Chromium evaporation and oxidation characteristics of alumina-forming austenitic stainless steels for balance of plant applications in solid oxide fuel cells

The chromium (Cr) evaporation behavior of several different types of iron (Fe)-based AFA alloys and benchmark Cr₂O₃-forming Fe-based 310 and Ni-based 625 alloys was investigated for 500 h exposures at 800 °C to 900 °C in air with 10% H₂O. The Cr evaporation rates from alumina-forming austenitic (AFA) alloys were ~5 to 35 times lower than that of the Cr₂O₃-forming alloys depending on alloy and temperature. The Cr evaporation behavior was correlated with extensive characterization of the chemistry and microstructure of the oxide scales, which also revealed a degree of quartz tube Si contamination during the test. Long-term oxidation kinetics were also assessed at 800 to 1000 °C for up to 10,000 h in air with 10% H₂O to provide further guidance for SOFC BOP component alloy selection.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Different hydrothermal corrosion results between two sides of sodalime float glass and the possible corrosion mechanism

Sodalime float (SF) glass is widely used in our societies and industries. Hydrothermal corrosion method is one of the effective ways to prepare a superhydrophobic glass, but there is still lack of knowledge about hydrothermal corrosion behavior and mechanism of SF glass. We have hydrothermally treated SF glass at 180 °C for different time, and tried to reveal the aqueous corrosion process of SF glass. We have characterized the morphologies and chemical compositions of samples, and found that (1) the two sides of SF glass have different corrosion resistances, and (2) a multilayer structural coating with a nanoflake layer (Mg-rich gel layer), a nanowire layer (Ca-rich gel layer), and a porous layer (etched layer) is formed on the air-side of SF glass. Based on the experimental results, we have proposed an aqueous corrosion mechanism of SF glass. The insights of the hydrothermal corrosion behaviors and mechanism provide helpful guidelines to glass surface structural control and functionalization.     

High-rate capability of carbon-coated micron-sized hexagonal TT-Nb2O5 composites for lithium-ion battery

With excellent specific capacity, superior cycle stability, safety and strong practical, Nb₂O₅ has been considered as one of the prospective anode materials for lithium-ion batteries (LIBs). However, current study suggests that Nb₂O₅ electrode materials for LIBs still face the vital issues of low electrical conductivity and poor rate performance. Therefore, carbon-coated TT-Nb₂O₅ materials are designed and synthesized through solid state method in this work, which present high specific capacity (228 mA h g^?1 at 0.2C), satisfactory rate properties (107 mA h g^?1 at 20 C). The outstanding electrochemical property can not only give the credit to the pseudocapacitance effect of TT-Nb₂O₅, but also attribute to introduction of carbon. The homogeneous carbon-coated materials enhance the electrical conductivity, increase the electron transmission speed and alleviate particle crushing. This research not only offers a new method for preparing excellent electrode materials, but also provides a kind of excellent anode material with prospective application for LIBs.     

超细粉在内循环流化床中的流态化特性

在内径120 mm的半圆柱形内循环流化床中,以平均粒径387 nm的Ti O2为原料,考察了单独通入流化气、射流气和同时通入流化气和射流气三种流化方式下超细粉的流化特性以及射流气速对超细粉聚团尺寸的影响。结果表明:同时通入流化气和射流气时,流化气能促进粉体循环,消除环隙死区;高速射流能有效破碎聚团,显著减小聚团尺寸,从而使超细粉在环隙区与导流管之间形成稳定循环,小聚团在环隙区实现平稳流态化。随着射流气速的增大,聚团尺寸减小,粒度分布变窄,在射流气速分别为60,90,120,150 m/s的条件下,聚团平均直径分别为194,158,147,135μm。     

Preparation and electrochromism of pyrochlore-type tungsten oxide film

Pyrochlore-type WO_3 powder was synthesized via hydrothermal method using aqueous sodium tungstate solution and oxalic acid as raw materials. The as-prepared powder was made into a soliquoid,from which films were made by dip coating process with indium-tin oxide(ITO).The obtained films were characterized by thermogravimetric and differential thermal analysis(TG-DTA), X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM), cyclic voltammetry(CV), chronoamperometry(CA) and ultravioletvisible(UV-Vis) absorption. Results show that the crystal of the pyrochlore-type WO_3 powder is perfect. When the calcination temperature rises from room temperature to500 ℃,the pyrochlore-type structure first becomes deformed, then it is destroyed and turns into amorphous phase,finally it will completely convert to WO_3 with a monoclinic structure. Electrochemical and optical tests demonstrate that the film calcined at 300 ℃ exhibits the best electrochromic performance and has a coloration efficiency of up to 68.5 cm~2 C~(-1) at 884 nm.     

Transparent niobate glass-ceramics for optical limiting

The construction of nonlinear optical materials featuring asymmetric transmission of light is of great technological importance for various applications, including optical switching and optical power limiting. A significant challenge is the scalable fabrication of material candidates with good photochemical stability, high optical transmittance, and excellent optical limiting performance. Here, we present a nanocrystallization avenue for constructing hybrid optical limiting materials that exhibit ultrafast and robust optical limiting performance. The experimental results show that the controllable relaxation of a niobate glass may lead to the clustering of Nb-O units and contracting of the bandgap. It results in the notable improvement in nonlinear optical properties, including the enhanced saturation irradiance (380 GW/cm²), doubly increased nonlinear coefficient, and decreased limiting threshold (200 GW/cm²). Our results suggest a promising material that exhibits promising applications for protecting eyes and sensitive components from laser-induced damage.