New anti-ablation candidate for carbon/carbon composites: Preparation,composition and ablation behavior of Y2Hf2O7 coating under an oxyacetylene torch

Y₂Hf₂O₇ possesses low thermal conductivity and high melting point, which make it promising for a new anti-ablation material. For evaluating the thermal stability and the potential applications of Y₂Hf₂O₇ on anti-ablation protection of C/C composites, Y₂Hf₂O₇ ceramic powder was synthesized by solution combustion method and Y₂Hf₂O₇ coating was prepared on the surface of SiC coated C/C composites using SAPS. Results shown that the coating exhibits good ablation resistance under the heat flux of 2.4?MW/m² with the linear and mass ablation rates are 0.16?μm?s^?1 and ?0.028?mg?s^?1, respectively, after ablation for 40?s. With the prolonging of the ablation time, the increasing thermal stress causes the increase of cracks. Moreover, the chemical erosion from SiO₂ and the physical volatilization of low temperature molten products aggravate failure of the Y₂Hf₂O₇ coating.     

Design and optimization of ceramic membrane structure: From the perspective of flux matching between support and membrane

The support flux was first investigated as a separate influencing factor for its effect on performances of ceramic filtration membranes. Three pre-membranes were prepared by tape-casting and then transfer-coated to supports to form dual-layer ceramic membranes after sintering. Experiments demonstrated that membrane layers with almost the same properties were obtained despite the huge difference in support flux. When the support flux increases from 3.120 to 97.53 m³m^?2h^?1, the flux of these three membrane series have increased by 75%, 186% and 228%, respectively. Experimental rules can provide structural design and evaluation from the perspective of permeability. The limit membrane flux of a certain system was derived according to the resistance distribution law of internal membrane structure and the Darcy's theorem. On this basis, a method for designing support flux was proposed. Furthermore, we present a criterion to quickly and easily evaluate the match between the support and the top layer, which is the ratio of membrane resistance to total resistance. Finally, the filtration resistance of penetration caused by suction of membrane particles into the support was measured for the first time, taking the advantage of the transfer-coating method that inherently free of penetration. Our works are expected to deepen the understanding of the ceramic membrane structure and provided guidance for its rational design and optimization.     

臭氧技术在废水处理中的应用

由于臭氧的强的氧化性能,使其成为一种强氧化剂和消毒剂;臭氧技术已经广泛用于废水处理行业,臭氧具有较好的的消毒杀菌、脱色、除臭味等作用,文章通过介绍臭氧的一些基本性质,臭氧消毒杀菌、氧化、脱色及除臭味的机理,臭氧的制取方式,现代臭氧技术的研究方向等,为废水处理中臭氧技术的应用提供参考。     

High‐performance thermosets with tailored properties derived from methacrylated eugenol and epoxy‐based vinyl ester

A renewable chemical, eugenol, is methacrylated to produce methacrylated eugenol (ME) employing the Steglich esterification reaction without any solvent. The resulting ME is used as a low‐viscosity co‐monomer to replace styrene in a commercial epoxy‐based vinyl ester resin (VE). The volatility and viscosity of ME and styrene are compared. The effect of ME loading and temperature on the viscosity of the VE–ME resin is investigated. Moreover, the thermomechanical properties, curing extent and thermal stability of the fully cured VE–ME thermosets are systematically examined. The results indicate that ME is a monomer with low volatility and low viscosity, and therefore the incorporation of ME monomer in VE resins allows significant reduction of viscosity. Moreover, the viscosity of the VE–ME resin can be tailored by adjusting the ME loadings and processing temperature to meet commercial liquid molding technology requirements. The glass transition temperatures of VE–ME thermosets range from 139 to 199 °C. In addition, more than 95% of the monomer is incorporated and fixed in the crosslinked network structure of VE–ME thermosets. Overall, the developed ME monomer exhibits promising potential for replacing styrene as an effective low‐viscosity co‐monomer. The VE–ME resins show great advantages for use in polymer matrices for high‐performance fiber‐reinforced composites. This work is of great significance to the vinyl ester industry by providing detailed experimental support. © 2018 Society of Chemical Industry     

Research on hydrophobicity of electrospun Fe3O4/PVDF nanofiber membranes under different preparation conditions

Abstract

Preparation condition can affect the structure and the properties of nanofiber membrane. In order to explore suitable conditions to prepare the Fe₃O₄/PVDF nanofiber membrane with good hydrophobicity, the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes obtained by electrospinning was investigated by changing preparation conditions like weight percentage of Fe₃O₄ nanoparticles, blending quality concentration of poly (vinylidene fluoride) (PVDF) and Fe₃O₄ nanoparticles, and positive voltage. And the variations of hydrophobicity of Fe₃O₄/PVDF nanofiber membranes modified by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane were studied. The results show that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has changed under different preparation conditions. The contact angles of samples increased after a modification by 1H, 1H, 2H, 2H-perfluorodecyl trimethoxysilane, which indicates that the hydrophobicity of Fe₃O₄/PVDF nanofiber membranes has been enhanced.     

Microwave dielectric properties of SrLa[Ga1−x(Mg0.5Ti0.5)x]O4 and SrLa[Ga1−x(Zn0.5Ti0.5)x]O4 (x = 0.2-0.8) ceramics

SrLa[Ga_1−x(R_0.5Ti_0.5)_x]O₄ (R = Mg, Zn) ceramics were prepared by a standard solid state sintering method. The single-phase ceramics with K₂NiF₄-type layered perovskite structure and I4/mmm space group were obtained, indicating that SrLa(R_0.5Ti_0.5) and SrLaGaO₄ can form the unlimited solid solutions. With increasing x for R = Mg and Zn, ε_r increases monotonously, the Qf value first increases and then decreases, while τ_f increases from a negative to a positive value. The optimized microwave dielectric properties were obtained as following: ε_r = 23.3, Qf = 89 400 GHz, τ_f = −0.8 ppm/°C for SrLa[Ga_0.6(Mg_0.5Ti_0.5)_0.4]O₄ and ε_r = 23.3, Qf = 76 200 GHz, τ_f = 0.2 ppm/°C for SrLa[Ga_0.7(Zn_0.5Ti_0.5)_0.3]O₄, indicating that the present solid solution ceramics are the promising candidates as microwave resonator materials for the telecommunication applications.     

埋地管道泄漏内封堵装置设计与研究

针对流体输送埋地管道泄漏问题,设计了一种利用管道机器人携带封堵气囊进行快速应急封堵修复的埋地管道泄漏内封堵装置。采用矩阵变换方法建立了牵引系统驱动轮过弯方程,利用MATLAB软件对过弯方程进行了验证,同时利用ADAMS软件仿真分析过弯路径与驱动轮转角对牵引系统行走速度的影响。研究结果表明:由两个串联封堵器组成的应急封堵系统可满足复杂工况下的管道泄漏封堵要求;牵引系统驱动轮在弯管内部行走时,单轮速度呈周期性变化,但三个驱动轮整体周期运动特性一致;驱动轮转角在25°~40°时,牵引系统行走速度与驱动轮转角成正比,且转角为30°时驱动效果最好。该内封堵装置的结构设计可为管道泄漏应急封堵领域装备的研发提供重要参考。