Influence of Si-Doping on the Performance of InGaN/GaN Multiple Quantum Well Solar Cells

Semiconductors - The performance of InGaN/GaN multiple quantum well (MQW) solar cells with five different Si-doping concentrations, namely 0, 4 × 1017 cm–3, 1 × 1018 cm–3, 3...     

YSZ/MoS2 self-lubricating coating fabricated by thermal spraying and hydrothermal reaction

Thermal sprayed ceramic coatings have extensively been used in components to protect them against friction and wear. However, the poor lubricating ability severely limits their application. Herein, yttria-stabilized zirconia (YSZ)/MoS₂ composite coatings were successfully fabricated on steel substrate with the combination of thermal spraying technology and hydrothermal reaction. Results show that the synthetic MoS₂ powders are composed of numbers of ultra-thin sheets (about 7 ~ 8?nm), and the sheet has obvious lamellar structure. After vacuum impregnation and hydrothermal reaction, numbers of MoS₂ powders, look like flowers, generate inside the plasma sprayed YSZ coating. Moreover, the growing point of the MoS₂ flower is the intrinsic micro-pores of YSZ coating. The friction and wear tests under high vacuum environment indicate that the composite coating has an extremely long lifetime (>?100,000 cycles) and possesses a low friction coefficient less than 0.1, which is lower by about 0.15 times than that of YSZ coating. Meanwhile, the composite shows an extremely low wear rate (2.30?×?10^?7 mm³ N^?1 m^?1) and causes slight wear damage to the counterpart. The excellent lubricant and wear-resistant ability are attributed to the formation of MoS₂ transfer films and the ultra-smooth of the worn surfaces of hybrid coatings.     

Transesterification of Palm-based Methyl Palmitate into Esteramine Catalyzed by Calcium Oxide Catalyst

The technology for transesterification reactions between methyl esters and alcohols is well established by using classical homogeneous alkaline catalysts, which provide high conversion of methyl esters to specialty or nonindigenous esters. However, in certain products where the purity of the esters is of concern, the removal of homogeneous catalysts after the completion of the reaction is a challenge in terms of production cost and water footprint. Therefore, a study to investigate the potential of heterogeneous catalysts was conducted on reactions between methyl palmitate and triethanolamine. The degree of basicity and active surface area of calcium oxide (CaO), zinc oxide (ZnO), and magnesium oxide (MgO) were first characterized by using temperature-programmed desorption (TPD-CO₂) and Brunauere–Emmett–Teller (BET), respectively. Among the metal oxides investigated, the CaO catalyst showed the best catalytic activity toward the transesterification process as it gave the highest conversion of methyl palmitate and yielded fatty esteramine compositions similar to the conventional homogeneous catalyst. The optimum transesterification condition by using the CaO catalyst utilized a lower vacuum system of approximately 200 mbar, which could minimize a considerable amount of energy consumption. Furthermore, low CaO dosage of 0.1% was able to give a conversion of 94.5% methyl ester and formed esteramine at 170 °C for 2 h. Therefore, the production of esterquats from esteramine may become more economically feasible through the methyl ester route by using the CaO catalyst, which can be recycled three times.     

Single-Crystalline TiO2(B) Nanobelts with Unusual Large Exposed {100} Facets and Enhanced Li-Storage Capacity

The {100} facet of single-crystalline TiO₂(B) is an ideal platform for inserting Li ions, but it is hard to be obtained due to its high surface energy. Here, the single-crystalline TiO₂(B) nanobelts from H₂Ti₃O₇ with nearly 70% {100} facets exposed are synthesized, which significantly enhances Li-storage capacity. The first-principle calculations demonstrate an ab in-plane 2D diffusion through the exposed {100} facets. As a consequence, the nanobelts can significantly accommodate Li ions in LiTiO₂ formula with specific capacity up to 335 mAh g⁻¹, which is in good agreement with the electrochemical characterizations. Coating with conductive and protective poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate), the cut-off discharge voltage is as low as 0.5 V, leading to a capacity of 160.7 mAh g⁻¹ after 1500 cycles with a retention rate of 66% at 1C. This work provides a practical strategy to increase the Li-ion capacity and cycle stability by tailoring the crystal orientation and nanostructures.     

Corrosion resistance of Al–Cr-slag containing chromium–corundum refractories to slags with different basicity

Al–Cr slag is the solid waste generated by the smelting of Cr metal. It presents a range of environmental hazards. This study addressed the corrosion resistance of Al–Cr slag containing chromium–corundum refractories to slags with different basicity. Herein, we provide suggestions for the use of Cr–corundum of different basicity in kilns. Al–Cr slag, brown fused Al₂O₃, and chrome green were used as the raw materials, with pure calcium aluminate cement being used as a binder. The brick samples, prepared using different blends of chrome green and corundum, were fired at 1600?°C, and subsequently subjected to a slag corrosion test. After corrosion by slag of different basicity, the phase composition and microstructure of the sample were analyzed by X-ray diffraction, energy dispersive spectrometer and scanning electron microscopy. There were two major findings. First, Cr–corundum brick made from Al–Cr slag has a better slag corrosion resistance than that made from Cr₂O₃ and brown fused Al₂O₃. Second, Cr–corundum brick made from Al–Cr slag has superior corrosion resistance to slag with a CaO:SiO₂ ratio of 2:1.     

Computational Fluid Dynamics Study on a Top-Blown Smelting Process with Lance Failure in an Isa Furnace

JOM - The Isa/Ausmelt smelting technology with a top submerged lance (TSL) has been extensively used in copper smelting processes. However, the TSL is extremely vulnerable to damage and failure...     

In-situ crystal growth and photoluminescence properties of YBO3: Tb3+ microstructures

Three-dimensional (3D) YBO₃:Tb³⁺ flower-like and dense flower-like hierarchitecture constituted of nanoflakes are solvothermally synthesized in the presence of polyborate precursors in the mixture of ethanol and water. The growth process of the YBO₃:Tb³⁺ flowers and dense flowers was explored based on the time-dependent experiment and the results showed that the growth mechanism follows an in situ growth rather than self-assembly process as reported previously. YBO₃:Tb³⁺ morphologies composed of nanoflakes are achieved by controlling the concentration of ethanol and dependence of photoluminescence on morphology was studied. Remarkable photoluminescence enhancement was observed for YBO₃:Tb³⁺ with flower-like morphology demonstrating the potential of the microstructure in future applications as a green phosphor. Such a synthetic method and growth mechanism may be applied to fabricate complex 3D architectures of other materials.