Remarkably enhanced energy storage properties of lead-free Ba0.53Sr0.47TiO3 thin films capacitors by optimizing bottom electrode thickness

The lead-free Ba_0.53Sr_0.47TiO₃ (BST) thin films buffered with La_0.67Sr_0.33MnO₃ (LSMO) bottom electrode of different thicknesses were fabricated by pulsed laser deposition method on a (001) SrTiO₃ substrate. It was found that the roughness of electrode decreases and substrate stress relaxes gradually with the increase of LSMO thickness, which is beneficial for weakening local high electric field and achieving higher E_b. Therefore, the recoverable energy density (W_rec) of BST films can be greatly improved up to 67.3 %, that is, from 30.6 J/cm³ for the LSMO thickness of 30 nm up to 51.2 J/cm³ for the LSMO thickness of 140 nm after optimizing the LSMO thickness. Furthermore, the thin film capacitor with a 140 nm LSMO bottom electrode shows an outstanding thermal stability from 20 °C to 160 °C and superior fatigue resistance after 10⁸ electrical cycles with only a slightly decrease of W_rec below 1.6 % and 3.7 %, respectively. Our work demonstrates that optimizing bottom electrodes thickness is a promising way for enhancing energy storage properties of thin-film capacitors.     

Characteristics and formation mechanism of porosities in CFRP during laser joining of CFRP and steel

An experimental investigation on the mechanism of porosity formation during the laser joining of carbon fiber reinforced polymer (CFRP) and steel is presented. The porosity morphology and distribution were characterized by optical and scanning electron microscopy, and the thermal pyrolysis behaviors were investigated by thermal analysis and designed back-side cooling experiments. The results show that there are two types of porosities in CFRP. Porosity I only appears when the heat input is more than 77.8 J/mm. It has a smooth inner wall and distributes near the bonding interface between CFRP and steel at the central area of melted zone, which is caused by gaseous products such as CO₂, NH₃, H₂O, and hydrocarbons produced by the pyrolysis of CFRP. Porosity II can be seen under all joining conditions. It has a rough inner wall and distributes far away from the bonding interface, concentrating at the final solidification locations. Porosity II is caused by the shrinkage of melted CFRP during solidification stage.     

Resistive switching characteristics of ZnO–graphene quantum dots and their use as an active component of an organic memory cell with one diode-one resistor architecture

We investigated the resistive switching characteristics of a polystyrene:ZnO–graphene quantum dots system and its potential application in a one diode-one resistor architecture of an organic memory cell. The log–log I–V plot and the temperature-variable I–V measurements revealed that the switching mechanism in a low-current state is closely related to thermally activated transport. The turn-on process was induced by a space-charge-limited current mechanism resulted from the ZnO–graphene quantum dots acting as charge trap sites, and charge transfer through filamentary path. The memory device with a diode presented a ∼10³ I_ON/I_OFF ratio, stable endurance cycles (10² cycles) and retention times (10⁴ s), and uniform cell-to-cell switching. The one diode-one resistor architecture can effectively reduce cross-talk issue and realize a cross bar array as large as ∼3 kbit in the readout margin estimation. Furthermore, a specific word was encoded using the standard ASCII character code.     

Hydrocarbon-based electrode ionomer for proton exchange membrane fuel cells

The electrode ionomer is a key factor that significantly affects the catalyst layer morphology and fuel cell performance. Herein, sulfonated poly(arylene ether sulfone)-based electrode ionomers with polymers of various molecular weights and alcohol/water mixtures were prepared, and those comprising the alcohol/water mixture showed a higher performance than the ones prepared using higher boiling solvents, such as dimethylacetamide; this is owing to the formation of the uniformly dispersed ionomer catalyst layer. The relation between ionomer molecular weight for the same polymer structure and the sulfonation degree was investigated. Because the chain length of polymer varies with molecular weight and chain entanglement degree, its molecular weight affects the electrode morphology. As the ionomer covered the catalyst, the agglomerates formed were of different morphologies according to their molecular weight, which could be deduced indirectly through dynamic light scattering and scanning electron microscopy. Additionally, the fuel cell performance was confirmed in the current-voltage curve.     

Chemistry of multifunctional polymers based on bis-MPA and their cutting-edge applications

Polymers play an important role in the advancement of materials for use in cutting-edge applications. A direct consequence of an increased demand for more sophisticated materials has been a drive toward developing polymers that exhibit a higher level of structural control, especially in terms of the number and type of functionalities provided within the polymer framework. A family of polymers that meets such a challenge is based on the readily available AB₂ monomer 2,2-bismethylolpropionic acid (bis-MPA) building block. Due to the ease with which the monomers can be synthesized, an array of multifunctional polymers have been produced including monodisperse dendrimers and dendrons and well-defined linear polymers as well as linear-dendritic hybridizations. This review outlines the evolution of the synthetic strategies for developing novel polymeric architectures based on bis-MPA and their assessment in both solution and substrate-based innovative applications.     

Formation of high-density scintillation ceramic from LuAG:Ce + Lu2O3 powders obtained by co-precipitation method

The results of formation of the high density effective scintillation ceramics consisting of two compounds of the cubic symmetry, LuAG:Ce and Lu₂O₃ (LuAG:Ce + Lu₂O₃), are described. Powders of a novel material LuAG:Ce + Lu₂O₃ were synthesized by co-precipitation method. The introduction of Lu₂O₃ into LuAG:Ce was shown to increase the density of the ceramics obtained and modify its scintillation properties.     

Investigation on phase shifting for a 4 K Stirling pulse tube cryocooler with He-3 as working fluid

He-3 is generally recognized for its ability to provide more excellent thermophysical performance than He-4, especially in the 4 K temperature range. However, this was not always the case in our preliminary experiments on a three-stage Stirling-type pulse tube cryocooler (SPTC). Our ongoing studies, as reported in this paper, demonstrate that the different working fluids also affect the performance through their phase shifting capability. This feature has been passed over in large part by researchers considering refrigerant substitution. Unlike previous theoretical analyses that focus primarily on regenerator losses, this report investigates the effects of the working fluid on the phase angle at the cold end in order to quantitatively reveal the relationship between the lowest attainable temperature and the cooling capacity. The analysis agrees well with our experimental results on a three-stage SPTC. While running with the operating parameters optimized for He-3, the lowest temperature of the SPTC decreased from 5.4 K down to 4.03 K. This is the lowest refrigeration temperature ever achieved with a three-stage SPTC.     

Hydrothermal synthesis and characterization of surface-modified δ-MnO2 with high Fenton-like catalytic activity

Surface-modified δ-MnO₂ with a hierarchical structure was synthesized via a hydrothermal redox reaction between toluene and KMnO₄. Toluene is oxidized to produce benzoic acid which rapidly adsorbs onto the surface of δ-MnO₂. The δ-MnO₂ sample prepared with toluene exhibited a much higher catalytic activity for the Fenton-like oxidation of methylene blue in aqueous solution than that prepared without toluene. The enhanced catalytic activity might be attributed to the surface-bound persistent free radicals produced from the electron transfer from the adsorbed C₆H₅–COO⁻ to Mn(IV).     

Liner services network design and fleet deployment with empty container repositioning

Transportation demand of shipping container fluctuates due to the seasonality of international trade, thus, every 3–6 months, the liner company has to alter its current liner shipping service network, redeploy ships and design cargo routes with the objective of minimizing the total cost. To solve the problem, the paper presents a mixed integer linear program model. The proposed model incorporates several relevant constraints, such as weekly frequency, the transshipment of cargo between two or more service routes, and transport time. Extensive numerical experiments based on realistic date of Asia–Europe–Oceania shipping operations show that the proposed model can solve real-case problems efficiently by CPLEX. The results demonstrate that the model can reduce ship’s capacity consumption and raise ships’ capacity utilization.