Optical dispersion and dielectric properties of rubrene organic semiconductor thin film

Rubrene thin film has been fabricated on a glass substrate by spin-coating at 300 K. The optical dispersion and dielectric properties of the film have been determined from the analysis of transmittance and reflectance measurements at normal incident of light between 200 and 700 nm. The optical transmittance of the film was estimated as of 80–85 % in the visible range. Optical absorption characteristics show that the absorption mechanism is due to the indirect transition. The transport and onset optical energy gaps were determined as 2.93 and 2.31 eV, respectively. Single term Sellmeier dispersion relation and Wemple–DiDomenico single oscillator model were used to determine the optical dispersion parameters. Several dispersion parameters such as lattice dielectric constant, optical dielectric constant at higher frequency, dispersion energy, oscillator energy, the ratio of carrier concentration to the effective mass, the average oscillator wavelength, and average oscillator strength were determined by analysis of refractive index dispersion. The loss factor, the electric modulus, the optical conductivity, the volume and surface energy loss functions, and the relaxation time were also evaluated from the optical dielectric constants analysis.     

被动网络信息收集与分析技术研究*

网络安全的关键问题是对受保护网络的全面了解.网络管理员可以通过使用嗅探器被动地监听网络通信而得到主动扫描网络所获得的大部分信息.介绍了如何在不影响网络带宽和网络服务的前提下使用被动信息收集技术获得有关网络信息的方法,给出了数据包的分析过程,讨论了被动信息收集技术的优点和不足.     

Effects of hydrogen on fatigue life of Ti-4Al-2V titanium alloy

1　INTRODUCTIONFewresearcheshaveplacedontheregionofhy drogen influenceonfatiguepropertiesoftitaniumal loys .Becausetheeffectsofhydrogenonpropertiesoftitaniumaredifferentfromthoseonsteel,plusthattitaniumalloysarehydrogenstoragematerials ,theeffectsofhydrogenarequitecomplex .AlthoughthefunctionsoffatigueloadingsΔσamplitudefortheini tiationandpropagationoffatiguecracksofhydrogenchargedtitaniumalloyshavenotbeenreported ,alotofstudies[1,2 ] ofthosefunctionsonstaticloadingshavebeenmade .Willi…     

含Si量对Mullite纤维/Al-Cu-Si复合材料及其基体合金时效行为的影响

用挤压铸造方法制备了Mullite/Al Cu Si复合材料。用硬度 (HB)测试仪、差示扫描量热仪 (DSC)和显微镜研究含Si量变化和Mullite纤维对Al Cu Si合金时效硬化行为的影响 ;元素Si、Mullite纤维以及二者同时存在对Al Cu Si合金时效析出序列的影响。结果表明 :Si和Mullite纤维明显抑制了Al Cu合金GP区的形成 ;随着含Si量增加 ,Al Cu Si合金的时效硬化过程加快 ;Mullite纤维对Al Cu和Al Cu Si合金的时效硬化过程都具有加速作用 ,同时提高了基体合金的时效硬度 ,但相对而言 ,Mullite纤维对无Si的Al Cu合金的时效硬化加速作用更为明显一些。     

基于生成对抗网络的MR图像合成研究

目前,深度学习已广泛用于MR医学图像分析,然而获取大量的MR训练数据集是一项巨大的挑战。针对传统基于物理方法的数据集扩充方法(如旋转、缩放、仿射变换等)均存在较大的局限性,提出一种新的图像合成器。首先对MR图像数据集进行统一的尺寸处理,然后将每张图像分为大小相等的非重叠块,再利用自动编码器提取图像块的编码,并将图像块编码和随机噪声作为生成器的输入,最后将生成的图像块拼接成完整的MR图像。采用该方法对脑部MR图像进行实验,并对生成图像进行定性定量分析。实验结果表明,所提方法能生成高质量的MR图像且优于其他主流方法。     

W-Ni/Yb2O3复合材料的制备及烧结性能研究

本文首先采用化学镀获得Ni-Yb2O3复合粉体,然后通过机械球磨制备了不同成分的W-（0.2、0.5、1、2）wt% Ni/Yb2O3复合粉末,最后在1600℃下烧结3h获得了W-Ni/Yb2O3复合材料。采用场发射扫描电子显微镜(FE-SEM)研究分析了Ni-Yb2O3复合粉体形貌、W-Ni/Yb2O3复合材料表面形貌。测定了W-Ni/Yb2O3复合材料相对密度、显微硬度和热导率。实验结果表明,W-Ni/Yb2O3复合材料的相对密度和显微硬度随着Ni-Yb2O3含量增加而增加,Ni-Yb2O3的加入促进了钨基材料的烧结致密化;同时,添加Ni-Yb2O3复合粉使钨基材料的晶粒得到细化,但对钨基材料导热性起到降低的作用。     

化学镀和粉末冶金法制备W/Cu梯度热沉材料

用化学镀法和粉末冶金的方法制备高致密的W/Cu梯度热沉材料。用场发射扫描电镜观察了材料的组织结构、界面和断口形貌。对材料的机械性能也进行了表征,如抗弯强度和显微硬度。结果表明材料每一层都很致密且组织结构均匀。从截面上材料成分呈梯度分布,每层之间没有明显的界面。三层W/Cu梯度热沉材料的相对密度可达99.2%。散热层、过渡层和封接层的显微硬度值分别是200、210和240 HV。抗弯实验结果所示封接层和散热层作为承重抗弯表面时的抗弯强度分别是428.5MPa和480.7MPa。     

电子辐照对CuZnAl形状记忆合金相变温度的影响

用能量1.7MeV不同注量的电子辐照CuZnAl形状记忆合金样品, 辐照在母相进行. DSC实验结果表明, 辐照前后样品的相变温度As从339K升高到347K, Ms从330K升高到340K, As-Ms从4K升高到7K. XRD分析结果表明辐照导致两组成对晶面间距差(Δd)增大, 证明辐照促进了有序化. 相变温度的变化是由于电子辐照产生的点缺陷造成了马氏体相点阵畸变和有序度的变化, 从而产生马氏体稳定化.     

Mulliet／Al—4.5Cu复合材料的时效析出行为

选用挤压铸造法制备mullite/Al-4.5Cu复合材料,采用硬度测试（HB）、差示扫描量热DSC、透射电镜（TEM）等手段研究了mullite/Al-4.5Cu复合材料的时效特性。结果表明：莫来石纤维的引入明显提高了基体合金的时效硬度,加速了基体合金的时效硬化速度,对GP区的形成有抑作用,但没有改变基体合金的时效析出序列。复合材料具有和基体合金相似的时效硬化曲线。温度对两类材料时效硬化行为的影响基本一致。