Nb和时效时间对热轧中锰TRIP钢中P偏聚的影响

热轧态中锰TRIP钢首先经650 ℃退火2 h,随后在550 ℃进行等温时效热处理,采用场发射扫描电镜(FE-SEM)研究该钢中P的偏聚和时效析出行为的变化情况。结果表明,中锰TRIP钢中P在晶界的偏聚是一种非平衡偏聚现象,临界时间约为50 h,与理论计算结果48 h较为吻合。在局部偏聚区域内,C与P存在共偏聚的关系,即P偏聚量高的地方,C含量也高。而合金元素Nb具有抑制P偏聚的效果,在20~70 h时效时间内,可以相对降低6.57%~19.5%的最大P偏聚量。根据电子背散射衍射(EBSD)菊池线分析,P偏聚量低于2.28at%时,P为固溶状态,高于2.28at.%时,P为析出状态。     

Headspace fingerprinting approach to identify the major pathway influencing volatile patterns of vinasse-cured duck processed by high pressure,as well as its impact on physicochemical and sensory attributes

As a decisive attribute, flavour could be influenced by HP treatments through multiple physical and chemical pathways within the high pressure (HP)-assisted meat curing process. This investigation aimed to identify the major pathway influencing volatile flavour patterns of two representative vinasse-cured duck (VCD) products with HP treatments (150–300 MPa/15 min), including wet and dry types, by employing headspace fingerprinting as an untargeted approach. Results suggested that HP treatments greatly lowered moisture contents and increased Warner-Bratzler shear force and thiobarbituric acid reactive substances of the cured samples. According to multivariate models, the volatile flavour patterns of the HP-processed VCD could be clearly separated from the unprocessed samples, but the VCD pressurised at different intensities represented similar volatile fingerprinting, which was validated by e-nose analysis. The discriminant analysis (OPLS-DA) model outlined vinasse-derived ethanol, acetic acid, 3-methyl-1-butanol, 2-methyl-1-butanol, phenethyl alcohol and 2-methyl-3-octanone as the major discriminant aromas across the unpressurised and pressurised samples.     

Influence of Si-Doping on the Performance of InGaN/GaN Multiple Quantum Well Solar Cells

Semiconductors - The performance of InGaN/GaN multiple quantum well (MQW) solar cells with five different Si-doping concentrations, namely 0, 4 × 1017 cm–3, 1 × 1018 cm–3, 3...     

YSZ/MoS2 self-lubricating coating fabricated by thermal spraying and hydrothermal reaction

Thermal sprayed ceramic coatings have extensively been used in components to protect them against friction and wear. However, the poor lubricating ability severely limits their application. Herein, yttria-stabilized zirconia (YSZ)/MoS₂ composite coatings were successfully fabricated on steel substrate with the combination of thermal spraying technology and hydrothermal reaction. Results show that the synthetic MoS₂ powders are composed of numbers of ultra-thin sheets (about 7 ~ 8?nm), and the sheet has obvious lamellar structure. After vacuum impregnation and hydrothermal reaction, numbers of MoS₂ powders, look like flowers, generate inside the plasma sprayed YSZ coating. Moreover, the growing point of the MoS₂ flower is the intrinsic micro-pores of YSZ coating. The friction and wear tests under high vacuum environment indicate that the composite coating has an extremely long lifetime (>?100,000 cycles) and possesses a low friction coefficient less than 0.1, which is lower by about 0.15 times than that of YSZ coating. Meanwhile, the composite shows an extremely low wear rate (2.30?×?10^?7 mm³ N^?1 m^?1) and causes slight wear damage to the counterpart. The excellent lubricant and wear-resistant ability are attributed to the formation of MoS₂ transfer films and the ultra-smooth of the worn surfaces of hybrid coatings.     

Corrosion resistance of Al–Cr-slag containing chromium–corundum refractories to slags with different basicity

Al–Cr slag is the solid waste generated by the smelting of Cr metal. It presents a range of environmental hazards. This study addressed the corrosion resistance of Al–Cr slag containing chromium–corundum refractories to slags with different basicity. Herein, we provide suggestions for the use of Cr–corundum of different basicity in kilns. Al–Cr slag, brown fused Al₂O₃, and chrome green were used as the raw materials, with pure calcium aluminate cement being used as a binder. The brick samples, prepared using different blends of chrome green and corundum, were fired at 1600?°C, and subsequently subjected to a slag corrosion test. After corrosion by slag of different basicity, the phase composition and microstructure of the sample were analyzed by X-ray diffraction, energy dispersive spectrometer and scanning electron microscopy. There were two major findings. First, Cr–corundum brick made from Al–Cr slag has a better slag corrosion resistance than that made from Cr₂O₃ and brown fused Al₂O₃. Second, Cr–corundum brick made from Al–Cr slag has superior corrosion resistance to slag with a CaO:SiO₂ ratio of 2:1.     

Computational Fluid Dynamics Study on a Top-Blown Smelting Process with Lance Failure in an Isa Furnace

JOM - The Isa/Ausmelt smelting technology with a top submerged lance (TSL) has been extensively used in copper smelting processes. However, the TSL is extremely vulnerable to damage and failure...