°;酸值1.5。并用毛细管气相色谱、红外光谱、核磁共振谱和色-质联机等对该挥发油进行了系统的成分分析。在分出的112个色谱峰中,共鉴定出 71 个化合物,占挥发油总量的 94.6%。其主要成分为芳樟醇、紫苏醇、香芹酮、荠苎烯、4-甲基-6-庚烯-3-酮、葎草烯、马鞭草烯酮、左旋松香芹酮、2-壬烯-4-炔等。     

高岭土改性聚酯纤维

介绍了高岭土在改性聚酯中的作用、纤维级高岭土的性质以及改性聚酯的制造方法．指出了我国开发高岭土改性聚酯纤维的的前景．