Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry     

对海水进行混凝除浊预处理研究

介绍采用聚合氯化铁（PFC）为絮凝剂，对海水进行混凝除浊预处理方法。考察了原海水pH、搅拌速度、反应时间及PFC用量对海水预处理效果的影响。结果表明，在原海水pH凋至9．0，搅拌速度控制在200min^-1，反应时间选择8—10min，PFC用量0．10μg／g的最佳条件下，能使处理后的海水浊度降至0．05mol／L，而联产的酸性废水中和剂浆料中Mg（OH）2含量在25％～45％，大肠菌群的去除率大于89．3％。     

应用API 581对输气站场进行定量风险评价

目前专门针对输气站场的风险评价方法还不多，现有的手段也只是根据国家法律法规得出定性的评价结果，然后按照评价结果对照得出整改方案。为此，对输气站场的定量风险评价工作提出了一套新方法，得到了定量的和更加客观的风险排序，为管道站场的完整性管理工作提供了有力的支持；并以陕京输气管道榆林压气站为例，应用美国石油学会标准API 581（基于风险检测的基本源文件）对站内设施进行了风险评价，计算了站内设备和管线的失效后果、失效概率，得到了定量风险值，进而分析了风险值产生差异的原因。最后，针对我国输气管道风险评估工作提出了看法和建议。     

营尔凹陷下白垩统油气勘探应避开高压水层

营尔凹陷下白垩统(K₁₎存在下沟组和赤金堡组2套源岩，目前它们已到成熟阶段。凹陷东侧长沙岭构造在下白垩统下沟组和赤金堡组储层中也发现油藏，但主要分布在高压水层的顶部及下部，而高压水层段存在良好的储层，并未发现油气。文章根据高压水层段的储层荧光特征，通过储层烃与源岩的对比，分析了下白垩统高压水层对油气运移的影响。研究结果表明：高压水层段，储层荧光弱，储层抽提物特征既不同于赤赤金堡组源岩，也不同于下构组源岩，为就近捕获的产物；高压水层未发生大规模的油气运移，其形成时间早于油气运移的时间。建议该区油气勘探目标的选择应避开高压水层，选择凹陷附近的圈闭、高压水层以下的层位。     

基于实际井眼轨迹的抽油杆柱API设计方法

目前的抽油杆柱设计方法大都基于设计井眼轨迹或经验公式，因此设计的抽油杆柱与井眼的匹配性并没有达到最优，结果可能影响了抽油杆柱的受力特性和寿命。概述了目前现有的抽油杆柱设计方法，提出了基于实际井眼轨迹的抽油杆柱API设计方法，即考虑到在三维空间中井下粘滞阻力及动载的影响，利用微单元分析方法计算出轴向载荷与轴向应力，然后在此基础上进行杆柱组合设计，并给出了设计流程。以江苏油田永21-3井为例，对几种设计方法的设计结果进行了对比分析，结果表明，江苏油田目前采用的抽油杆柱设计方法包含了人为经验因素，并不是最优的杆柱设计结果，有待进一步改进。     

Laterally coupled buried heterostructure high-Q ring resonators

All-buried InP-InGaAsP ring resonators laterally coupled to bus waveguides are demonstrated. The buried configurations offer a lower built-in refractive index step along the resonator periphery, which affords enhanced optical coupling coefficients between the waveguides and reduced scattering losses caused by the resonator sidewall imperfections. Very low optical intensity attenuations of 0.4 cm/sup -1/ and coupling-limited quality factors of greater than 10/sup 5/ are observed from 200-/spl mu/m-radii ring resonators. The measured spectral linewidth is as narrow as 0.0145 nm.     

A decision support system for interactive decision making - Part II: analysis and output interpretation

For pt.I see ibid., p.42-55 (2003). The development of a comprehensive decision support system, GMCR II, for the systematic study of real-world interactive decision problems is presented. The companion paper (Part I), discusses how GMCR II elicits, stores, and manages conflict models; here (Part II), the focus is on GMCR IIs analysis and output interpretation subsystems. Specifically, this paper describes the powerful and efficient analysis engine contained in GMCR II, its informative output presentation and interpretation facilities, and a number of follow-up analyses. Furthermore, an illustrative case study is used to demonstrate how GMCR II can be conveniently applied in practice.     

选择测试阀在现场测试中的应用

选择测试阀是新一代全通径压控式测试器，在结构和性能上有了本质的创新，使现场操作更加简便、安全，对井筒条件要求低，更适用于高温、高压、深井、气井的地层测试，拓宽了地层测试和其它井下作业的兼容性。经7井次应用，其安全性、可靠性越来越得到认可。     

润滑油用纳米TiO2的表面改性及自修复性能研究

采用油酸对纳米TiO2进行表面改性，使其稳定分散于基础油中。利用HQ-1摩擦磨损试验机考察纳米TiO2的自修复性能，并探讨其自修复机理。试验结果表明，经改性后的纳米TiO2粉体作为润滑添加剂具有良好的分散稳定性、减摩抗磨性和自修复性。