竹材丙酮法木质素高效分离技术研究

在一定的温度、压力条件下,利用丙酮提取竹材中的木质素,丙酮通过蒸馏回收后,可以反复利用;而通过蒸馏,得到的高纯度的木质素是重要的化工原料,整个过程形成一个封闭循环系统,基本上无三废排放;研究结果表明:当丙酮浓度为80%,液固比为10∶1,在最高反应温度160℃下保温3h,降解木质素的效果最佳;为解决制浆造纸行业废水对环境的污染问题提出了一条新的途径。     

Electrochemical performance of nanocrystalline Li3V2(PO4)3/carbon composite material synthesized by a novel sol–gel method

A novel sol–gel method based on V₂O₅·nH₂O hydro-gel was developed to synthesize nanocrystalline Li₃V₂(PO₄)₃/carbon composite material. In this route, V₂O₅·nH₂O hydro-gel, NH₄H₂PO₄, Li₂CO₃ and high-surface-area carbon were used as starting materials to prepare precursor, and the Li₃V₂(PO₄)₃/carbon was obtained by sintering precursor at 750 °C for 4 h in flowing argon. The sol–gel synthesis ensures homogeneity of the precursors and improved reactivity. The sample was characterized by XRD, SEM and TEM. X-ray diffraction results show Li₃V₂(PO₄)₃ sample is monoclinic structure with the space group of P2₁/n. The TEM image indicates that the Li₃V₂(PO₄)₃ particles modified by conductive carbon are about 70 nm in diameter. The Li₃V₂(PO₄)₃/carbon system showed that the discharge capacities in the first and 50th cycle are about 155.3 and 143.6 mAh/g, respectively, in the range of 3.0–4.8 V. The sol–gel method is fit for the preparation of Li₃V₂(PO₄)₃/carbon composite material which may offer some favorable properties for commercial application.     

Seasonal evolution of the interannual variability of chlorophyll-a concentration and its forcing factors in the northwestern Pacific from 1998 to 2010

The northwestern Pacific Ocean is a complex region with significant biological spatial variations on a seasonal timescale. To investigate the joint variation patterns on both seasonal and interannual timescales, a season-reliant empirical orthogonal function (S-EOF) analysis was applied to seasonal mean chlorophyll-a concentration (chl-a) anomalies in the northwestern Pacific Ocean during the period 1998–2010. The first two dominant modes accounted for nearly 31% of the total interannual variance, with the second S-EOF mode (S-EOF2) lagging behind the first S-EOF mode (S-EOF1) by one year. S-EOF1 featured a strong variation pattern to the north of 30° N, with maximum chl-a in winter and minimum chl-a in summer. However, S-EOF2 indicated an opposite seasonally evolving pattern compared with S-EOF1, with chl-a increasing along the Kuroshio and extension current from boreal winter to autumn. Both these modes revealed significant relationships with climate-related indices. The two modes corresponded to the central Pacific (CP) La Niña developing episodes and the turnaround from eastern Pacific (EP) La Niña to CP El Niño, respectively. Both modes were associated with the cold phase of the Pacific Decadal Oscillation, which played an important role in prolonging the impact of the El Niño/Southern Oscillation on chl-a seasonal evolution from 1998 to 2010. In addition, we discuss the possible factors dominating chl-a seasonal variation, in terms of the subregions of the northwestern Pacific Ocean. In the subtropical northwestern Pacific Ocean (15° N – 30° N), the chl-a growth was primarily nutrient-limited, whereas in the mid-latitude northwestern Pacific Ocean (35° N – 50° N), the chl-a growth was mainly light-limited.     

Synthesis and characterization of copolythiophene

Copolythiophenes (Co‐PTs), poly(3‐hexylthiophene‐co‐3‐thiophene carboxylic acid) (P3HT‐TCa), poly(3‐hexyloxylthiophene‐co‐3‐thiophene carboxylic acid) (P3HOT‐TCa), and poly(3‐phenylthiophene‐co‐3‐thiophene carboxylic acid) (P3PhT‐TCa), were synthesized by chemical oxidized polymerization to investigate the effect of copolymerization on the properties of polythiophenes (PTs). Gel permeation chromatography showed that the molecular weight (MW) of Co‐PT was lower than that of homopolythiophene. Fourier transform infrared (FTIR) spectra indicated that the copolymerization was successful between the monomers. The λ_max of Co‐PTs gave a “blue shift” in ultraviolet‐visible (UV‐VIS) spectra. Photoluminescence (PL) spectra showed that the PL intensity of Co‐PT became weaker than that of homopolythiophene and the disappearance of PL had been observed in P3HOT‐TCa. The thermal stability of Co‐PT was influenced by the carboxyl for its low decomposition temperature. Furthermore, the copolymerization between multi‐wall carbon nanotube containing thiophene ring (MWNT‐Th) and 3‐hexyloxylthiphene could also take place successfully. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

混合物MH-81状态方程的研究——从无限稀释活度系数预测混合物汽液平衡

本文由无限稀释活度系数求取混合物MH-81状态方程的二元相互作用参数,预测了二元混合物的汽液平衡,获得了较满意的结果。     

一种新的S/PDIF接收机数据译码的实现方法

论文分析了S/PDIF音频数据流的特点,引入模式识别中的训练机对S/PDIF音频数据流进行现场脉冲宽度特征提取。依据训练机结果建立分类器实现脉冲宽度分类,根据脉冲宽度进行同步前置码和逻辑电平的解码。利用硬件描述语言Verilog进行设计实现与验证,仿真结果说明这种特征提取方法可以提高S/PDIF接收机数据解译码的适应性和准确性。     

Synthesis and Morphology of TiO2 Nanotube Arrays by Anodic Oxidation Using Modified Glycerol-Based Electrolytes

Titanium dioxide (TiO₂) nanotube arrays were prepared by electrochemical anodization of titanium sheets in the glycerol 176 mL/H₂O 44 mL/NH₄F 0.5 wt% electrolytes modified with H₂SO₄ and NaAc addition. The surface morphologies, average inner diameter, and the length of the nanotube arrays changed with the solution pH in the range from 5.6 to 4.0 by adding H₂SO₄. A uniform surface morphology of the nanotubes with average inner diameter of ∼80 nm and a length of ∼1000 nm was obtained when the solution pH was 5.0. The growth rates of the nanotubes were remarkably enhanced by NaAc addition in the range of 0.04–0.14 M . With NaAc addition of 0.10 M , the length of the nanotube arrays reached 4.16 μm after an 8-h anodization, increasing 3.23 μm compared with no NaAc addition. The relationship between solution pH and growth of TiO₂ nanotubes was analyzed by current–time curves, solution electrical conductivities, and scanning electron microscopy (SEM), and the role of NaAc was also discussed based on SEM and solution electrical conductivities.     

后XP时代网络安全防护技术探究

伴随着微软公司不断改革与发展,windows XP服务也在今年2014年4月8日正式退役.世界各个行业与单位都开始在工作中进一步使用计算机技术,但不少老用户依旧习惯使用windowsXp系统,这就需要在后XP时代网络安全防护技术不断适应这部分客户的需求,保障他们电脑使用的安全性,为以后计算机网络安全防护提供有效防护措施.     

微晶纤维素增粘剂的研制

以棉浆为原料，废盐酸为水解催化剂，所得合成革用微晶纤锥素增粘剂的质量指标达到了德国和日本同类产品的标准。     

Study of different effect on foaming process of biodegradable bionolle in supercritical carbon dioxide

Microcellular foaming of biodegradable Bionolle in supercritical CO₂ has been produced. The effects of a series of variable factors, such as saturation temperature, saturation pressure, and depressurization time and step on the foam structures and density, were studied through measurement of density and SEM observation. The experimental results show that higher saturation temperatures lead to an increase in bulk densities; and different depressurization time and step result in different product cell morphology. In addition, at some saturation temperature, the orientation of the cells can be found in the product morphology. XRD experimental results show that the foaming treatment with SC CO₂ increased the crystallinity of Bionolle. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 2901–2906, 2006