Transformation of β-Ni(OH)2 to NiO nano-sheets via surface nanocrystalline zirconia coating: Shape and size retention

Shape and size of the synthesized NiO nano-sheets were retained during transformation of sheet-like β-Ni(OH)₂ to NiO at elevated temperatures via nano-sized zirconia coating on the surface of β-Ni(OH)₂. The average grain size was 6.42 nm after 600 °C treatment and slightly increased to 10 nm after 1000 °C treatment, showing effective sintering retardation between NiO nano-sheets. The excellent thermal stability revealed potential application at elevated temperatures, especially for high temperature catalysts and solid-state electrochemical devices.     

铟（Ⅲ）－钼酸铵－罗丹明B显色反应体系的研究及其应用

铟（Ⅲ）与钼酸铵和罗丹明Ｂ在ＰＶＡ存在下的酸性水溶液中形成离子缔合物而产生显色反应，该体系的灵敏度高，摩尔吸光系数ε＝２．４４×１０５Ｌ·ｍｏｌ－１ｃｍ－１，离子缔合物稳定性好，至少稳定４８ｈ。研究了显色体系的光度特性和３０多种共存离子的影响，该法应用于纯锡中痕量铟的测定，结果满意。     

超临界流体技术应用研究

超临界流体技术具有许多传统技术所没有的快速，高效，低能耗，污染少等优点，在材料制备，医药工业，生物工程，食物，环境，化工等许多方面展现了广阔的应用前景。综述了其在萃取，材料制备和作为反应介质等方面的应用。     

Fabricating Water-Insoluble Polyelectrolyte into Multilayers with Layer-by-layer Self-assembly

Summary A water insoluble azo-containing polyelectrolyte (PEAPB6P-AC) was successfully fabricated into multilayer films based on the layer-by-layer adsorption technique by using N, N-dimethylformamide (DMF) as the assembling media. The multilayer growth and structure were studied with UV-vis spectroscopy, and the multilayer surface were imaged with Atomic Force Microscopy and compared with that fabricated in water. The results show that assembling PEAPB6P-AC in DMF can effectively eliminate the hydrophobic aggregation of the azo units and consequently results in a much smoother multilayer surface than that fabricated in water. This improvement to the layer-by-layer adsorption technique, which can avoid some major difficulties faced when assembling hydrophobic polyelectrolytes in aqueous solutions, seems to be a versatile way to fabricate high quality multilayer films when using the hydrophobic even water-insoluble polyelectrolytes as assembling units.     

企业核心竞争力关键要素——质量

介绍了如何体现产品质量及如何控制产品质量。     

C-19 diacid-based polyamides

The preparation and properties of polyamide hot-melt adhesives derived from Koch C-19 diacid are described. They are comparable to those of commercial C-36 dimer acid-based polyamides for bonding leather and metals and somewhat superior to those of polyamides made from C-19 diacid derived from a hydroformylation process. Presented at the AOCS annual meeting, Toronto, May 1982.     

Preparation,characterization, and adsorption properties for metal ions of a novel chelating resin containing sulfoxide and diethylene glycol

A novel chelating resin containing sulfoxide and diethylene glycol, poly{4‐vinylbenzyl‐[2‐2‐(hydroxyethyl)ethoxyl]sulfoxide} (PVESO) was synthesized using chloromethylated polystyrene (PS‐Cl) as material. Its structure was characterized by elemental analysis, infrared spectra, and scanning electron microscopy (SEM). The adsorption capacities of the resin for Hg²⁺, Ag⁺, Cu²⁺, Zn²⁺, and Pb²⁺ at various pH values were determined. The maximum adsorption capacities for Hg²⁺ and Ag⁺ were 1.56 and 0.75 mmol g^?1 respectively. The resin had high selectivity for Hg²⁺ and Ag⁺ over the pH range 1.0–7.0. The adsorption capacities for Hg²⁺ and Ag⁺ under competitive condition were also determined by batch experiment method. In addition, the adsorption kinetics of the resin towards Hg²⁺ at different temperatures was also investigated. The results showed that the adsorption rate was governed by film diffusion at 20°C and 25°C, by particle diffusion at 30°C and 35°C. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 6054–6059, 2006     

腐植酸类液体肥料生产技术和产品质量中的几个问题

本文通过胶体化学基本原理和实验数据，对水剂型腐植酸类液体肥料的组分、性质、浓度、流动性、稳定性、抗絮凝性等若干技术和质量问题进行了探讨，并提出一些改进建议。     

Soap‐free emulsion copolymerization of perfluoroalkyl acrylates in the presence of a reactive surfactant

Soap‐free emulsion copolymerization of perfluoroalkyl acrylate (FA)/methyl methacrylate (MMA)/n‐butyl acrylate (n‐BA) was carried out in the presence of sodium 2‐acrylamide‐2‐methyl propanesulfonate (AMPSNa) as a reactive surfactant and potassium persulfate (KPS) as an initiator. An analysis of the effects of concentration of AMPSNa, KPS, FA as well as polymerization temperature on the kinetic features (rate of polymerization) and colloidal characteristics (mean particle diameter, particle disperse index, particle numbers, and surface charge density) was followed. NMR, FTIR, AFM, and fluorine‐selective electrode analysis were used to characterize the composition and morphology of the FA copolymers. Both AFM analysis and contact angle measurements strongly implied that the fluorinated segments migrated to the outmost surface and created films with lower surface energy. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 2438–2444, 2007     

Consolidation of sand formation using freon'll gas hydrate

Freon 11 gas hydrate was used to block the pores of four size ranges of sand from 24 mesh to 60 mesh. A 50.8 mm deep bed of sand when thus “frozen” with hydrate could sustain a dfferential water pressure of at least 6895 kPa. A subcooling of about 5 to 6°C below its thermodynamic formation temperature was required to cause the hydrate to form such a plug. Once formed, the hydrate remained stable at temperatures up to its decomposition temperature. The time required for the hydrate crystal to grow to a size large enough to block the pores of the bed was about two hours. The amount of hydrate forming agent required to block the sand pores was found to be approximately that calculated from the ideal composition of the hydrate.