Weathering modification of acrylic emulsion by introducing UV absorbing groups

A new kind of UV-absorbing silicon-fluorinated acrylic emulsion was prepared by emulsion polymerization with 4-allyloxy-2-hydroxybenzophenone, 3-methacryloxypropyltrimethoxysilane (MPS) and hexafluorobutyl methacrylate (HFMA) as functional monomers. The emulsion and its coating were characterized by transmission electron microscope, Fourier transform infrared spectrum (FTIR), X-ray photoelectron spectroscopy, ultraviolet absorption spectrum,thermo-gravimetric analysis, water contact angle (CA), and artificial accelerated aging test. The results indicated that the emulsion with core-shell structure was synthesized and showed prominent absorption peaks at 320 and 350 nm. The water CA of the coating was increased from 70.2° to 86.7° because of the incorporated HFMAs and MPSs. Both of the initial and final decomposition temperatures of the coating were increased by more than 20°C compared with those of the unmodified coating. After 10 days of accelerated aging, the color difference (ΔE) and rate of loss of gloss (ΔG) were only 2.78% and 5.22%, while those of the unmodified coating were as high as 22.94% and 78.57%, respectively. Because of the UV absorbers were incorporated by chemical reaction, the new coating had a more durable and effective anti-ultraviolet performance compared with the coatings the UV absorbers were introduced by physical blending.     

IDEF0法建立模具CAD／CAM系统的功能模型

本文阐述了 IDEFO 法建立系统功能模型的步骤、方法和意义,IDEFO 法是一种结构化的系统分析方法,最后用一个简单实例加以说明。     

Fuzzy adaptive networks in machining process modeling: surface roughness prediction for turning operations

Due to the complexity of the machine tool structure and the cutting process, the dynamics of machining processes are still not completely understood. This is especially true due to the demand of high-speed machining to increase productivity. In order to model and control these complex processes, new approaches, which can represent complex phenomenon combined with learning ability, are needed. The combined neural–fuzzy approach appears to be ideally suited for this purpose. In this paper, the recently developed fuzzy adaptive network (FAN) is used to model surface roughness in turning operations. The FAN network has both the learning ability of neural network and linguistic representation of complex, not well-understood, vague phenomenon. Furthermore, it can continuously improve the initially obtained rough model based on the daily operating data. To illustrate this approach, a model representing the influences of machining parameters on surface roughness is established and then the model is verified by the use of the results of pilot experiments. Finally, a comparison with the results based on statistical regression is provided.     

Effect of grain size on high-temperature oxidation behavior of Cu-80Ni alloy

1　INTRODUCTIONTheoxidationofunalloyedcopperandnickelhasalreadybeenstudiedindetail.Whilethehigh tem peratureoxidationofCu Nialloys ,alsostudiedanumberoftimestodate[13] ,isanexampleofarela tivelysimpleclassofscalingofbinaryalloysbyasin gleoxidant,becausethemetalsformacontinuousse riesofsolidsolutions ,whiletheiroxides ,CuO ,Cu2 OandNiO ,exhibitsmallmutualsolubilitiesandshowsignificantdifferencesinthethermodynamicstabilityandparabolicgrowthrates .Thus ,copper richalloysformexternalscales…     

中厚板在线30通道超声波探伤方法及应用

介绍了柳钢公司在生产锅炉板、压力容器板过程中，曾试用了６种探伤方法；而研制的３０通道在线超声波探伤法不仅可满足国家标准要求，而且能适应生产节奏，并具有快速、准确、简便的特点。     

TENSILE FRACURE IN AN Al-Li ALLOY 8090

ＴＥＮＳＩＬＥＦＲＡＣＵＲＥＩＮＡＮＡｌ－ＬｉＡＬＬＯＹ８０９０￥Ｊｉａｎｇ，Ｄａｍｉｎｇ；Ｗａｎｇ，Ｙｉｎｏｎｇ；Ｈｏｎｇ，Ｂａｎｄｅ；Ｌｅｉ，Ｔｉｎｇｑｕａｎ（ＨａｒｂｉｎＩｎｓｔｉｔｕｔｅｏｆＴｅｃｈｎｏｌｏｇｙ，Ｈａｒｂｉｎ１５００８０）Ｓｕ...     

Oxidation Behavior of Rh–30Ni–18Nb Refractory Superalloy

The isothermal-oxidation behavior of Rh–30Ni–18Nb refractory alloy was investigated up to a period of 312 hours in air from 1000 to 1350°C. A comparison of the oxidation behavior of this alloy with a conventional Ni-base superalloy (Inconel 713 C) shows an order-of-magnitude higher oxidation resistance. This experimental alloy oxidizes by forming alternate layers of Nb₂O₅ and RhO while NiO is on the surface in contact with air. Optical and scanning-electron microscopy (SEM) was used to study the microstructure and morphology for the characterization of the oxides. Thermal stability of the alloy for extended periods of exposure to air at 1400°C was studied using transmission-electron microscopy (TEM).     

SHS制备陶瓷内衬复合管中多孔层抑制措施

研究了在重力自蔓延法制备陶瓷内衬复合钢管过程中在复合热管底部出现的多孔层现象,以及各类添加剂对其的影响,分析了多孔层出现的原因,探讨了抑制措施。试验结果表明,SiO2的存在是产生多孔层的主要原因,并且多孔层部分随着SiO2含量的增加而增加,助燃剂也能导致多孔层的出现。当SiO2的质量分数小于2%时,适量加入氟化物,可以有效减少多孔层的体积。     

汽车用磁性材料和磁性器件

汽车前灯装置用的磁性材料为了减少汽车夜间行驶的交通事故,一个重要的办法就是提高驾驶员的眼睛的夜间辨认能力,这就要在汽车上安装高亮度前灯（High Intensity Dischrge Lamp,简写为HID灯）,这种灯较传统用的卤灯省电且更亮,这样驾驶员就能借助它容易发现路面障碍物.HID灯是水银灯、金属卤化物灯、高压钠灯的统称.其中金属卤化物灯用作汽车前灯有2个缺点：①从点灯至达到规定亮度需数分至数十分钟;②一旦灯灭,再点着也必需数分至数十分钟.为克服这两点缺点在其点灯电路中必须设置变换器和触发器.