It has been well known that the greening of Allium sativum cloves could be formed after immersed in acetic acid solution. Nonetheless, no investigation was reported on colour development of A. sativum in response to acetic acid vapour until now. In this study, the brief exposure of A. sativum to acetic acid vapour (200–400 ppm) was combined with controlled atmosphere (5%, 20% and 80% CO₂) packaging storage to break cell membrane and green garlic. The garlic bulbs were fumigated with acetic acid before controlled CO₂ atmosphere packaging for 25 days at 4 °C. Fumigation with 200 ppm acetic acid followed by high CO₂ atmosphere packaging (80% CO₂) facilitated the garlic greening. It was also verified that γ‐glutamyl transpeptidase was involved in garlic greening in present study, and the compromise of glacial acetic acid vapour fumigation and CO₂ gas atmosphere in package stored at low temperature could result in garlic greening as well.     

Microstructure and damage evolution of SiCf/PyC/SiC and SiCf/BN/SiC mini-composites: A synchrotron X-ray computed microtomography study

SiC_f/PyC/SiC and SiC_f/BN/SiC mini-composites comprising single tow SiC fibre-reinforced SiC with chemical vapor deposited PyC or BN interface layers are fabricated. The microstructure evolutions of the mini-composite samples as the oxidation temperature increases (oxidation at 1000, 1200, 1400, and 1600?°C in air for 2?h) are observed by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction characterization methods. The damage evolution for each component of the as-fabricated SiC_f/SiC composites (SiC fibre, PyC/BN interface, SiC matrix, and mesophase) is mapped as a three-dimensional (3D) image and quantified with X-ray computed tomography. The mechanical performance of the composites is investigated via tensile tests.The results reveal that tensile failure occurs after the delamination and fibre pull-out in the SiC_f/PyC/SiC composites due to the volatilization of the PyC interface at high temperatures in the air environment. Meanwhile, the gaps between the fibres and matrix lead to rapid oxidation and crack propagation from the SiC matrix to SiC fibre, resulting in the failure of the SiC_f/PyC/SiC composites as the oxidation temperature increases to 1600?°C. On the other hand, the oxidation products of B₂O₃ molten compounds (reacted from the BN interface) fill up the fracture, cracks, and voids in the SiC matrix, providing excellent strength retention at elevated oxidation temperatures. Moreover, under the protection of B₂O₃, the SiC_f/BN/SiC mini-composites show a nearly intact microstructure of the SiC fibre, a low void growth rate from the matrix to fibre, and inhibition of new void formation and the SiO₂ grain growth from room to high temperatures. This work provides guidance for predicting the service life of SiC_f/PyC/SiC and SiC_f/BN/SiC composite materials, and is fundamental for establishing multiscale damage models on a local scale.     

Large increase of Curie temperature in (110)-oriented La0.7Sr0.3MnO3 films

From the perspectives of scientific researches and practical applications, it is desirable to explore high operating temperature ferromagnetic films. The effect of biaxial strain on magnetic properties of (110)-oriented La_0.7Sr_0.3MnO₃ films was studied. High quality La_0.7Sr_0.3MnO₃ films were grown on (110)-oriented perovskite single crystal substrates using pulsed laser deposition, varying substrate-induced misfit strains from ??2.27–0.75%. A remarkable enhancement of Curie temperature has been achieved for (110)-oriented La_0.7Sr_0.3MnO₃ films clamped with small misfit strains (i.e., grown on LAST (110)). The enhanced Curie temperature of (110)-oriented La_0.7Sr_0.3MnO₃ films could be attributed to the misfit strain between the films and the underlying substrates and may have technological implication for applications at high temperature environments.     

Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.     

郭庄煤业选煤厂振动筛筛选形式的优化研究

针对郭庄煤业选煤厂振动筛振动筛分方式可靠性差、筛分效率低下、物料筛分率低的难题,本文提出了三种新的振动筛分方案,对不同筛分方案的实际应用效果进行了分析。结果表明三移动一摆动的振动筛分方式对物料的综合分散度最高,稳定性好,该筛分方案已在郭庄煤业选煤厂煤炭筛分过程中得到了全面的应用。     

Research on hydrophobicity of electrospun Fe3O4/PVDF nanofiber membranes under different preparation conditions

Abstract

Preparation condition can affect the structure and the properties of nanofiber membrane. In order to explore suitable conditions to prepare the Fe₃O₄/PVDF nanofiber membrane with good hydrophobicity, the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes obtained by electrospinning was investigated by changing preparation conditions like weight percentage of Fe₃O₄ nanoparticles, blending quality concentration of poly (vinylidene fluoride) (PVDF) and Fe₃O₄ nanoparticles, and positive voltage. And the variations of hydrophobicity of Fe₃O₄/PVDF nanofiber membranes modified by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane were studied. The results show that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has changed under different preparation conditions. The contact angles of samples increased after a modification by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane, which indicates that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has been enhanced.     

Study on wax precipitation characteristics of wax deposit in pipes

Wax deposit properties are a significant concern in pipeline pigging during waxy crude oil transportation. In the present work, the impacts of flow conditions and oil properties on the wax precipitation characteristics of wax deposits are investigated. A flow loop apparatus was developed to conduct wax deposition experiments using four crude oils collected from different field pipes. The differential scanning calorimetry (DSC) technique was employed to observe the wax precipitation characteristics of crude oil and wax deposit. The results show that the wax content and the wax appearance temperature (WAT) of the deposits increase with shear stress and radial temperature gradient, and decrease with radial wax molecule concentration gradient near the pipe wall. The DSC tests on the wax deposits revealed that the deposit wax content is strongly correlated to the oil wax content. Furthermore, an empirical correlation was developed to predict the wax content and the WAT of the wax deposit. Verification of the empirical correlation using the different oils indicated that the average relative error of the wax content prediction and average absolute error of WAT prediction were 13.2% and 3.6°C, respectively.