采用新的陶瓷工艺技术,在气氛保护条件下,通过固相烧结反应法制备出温差电多晶材料。对膺三元固溶体化合物 P 型(72%Sb_2Te_3+25%Bi_2Te_3+3%Sb_2Se_3)和 N 型(90%Bi_2Te_3+5%Sb_2Te_3+5%Sb_2Se_3)的掺杂陶瓷样品进行了性能与结构研究。找到了最佳工艺制度。样品性能参数为:N 型:α=186μV/K σ=1250Ω~(-1)·cm~(-1) λ=14.7mW/(cm.K) Z=2.9×10~(-3)/KP 型:α=220μV/K σ=900 Ω~(-1)·cm~(-1) λ=14.0mW/(cm.K) Z=3.1×10~(-3)/K     

Fracture of Aramid Fiber/Epoxy Resin Micro Composites

Kevlar-49 fiber was modified through cold air plasma treatment and plasma grafting with acrylic monomers. Fracture of aramid fiber/epoxy resin micro composites has been studied by means of single fiber pull-out test. Tow types of pull-out curves are correlated with the different failure modes. A polyacrylic acid-co-ethyl acrylate graft layer can improve the adhesion and protect the fiber from damage caused by interfacial stresses.     

一种碳－碳复合材料长寿命防氧化涂层的失效机制

用液相法联合ＣＶＤ法和硅化法制备了一种碳－碳复合材料复合梯度涂层，在此基础上对这种涂层在氧化过程中的失效机制进行了研究．结果表明：氧化层与液相层界面反应生成的气相产物是涂层失效的根本原因界面上气泡的不均匀形核、长大和破裂导致涂层表面出现孔洞．孔洞处气泡优先形核、长大和破裂并发展成为缺陷而使涂层失效     

ANALYSIS ON ROOM TEMPERATURE TENSILE STRENGTH OF δ-Al_2O_3, FIBER / Al-12Si COMPOSITE

对δ－Ａｌ２Ｏ３纤维／Ａｌ－１２Ｓｉ复合材料室温拉伸强度的分析表明，在实验条件下该复合材料存在δ－Ａｌ２Ｏ３纤维的最小体积分数Ｖｍｉｎ和临界体积分数Ｖｃｒｉｔ，并求出其基体强度δｍ和室温强度σｃ－δ－Ａｌ２Ｏ３纤维体积分数Ｖｆ直线方程及纤维的临界长度ｌｃ和复合材料的剪切应力τＰ确定复合材料的ＲＯＭ预测曲线，应首先判断σｍ是否等于未增强合金的强度σｕｍ才能得出正确的结论。     

化学键性质机械合金化过程中非晶形成能力的影响

研究了Ｂ２型金属间化合物ＦｅＡｌ和ＦｅＴｉ的机械合金化过程，发现的相同的试验条件下，ＦｅＡｌ形成化学无序的固溶体，ＦｅＴｉ形成结构无序的非晶态，此现象可用ＦｅＡｌ的化学键为金属－离子混俣键，而ＦｅＴｉ的化学键为金属－共价－离子混合键来解释。     

湿化学法制备纳米ATO导电粉

采用非均相成核法 ,在Sn(OH) 4 晶种上均匀生长Sb掺杂Sn(OH) 4 ,制备纳米ATO粉末。以电阻测定系统研究了合成条件如掺杂浓度、反应温度、pH值、SnCl4浓度等对最终粉末电阻性能的影响。以TG DSC热分析、XRD、TEM等手段研究了晶粒生长过程 ,XRD显示为四方金红石型结构 ,平均粒径为15nm。当Sb/Sn(mol比 ) =0 .0 5 ,pH =2 ,T =60℃ ,SnCl4=1.2～ 1.8mol·L-1时 ,粉体电阻小于 0 .5Ω。     

80钢盘条拉拔断裂原因分析

用扫描电镜、金相显微镜观察分析了80钢盘条拉拔断裂的断口，并对盘条进行了理化检验分析。结果表明，盘条组织中较多的网状二次渗碳体是盘条在拉拔过程中脆断的主要原因。     

Thermal Characterization of 1.3 μm InAsP/InGaAsP Ridge Waveguide MQW Lasers Based on Spectroscopy Method

An experimental way to analyze the thermal characterization of semiconductor lasers based on spectroscopy method under pulse driving conditions has been developed. By using this way the thermal characteristics of strain compensated 1.3 μm InAsP/InGaAsP ridge waveguide MQW laser diodes have been investigated. Results show that by measuring and analyzing the lasing spectra under appropriate driving parameters and temperature ranges, the thermal resistance of the laser diodes could be deduced easily. A higher thermal resistance of 640 K/W has been measured on a narrow ridge laser chip without soldering. Other thermal and spectral properties of the lasers have also been measured and discussed.     

实证分析:上市公司资本结构的影响因素

在国内外相关研究的基础上，利用我国资本市场的公开数据，对上市公司资本结构的影响因素进行实证研究，得出了若干重要结论。     

稠油油藏的注汽量预测

利用HCZ预测模型，可对已开发油田的年产量和累计产量进行全程预测，并且在实际应用中取得了较好的预测结果。本文结合稠油田的实际情况，推导出HXZ预测模型在热采中注汽参数的预测公式。结合曙光油田曙1－7－5块的开发数据进行了预测，效果较好。