Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Cholesterol‐imprinted polymer receptor prepared by a hybrid imprinting method

A novel cholesterol‐imprinted polymer (CMIP‐H) was prepared by a hybrid method of covalent imprinting and non‐covalent imprinting. This approach involves the copolymerization of a template‐containing monomer, cholesteryl 2‐hydroxyethyl methacrylate carbonate, and a cross‐linker, followed by hydrolysis to afford a flexible guest‐binding site accompanied with the easy and efficient removal of a ‘sacrificial spacer’. The effect of solvent on the binding capacity of CMIP‐H towards cholesterol was studied, indicating that a good binding capacity towards cholesterol could be achieved in a less‐polar solvent. The binding experiments of CMIP‐H towards a series of structural analogues of cholesterol, including cholesterol acetate, progesterone and stigmasterol, were carried out in hexane. The results showed that CMIP‐H almost did not bind cholesterol acetate at all because the hydrogen‐bonding site is blocked. It exhibited a similar binding towards both cholesterol and stigmasterol, but much higher binding towards progesterone. Copyright © 2005 Society of Chemical Industry     

春光油田现代油藏经营管理模式的

介绍并分析了春光油田现代油藏经营管理模式的构建与运作及实施效果.     

Peracetic acid pretreatment of sugarcane bagasse for enzymatic hydrolysis: a continued work

Previous work has shown that the enzymatic hydrolysis of sugarcane bagasse could be greatly enhanced by peracetic acid (PAA) pretreatment. There are several factors affecting the enzymatic digestibility of the biomass, including lignin and hemicelluloses content, cellulose crystallinity, acetyl group content, accessible surface area and so on. The objective of this work is to analyze the mechanism of the enhancement of enzymatic digestibility caused by PAA pretreatment. Delignification resulted in an increase of the surface area and reduction of the irreversible absorption of cellulase, which helped to increase the enzymatic digestibility. The Fourier transform infrared (FTIR) spectrum showed that the absorption peaks of aromatic skeletal vibrations were weakened or disappeared after PAA pretreatment. However, the infrared crystallization index (N.O'KI) was increased. X‐ray diffraction (XRD) analysis indicated that the crystallinity of PAA‐treated samples was increased owing to the partial removal of amorphous lignin and hemicelluloses and probable physical change of cellulose. The effect of acetyl group content on enzymatic digestibility is negligible compared with the degree of delignification and crystallinity. The results indicate that enhancement of enzymatic digestibility of sugarcane bagasse by PAA pretreatment is achieved mainly by delignification and an increase in the surface area and exposure of cellulose fibers. Copyright © 2008 Society of Chemical Industry     

印染废水处理工艺研究及实例

本文简要介绍了印染废水水质特征,提出了处理工艺,并利用两个工程实例说明了该工艺的可行性.