The improvement of the self-healing ability of MoSi2 coatings at 900–1200 °C by introducing SiB6

The brittleness of MoSi₂ ceramic and the thermal mismatch between MoSi₂ coating and C / C composite lead to brittle cracking of the coating at 900−1200 °C. This problem has been overcome in this studyby introducing submicron-SiB₆ into the coating. The pre-fabricated cracks and a kinetics model of hot-pressed SiB₆-MoSi₂ ceramic could quantitatively predict the glass growth and crack healing. As expected, enhancing temperature and SiB₆ content increased the growth rate of the borosilicate glass and the crack healing ability of MoSi₂ ceramic, which was ascribed to the lower oxidation activation energy and larger specific surface area of submicron-SiB₆. For the plasma sprayed coating, SiB₆ with submicron structure was benefit for cracking inhibition and formation of borosilicate glass during oxidation, reducing the oxygen permeability and the consumption of inner coating. Hence, the 15 % SiB₆-MoSi₂ coatings raised the protection times to 84 and 120 h at 900 and 1200 °C respectively, presenting favorable oxidation protective performance.     

Failure analysis on welded joints of 347H austenitic boiler tubes

Microstructural and thermo-mechanical analyses using the finite element method (FEM) were performed on the welded joint of 347H boiler tubes in a coal-fired power plant after 3600 h of operation. The cracks in the failed tube started on the inner surface of the heat-affected zone (HAZ). This area had a high hardness value and volume fraction of strain-induced martensite. The plastic deformation around the crack was concentrated near the grain boundaries. This failure occurred as the stabilizing effect disappeared due to carbide dissolution in the heat-affected zone, and plastic deformation and tensile residual stress were formed at the inner side due to the solidification contraction of the outer bead.     

Combination of heat treatment and chitosan coating to improve postharvest quality of wolfberry (Lycium barbarum)

The synergistic application of hot water dip at 42 °C for 30 min and 1% chitosan coating on differentiation in postharvest quality traits, microstructure as well as microbiological evolution of wolfberry fruits was investigated. Fresh wolfberry fruits were stored at 2 ± 0.5 °C and 90% relative humidity (RH) for 28 days. Results indicated the combination of prestorage heat treatment and chitosan coating maintained higher levels of ascorbic acid, total phenolic contents and antioxidant capacity as well as lower decay, compared with untreated wolfberry fruits. The possible mechanism was that the heat treatment almost sealed open stomata to limit the sites of pathogen penetration into fruits independently, followed by the biofilm formed by chitosan which controlled secondary infections as well as slowed changes in fruit respiration and metabolic activity in wolfberries. The synergistically treated fruit also exhibited a higher acceptability obtained by sensory analysis after cold storage. In this sense, the integrated application of heat treatment and chitosan coating could be regarded as an effective strategy to extend storage life and maintain the postharvest quality of wolfberry fruits.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

Silver-plated polyamide fabrics with high electromagnetic shielding effectiveness performance prepared by in situ reduction of polydopamine and chemical silvering

In this article, the silver-plated polyamide fabrics (SPPAFs) with high electroconductibility and shielding effectiveness were fabricated by using in situ reduction of polydopamine and chemical silvering. The effects of SPPAFs dopamine (C₈H₁₁O₂N) and silver nitrate (AgNO₃) concentration on surface resistivity and electromagnetic interference shielding effectiveness were studied. The results showed that the surface resistivity of SPPAFs can reach a minimum value of 0.06 ± 0.014 Ω cm⁻¹, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 120 g L⁻¹. The shielding effectiveness of SPPAFs in the wide frequency range of 10–3000 MHz increases with the increase in the concentration of AgNO₃, and increases first and stabilizes afterward with increasing C₈H₁₁O₂N concentration. When the concentration of C₈H₁₁O₂N and AgNO₃ is 3 and 120 g L⁻¹, respectively, mean shielding effectiveness values in the low-, medium-, and high-frequency bands are 71.3, 73.8, and 76.1 dB, respectively. Moreover, the mean shielding effectiveness values is 83.79 dB in the frequency range of 1.2–2.3 GHz. The dominant shielding mechanism of SPPAFs is the reflected electromagnetic waves and the absorption shielding effectiveness is less than 2 dB. The average electromagnetic shielding values of SPPAFs are above 67 dB after 16 weeks of storage, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 80 and 100 g L⁻¹. The prepared SPPAFs show promising applications in military textiles and smart wearable clothing. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48227.