非晶态Pd—Cu—Si合金的晶化动力学研究

本文应用DSC研究了非晶态Pd-Cu-Si合金的晶化过程动力学.根据Kissinger峰移法和Arrhenius方程分别计算了晶化激活能,发现等温晶化动力学在0.15相似文献   

Kinetics of synthesis of Li4Ti5O12 through solid-solid reaction

1. Introduction The solid-solid reaction used in synthesizing various kinds of electrochemical materials has many advantages, such as simple process, without using solvent, saving energy, friendly to the environment and easy to obtain good quality materials like nano-size materials. Recently, the manufacturing of electrochemistry materials has been paid more atten- tion due to its increasing needs. Therefore it is a natural interest to study the synthesis of electro- chemical materials by usin…     

基于I-DEAS的注塑模虚拟装配及运动仿真

在分析虚拟装配理论的基础上，利用三维设计软件I—DEAS进行了注塑模的虚拟装配和运动过程仿真，并利用二次开发语言(.prg文件)实现整体装配动态显示，对注塑模进行预装配及干涉检测，并获得了具有真实动画感的装配模型。     

Effect of sintering process on microstructure and magnetic properties of high frequency power ferrite

An oxide ceramic process was adopted to prepare high frequency manganese-zinc (MnZn) power ferrite. In combination with the microstructure analysis of material, the influences of sintering process on initial permeability (μi) and high frequency loss in unit volume (Pcv) of MnZn power ferrite were investigated. The results show that in order to obtain fine microstructure and high frequency properties, the preferable sintering temperature and atmosphere are 1230 ℃ and oxygen partial pressure ( PO2) of 4%, respectively.     

Microstructure and magnetic performance of Ni-substituted high density MnZn ferrite

The effects of NiO on microstructure and magnetic properties of Mn-Zn ferrite with a nominal composition of Zn0.32Mn0.60-xNixFe2.08O4 were investigated. The calcined powder of Mn-Zn ferrite was characterized by X-ray diffraction (XRD), the fracture surface of Mn-Zn ferrite was checked by scanning electronic microscope (SEM), and then the magnetic properties were measured. As a result, the substitution of Ni can cause the crystallattice constant of MnZn ferrite to decline, and the grain size to decrease, therefore improve the magnetic performance of MnZn ferrite whose density exceeds 5.0 g·cm-3.     

Continuous cleaning of A356 alloy melt using high frequency electromagnetic field

A set of device for electromagnetic separation (EMS) was designed and applied to process the continuous flowing melt. Tensile test was employed to compare effect of electromagnetic separation with that of the traditional processes. Compared with filtration by ceramic foam filter and process without filtration, multiple process combined with filtration and electromagnetic separation can effectively remove most of inclusions with diameter finer than 10μm in A356 alloy casting, hence improve its tensile properties. After being processed by electromagnetic filtration,the tensile strength of A356 scrap is enhanced by 8.27%, approaching the level of fresh A356 alloy.     

Influence of expandable graphite on fire resistance and water resistance of flame-retardant coatings

Expandable graphite (EG) coating and ammonium polyphosphate-pentaerythritol-melamine (APP-PER-MEL) coating were prepared. Thermal degradation and char formation of the coatings were investigated by differential thermal analysis (DTA), thermogravimetry (TG), X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results have shown that the anti-oxidation and fire-resistant properties of expandable graphite coating containing EG with size of 74 μm are better than those of APP-PER-MEL coating. The static immersion test was applied to study water resistance of the coatings, and the fire protection test and mechanical test were used to analyse heat insulation and mechanical properties of coatings before and after water immersion. The fire-resistant and mechanical properties of APP-PER-MEL coating were severely damaged by water immersion, whereas EG coating containing 8.5% EG with size of 74 μm could retain the good fire resistance even after 500 h water immersion.     

CNG储气瓶的金属磁记忆检测

使用金属磁记忆检测方法和超声方法对在役的七组公交车CNG高压储气瓶组进行了检测,并对比分析了两种方法的检测结果。结果表明,金属磁记忆方法检测到的可疑区域涵盖了超声检测到的缺陷区域,因此用磁记忆方法检测高压储气瓶,有较高的可靠性和高效性。     

大中型连杆锻件的切边、冲孔、校正工艺

在分析大中型连杆类锻件生产难点的基础上，提出了通过优化锻造工艺方案，设计了切边冲孔校正复合模。提高了带大孔的连杆类锻件的产品质量和生产效率。     

几种重氮氨基类新显色剂的合成及其与镉（Ⅱ）显色反应的研究

3种重氮氨基类新显色剂的合成及其与镉(Ⅱ)的显色反应。在表面活性剂 Triton X-100存在下,3种试剂均与镉(Ⅱ)生成络合比为3:1的红色络合物。其表观摩尔吸光系数在1.80×10~5以上。镉量在0～12μg/25mL 符合比尔定律。并对3种试剂的性能与结构的关系作了比较。将其中一种试剂(BPDAA)用于废水中痕量镉的测定,结果满意。