Simulation Analysis of the Heat Transfer Performance of an N-type Microchannel Heat Exchanger

A microchannel heat exchanger with a triangular wave and symmetrical triangular wave structure was proposed in this paper. In addition, a new N-type microchannel heat exchanger was developed to balance the heat transfer performance and pressure drop. The relationship between different configurations of the N structure of the microchannel and the heat transfer performance was analyzed. The results showed that, at a high inlet flow rate, the symmetrical triangular wave microchannel had the best heat transfer performance, followed by the triangular wave microchannel and the straight channel. At the same flow rate, the degree of disturbance of the fluid was highest in the symmetrical N-structure microchannel, and an excellent heat transfer effect was observed.     

Lead-free sodium niobate nanowires with strong piezo-catalysis for dye wastewater degradation

In this work, the hydrothermally-synthesized sodium niobate nanowires were used to decompose Rhodamine B dye solution through the piezo-catalytic effect. With the sodium niobate catalyst, a high piezo-catalytic degradation ratio of ～80% was achieved under the excitation of vibration for the Rhodamine B dye solution (～5?mg/l). These active species in the catalytic process, hydroxyl radicals and superoxide radicals with the strong oxidation ability, were also observed, which confirmed the key role of piezoelectric effect for piezo-catalysis. The piezo-catalysis of sodium niobate nanowires provides a high-efficiency and reusable tool in application in depredating the dye wastewater.     

Densification mechanism during reactive hot pressing of B4C-ZrO2 mixtures

The densification behaviors of pure B₄C and B₄C-ZrO₂ mixtures were compared during hot pressing. The results showed that in-situ formed ZrB₂ effectively enhanced the densification process of B₄C-ZrO₂ mixtures, more significantly during the intermediate stage. Within the relative density ranging from 0.75 to 0.90, the B₄C-15?wt%ZrO₂ mixture (B15Z) achieved the maximum densification rate as twice much as that of pure B₄C. The stress exponent n>3 indicated plastic deformation was the dominant densification mechanism of B15Z. The viscosities of plastic flow were evaluated using Murray-Rodger-William equation and the viscosity of B15Z was only a quarter of that in pure B₄C. The sintering activation energy was calculated to be 305.9?kJ/mol for pure B₄C and 197?kJ/mol for B15Z, respectively. It was proposed that the lower viscosity of plastic flow and activation energy accelerated the sliding and propagating motions of plastic flow, by which underlain the enhanced densification behaviors of B₄C-ZrO₂ mixtures.     

Super-oleophilicity Co-doping Co2+/F-/TiO2 one-dimensional nanotubes for photocatalytic denitrification of light oil

In this study, a simple hydrothermal synthesis method was adapted for the preparation of Co-doping Co²⁺/F^-/TiO₂ nanotubes photocatalyst, and the micro-nano structure of catalysts prepared by biomimetic technology which makes the catalyst have super-oleophilicity property. Co²⁺/F^-/TiO₂ revealed improved photocatalytic performance for denitrification of light oil compared to single TiO₂ photocatalysts. The enhance of photocatalytic activity can be attributed to narrowing the band gap, increasing the light response wavelength and exposing more highly active crystal surfaces due to synergistic effects of Co²⁺ and F^? in the photocatalyst.     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.     

Effect of an abrupt change in pulling rate on microstructures of directionally solidified Al2O3-Er3Al5O12 eutectic and off-eutectic composite ceramics

Directionally solidified microstructures of Al₂O₃-Er₃Al₅O₁₂ eutectic and off-eutectic in situ composite ceramics were explored under abrupt-change pulling rate conditions. Corresponding temperature distributions and interface locations were studied. In eutectic composition, fluctuation of eutectic spacing occurred when the pulling rate increased abruptly. A gradually increase or abrupt increase in eutectic spacing was observed when the pulling rate decreased abruptly. In hypoeutectic and hypereutectic compositions, formation of the primary phases were suppressed when the pulling rate increased abruptly from 10?µm/s to 100?µm/s, while primary phases precipitated when the pulling rate decreased abruptly from 100?µm/s to 10?µm/s. The interface altitude decreased after the pulling rate increased abruptly, but increased after the pulling rate decreased abruptly. The liquid composition restriction (around the eutectic composition) at the eutectic interface plays an important role in the suppression of the primary dendrite and coupled eutectic oxides can be obtained in off-eutectic compositions even under higher solidification rate conditions.     

Visual Detection of Adenosine Triphosphate by Taylor Rising: A Simple Point-of-Care Testing Method Based on Rolling Circle Amplification

Rapid and sensitive point-of-care testing (POCT) is an extremely critical mission in practical applications, especially for rigorous military medicine, home health care, and in the third world. Here, we report a visual POCT method for adenosine triphosphate (ATP) detection based on Taylor rising in the corner of quadratic geometries between two rod surfaces. We discuss the principle of Taylor rising, demonstrating that it is significantly influenced by contact angle, surface tension, and density of the sample, which are controlled by ATP-dependent rolling circle amplification (RCA). In the presence of ATP, RCA reaction effectively suppresses Taylor-rising behavior, due to the increased contact angle, density, and decreased surface tension. Without addition of ATP, untriggered RCA reaction is favorable for Taylor rising, resulting in a significant height. With this proposed method, visual sensitive detection of ATP without the aid of other instruments is realized with only a 5 μL droplet, which has good selectivity and a low detection limit (17 nM). Importantly, this visual method provides a promising POCT tool for user-friendly molecular diagnostics.