Mg0.5NixZn0.5-xFe2O4 spinel as a sustainable magnetic nano-photocatalyst with dopant driven band shifting and reduced recombination for visible and solar degradation of Reactive Blue-19

Focussing on visible light active ferrites for high performance removal of noxious pollutants, we report the synthesis of Mg_0.5Ni_xZn_0.5-xFe₂O₄ (x = 0.1, 0.2, 0.3, 0.4, & 0.5) ferrite nanoparticle for degradation of reactive blue-19 (RB-19). Lattice parameters calculated using intense X-ray diffraction (XRD) peaks and Nelson-Riley plots (N-R plot) are in well agreement with each other. The sample Mg_0.5Ni_0.4Zn_0.1Fe₂O₄ (M5N4) exhibits best performance with 99.5% RB-19 degradation in 90 min under visible light. Photoluminescence (PL) results confirm that recombination of charge carriers is highly reduced in the photocatalyst. Scavenging experiments suggest that O₂⁻ radicals were the dominant species responsible for photocatalytic performance. The photocatalytic mechanism was explained in terms of dopant driven shifting of conduction bands and valence bands (calculated by Mott-Schottky plots). The thermodynamic probability of radical generation along with role of redox cycles of metal ions has been discussed in the mechanism. The dye degradation was ascertained by detection of intermediates via mass spectrometry analysis and a possible degradation route was also predicted. The findings in this work provide intriguing opportunities to modify the electronic band structure of spinel ferrites for visible and solar light photocatalytic activity for environmental detoxification.     

Value chain analysis of bio-coal business in Finland: Perspectives from multiple value chain members

The purpose of this study is to provide a comprehensive outline of the Value Chain (VC)¹ of bio-coal in Finland, define the proper business models of bio-coal business, and investigate the interrelationships between VC activities. The major findings are: 1) the study found significant interrelationships between support and primary activities in the bio-coal VC which suggest that we should not emphasis only the core value/primary activities of the bio-coal business, but pay more attentions to the “side values”/support activities; 2) The study identified political and environmental factors as the effective drivers, while technology and cost-profit uncertainty as major restrictions for the Finnish bio-coal business. The authors would like to suggest that instead of purely “environmental concerns”, the term “sustainability credentials” should be emphasized, which means value creating and adding items should not limit to monetary values, but consider social and environmental value propositions. 3) The study identified “low competition” in the current bio-coal business in Finland, which implies opportunities of market entrance for Finnish and international companies; 4) The study identified that the current Finnish bio-coal model is the decentralized model at the local level. However, the future Finnish bio-coal model will be a large scaled model, with a focus on export sales.     

The bushmeat and food security nexus: A global account of the contributions,conundrums and ethical collisions

Wild meat or ‘bushmeat’ has long served as a principal source of protein and a key contributor to the food security of millions of people across the developing world, most notably in Africa, Latin America and Asia. More recently, however, growing human populations, technological elaborations and the emergence of a booming commercial bushmeat trade have culminated in unprecedented harvest rates and the consequent decline of numerous wildlife populations. Most research efforts aimed at tackling this problem to date have been rooted in the biological disciplines, focused on quantifying the trade and measuring its level of destruction on wildlife and ecosystems. Comparatively little effort, on the other hand, has been expended on illuminating the role of bushmeat in human livelihoods and in providing alternative sources of food and income, as well as the infrastructure to make these feasible. This paper aims to shift the focus to the human dimension, emphasising the true contributions of bushmeat to food security, nutrition and well-being, while balancing this perspective by considering the far-reaching impacts of overexploitation. What emerges from this synthesis is that bushmeat management will ultimately depend on understanding and working with people, with any approaches focused too narrowly on biodiversity preservation running the risk of failure in the long term. If wildlife is to survive and be utilised in the future, there is undoubtedly a need to relax adherence to unswerving biocentric or anthropocentric convictions, to appreciate the necessity for certain trade-offs and to develop integrated and flexible approaches that reconcile the requirements of both the animals and the people.     

High-temperature stability of Mg(Al,Cr)2O4 spinel co-existing with calcium aluminates in air

Cr₂O₃ is a well-known corrosion resistant oxide used in refractory applications. However, it can oxidize into toxic and water-soluble Cr(VI) compounds upon reaction with calcium aluminate cement phases in the presence of oxygen, which subsequently causes disposal problems after use. This study describes the extent to which chromium in the spinel Mg(Al,Cr)₂O₄ phase can be oxidized to Cr(VI) when it reacts with the calcium aluminate cement phases C₁₂A₇, CA, CA₂ and free CaO at 1300 °C in air, using XRD, XPS and leaching tests (TRGS 613 standard) as analytical tools. On reaction with CaO, the Mg(Al,Cr^III)₂O₄ spinel mainly transformed into hauyne (Ca₄Al₆Cr^VIO₁₆) and Ca₅Cr₃O₁₂ which contains both Cr(IV) and Cr(VI). The reaction of C₁₂A₇ and CA with the spinel phase also resulted in the formation of Ca₄Al₆CrO₁₆. Conversely, the reaction of Mg(Al,Cr^III)₂O₄ spinel with CA₂ resulted in the formation of only a trace amount of Cr(VI). Water-soluble Cr(VI) leached in large quantities (>100 mg/L) from samples where the Mg(Al,Cr^III)₂O₄ reacted with either C₁₂A₇ or CA. Almost no Cr(VI) leached from the sample when Mg(Al,Cr^III)₂O₄ reacted with CaO, using the standard TRGS 613 leach test, but a significant amount of Cr(VI) was released into solution when leached with a HCl solution for 12 h. Both Cr(IV) and Cr(VI) present in the Ca₅Cr₃O₁₂ dissolved into acidic solution. Only a small amount of Cr(VI) leached from the sample that resulted when spinel was reacted with CA₂, even after a prolonged HCl leach. Cr(III) in spinel Mg(Al,Cr)₂O₄ is very stable and does not leach in either distilled water or acidic solution.     

Application of the Microsoft Excel Solver tool in the solution of optimization problems of heat exchanger network systems

Optimization of heat exchanger networks (HEN_S) is a field of interest in Chemical Engineering. The aim is to use the residual heat of process streams to raise the temperature of other process streams which are cold, thus minimizing the use of hot and cold utilities. The usual way to deal with this task is to pose a linear programming problem according to a transshipment model in order to minimize either the general services consumptions or the number of hot and cold stream matchings required. This optimization is subjected to several restrictions given by the energy balances corresponding to each heat exchange.The high number of variables and equations obliges the use of specific software to solve these problems, e.g. GAMS (General Algebraic Modelling System). However, this software is not intuitive and requires a long time of training and a certain level of practice for the students to adequately use it.This work describes the use of Microsoft Excel-Solver for the sequential solving of HEN_S optimization problems according to the transshipment model. Solver is a much simpler, intuitive and easily available tool for the students who, besides, usually learn how to use it in the first years of their degree, in Informatics or similar subjects. Thus, it is not necessary to spend extra time in the teaching of the software, time that may be devoted to other contents.This paper presents an example of HEN_S problem proposed in the subject Simulation and Optimization of Chemical Processes corresponding to the Joint Master in Chemical Engineering of the Rey Juan Carlos University and the Autónoma University of Madrid and solved by the students using Excel-Solver.     

Fabrication and properties of Si3N4 based ceramics using combustion synthesized powders

Silicon nitride (Si₃N₄) based ceramics were fabricated with β-SiAlON and Si₃N₄ powders synthesized by combustion synthesis method via power injection molding (PIM). In the PIM process, the solids loading for each material was first determined from the results of the torque rheometer experiment. The mixing process was repeated to produce the homogeneous feedstock, and homogeneity of feedstocks was evaluated by observing the shear viscosity with time at a constant shear rate. The rheological behavior of feedstocks was investigated using capillary rheometer. It found that both feedstocks have no problem in injection molding. The binder decomposition behavior was also investigated, and a wax-polymer binder system was nearly removed by the optimized solvent and thermal debinding processes. Thereafter, the debound samples were sintered at 1750 and 1800 °C for 4 h in nitrogen atmosphere. Regardless of sintering temperature, the relative density of higher than about 96% was achieved. When comparing mechanical properties including bending strength, Vickers hardness and fracture toughness, Si₃N₄ with 2 wt% Y₂O₃ and 5 wt% Al₂O₃ (Si₃N₄+2Y5A) had higher values than β-SiAlON with 4 wt% Y₂O₃ (β-SiAlON+4Y) regardless of sintering temperature. It was supported by observing the microstructures of the plasma-etched samples.     

The overall crystallization behavior of polyethylene/wax blends as phase change materials for thermal energy storage: A mini review

This review paper deals with the overall crystallization behavior of polyethylene/wax blends as phase change materials (PCMs) for thermal energy storage with the determination of their thermal properties. The addition of molten wax to the polyethylenes decreases the crystallization and melting temperatures of the blends. However, incorporating fillers to the polyethylene/wax blends can either decrease or increase the crystallization and melting temperatures of the composites depending on the filler type. The normalized enthalpy values of linear low-density polyethylene showed no significant change when increasing the wax content. On the contrary, the normalized enthalpy values of the wax in the blends were lesser than that of pure wax and increased with increasing wax content. Since the wax in the blend had a lower crystallinity compared to pure wax, this influences its effectiveness as a PCM for thermal energy storage. The effect of different polyethylenes on the wax morphology gave rise to enhance phase separation when wax was blended to high-density polyethylene as compared to the other polyethylenes. On the contrary, the effect of various waxes on the morphology of polyethylene resulted in different morphologies due to the molecular weight of the wax used and the structure of the polyethylene chain. The addition of fillers to the polyethylene (PE)/wax samples resulted in enhanced phase separation. The overall isothermal crystallization rate and the equilibrium melting temperature of PEs in the PEs/wax blends were depressed by wax addition due to the wax dilution effect.