5，11-二乙基吲哚[3，2-b]咔唑的合成及光谱特性

以苯肼为原料,与1,4-环己二酮反应,制得环己胺-1,4-二酮一二苯腙,再在硫酸、醋酸强酸性环境下闭环制得吲哚[3,2-b]咔唑,经N-烷基化反应制得乙基取代基的吲哚[3,2-b]咔唑衍生物．本文合成方法使其产率由参考文献的64％提升到80％,其结构经’HNMR表征,并初步研究了该化合物的光谱性质．     

锂离子电池用层状LiMnO_2的合成及性能

采用离子交换法合成了准确化学计量比的层状LiMnO2锂离子电池正极材料.通过热重分析确定了前驱体NaMnO2的焙烧温度为800℃,通过XRD测试确定了前躯体的焙烧时间为48 h.采用电子扫描电镜测试LiMnO2材料的颗粒平均粒径为3μm.在2.0～4.5 V(vs Li/Li+)条件下进行充放电测试,结果表明LiMnO2经过50次循环后,放电比容量仍可达到125 mAh/g(0.2 C).     

锂离子电池正极材料LiNi_(0.8)Co_(0.2)的掺杂改性研究

采用共沉淀法和成LiNi0.8Co0.2O2,探讨影响锂离子电池正极材料LiNi0.8Co0.2O2电化学性能及结构的因素.为了提高材料的电化学性能,对材料进行了掺杂改性的研究,分别掺入Al、Mn、Mg和Fe四种元素.通过在2.8～4.2V范围内的充放电测试分析,掺入Mn的正极材料LiNi0.8Co0.1Mn0.1O2具有最高的放电比容量以及最低的容量损失,其首次放电容量为168.84 mAh/g,十次循环后的放电容量为166.9 mAh/g.     

基于“卓越计划”的运输管理学教学改革研究

运输管理学是物流工程专业核心课程之一。今依据对物流企业的调研结果,从课程定位、教材选择、课堂内容及课堂教学方法等方面进行课程教学改革研究,提出教学内容的模块化、工作项目化及驱动任务设计等环节,构建多种手段并用的课程教学体系。结果表明,教学改革充分发挥了学生的积极性和创造力,为培养出高质量的物流工程技术人才打下了基础。     

境外公共安全防恐培训的几点思考

境外公共安全防恐培训能够强化员工对境外公共安全工作的认识,提高应对境外公共安全突发事件的能力;能够普及境外公共安全管理知识,增强员工境外工作期间的个人安全意识和防卫自救能力能够制定并落实境外公共安全管理责任及措施。汉油田职培中心境外公共安全防恐培训进行了严谨的培训需求调研和定位,教材开发和内容设计更趋完善,教学方法形式多样,课件制作引人入胜,防恐演习更具针对性和实用性。但在教师的亲身体验、培训内容的选取、教学团队的师资培养、防恐演习场地设施和人员的限制等方面还需要改进。     

全液压制动系统液压制动阀的动态特性

为研究制动阀动态性能对全液压制动系统的影响,介绍了串联式双回路液压制动阀的工作原理,建立了其动态数学模型;采用AMESim软件建立了相应的仿真模型,分析了液压制动阀的制动压力比例特性、阶跃响应特性及双回路制动的安全性,并进行了实验验证．研究结果表明:制动阀仿真模型准确可信;该制动阀性能良好,能够满足全液压制动系统的要求;通过对液压制动阀控制弹簧刚度的组合优化,可以更好地适应空满载重量差别较大的整机制动需求．     

压制力及树脂加入量对重负荷砂轮内缘性能的影响

为了降低钢铁行业生产成本,提高中国钢铁行业的竞争力,开展对重负荷砂轮的研究十分必要。通过扫描电镜观察以及能谱分析,确定了进口高级重负荷砂轮的固体组分;通过改变重负荷砂轮内缘的压制力的大小和树脂的含量,对比重负荷砂轮内缘性能的影响,探究了实现重负荷砂轮内缘最佳性能的配料和成型方案。实验表明：当压制压力在450 kN,树脂含量在18%时,重负荷砂轮的体积密度、气孔率和耐压强度都处于综合最佳组合。     

Evolution and characterization of damage of concrete under freeze-thaw cycles

To study the internal damage of concrete under freeze-thaw cycles, concrete strains were measured using embedded strain gauges. Residual strain and coefficients of freezing expansion (CFE) derived from strain-temperature curves were used to quantify the damage degree. The experimental results show that irreversible residual strain increases with the number of freeze-thaw cycles. After 50 cycles, residual strains of C20 and C35 concretes are 320με and 100με in water, and 120 με and 60 με in saline solution, respectively. In lower temperature range (-10 ℃ to -25 ℃) CFE of C20 and C35 concretes decrease by 9.82×10-6/K and 8.44×10-6/K in water, and 9.38×10-6/K and 5.47×10-6/K in saline solution, respectively. Both residual strains and CFEs indicate that during the first 50 freeze-thaw cycles, the internal damage of concrete in saline solution is less than that of concrete in water. Thus residual strain and CFE can be used to measure the frost damage of concrete.     

Hydration of activated anhydrate phosphogypsum

Phosphogypsum(PG) calcined at 500 °C was activated by K₂SO₄ and salt lime with loose structure as seed crystal. To determine the effect of activation, hydration of the anhydrate PG activated was investigated by examination of the setting time, the proportion of hydrated anhydrate PG, the microstructure of the hardenite and the resistance to water. Results show that activated anhydrate PG hydrates much more rapidly than that in the absence of activators. The activated anhydrate PG has proper setting time and hydrated proportion. The resistance to water was greatly improved. SEM photos show that the set activated PG has hydrated products of rod-like and closely connected crystals. The different addition of activator leads to different compact structure.