Two-step pyrolytic engineering to form porous nitrogen-rich carbons with a 3D network structure for Zn-air battery oxygen reduction electrocatalysis

It is of great urgency to design inexpensive and high-performance oxygen reduction reaction (ORR) electrocatalysts derived from biowastes as substitutes for Pt-based materials in electrochemical energy-conversion devices. Here we propose a strategy to synthesize three-dimensional (3D) porous nitrogen-doped network carbons to catalyze the ORR from two-step pyrolysis engineering of biowaste scale combined with the use of a ZnCl₂ activator and a FeCl₂ promotor. Electrochemical tests show that the synthesized network carbons have exhibited comparable ORR catalytic activity with a half-wave potential (~0.85 V vs. RHE) and outstanding cyclical stability in comparison to the Pt/C catalyst. Beyond that, a high electron transfer number (~3.8) and a low peroxide yield (<7.6%) can be obtained, indicating a four-electron reaction pathway. The maximum power density is ~68 mW cm^?2, but continuous discharge curves (at a constant potential of ~1.30 V) for 12 h are not obviously declined in Zn-air battery tests using synthesized network carbons as the cathodic catalyst. The formation of 3D porous structures with high BET surface area can effectively expose the surface catalytic sites and promote mass transportation to boost the ORR activity. This work may open a new idea to prepare porous carbon-based catalysts for some important reactions in new energy devices.     

Strain engineering for thermal conductivity of single-walled carbon nanotube forests

We perform classical molecular dynamics simulations to investigate the mechanical compression effect on the thermal conductivity of the single-walled carbon nanotube (SWCNT) forest, in which SWCNTs are closely aligned and parallel with each other. We find that the thermal conductivity can be linearly enhanced by increasing compression before the buckling of SWCNT forests, but the thermal conductivity decreases quickly with further increasing compression after the forest is buckled. Our phonon mode analysis reveals that, before buckling, the smoothness of the inter-tube interface is maintained during compression, and the inter-tube van der Waals interaction is strengthened by the compression. Consequently, the twisting-like mode (good heat carrier) is well preserved and its group velocity is increased by increasing compression, resulting in the enhancement of the thermal conductivity. The buckling phenomenon changes the circular cross section of the SWCNT into ellipse, which causes effective roughness at the inter-tube interface for the twisting motion. As a result, in ellipse SWCNTs, the radial breathing mode (poor heat carrier) becomes the most favorable motion instead of the twisting-like mode and the group velocity of the twisting-like mode drops considerably, both of which lead to the quick decrease of the thermal conductivity with further increasing compression after buckling.     

Synthesis and characterization of Manganese doped Tungsten oxide by Microwave irradiation method

The aim of this article is to synthesis tungsten oxide (WO₃) nanoparticle along with Manganese (3 wt% and 10 wt%) by Microwave irradiation method. The physical properties of the synthesized Manganese doped Tungsten oxide materials were characterized by X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Transmission Electron Microscope (TEM), UV-Diffuse Reflectance Spectroscopy, SEM-EDAX and Photoluminescence studies. The predominant peaks obtained in X-ray diffraction pattern reveal the crystalline nature of the nanoparticles and the structure belongs to Monoclinic for pure and Mn doped WO₃. FTIR analysis shows the presence of Tungsten and oxygen in the synthesis material and verified with EDAX. TEM analysis shows both pristine and Mn doped WO₃ nanopaticles. They are having spherical shaped morphology with average particle size from 35 to 40 nm. UV-DRS revealed that the bandgap energy for pure and Manganese doped WO₃ are discussed in this article. The Scanning Electron Microscope analysis shows the plate like morphology for pure WO₃ and the morphology were decreased by doping Manganese. The defects and oxygen deficiencies were analysed by photoluminescence spectroscopy.     

Preparation and characterization of mullite whisker reinforced ceramics made from coal fly ash

Ceramics with mullite whiskers were prepared from coal fly ash and Al₂O₃ raw materials, with AlF₃ used as an additive. The phase structures and microstructures of the ceramics were identified via X-ray diffraction and scanning electron microscopy, respectively. The results show that pickling of coal fly ash is an effective method for enhancing the flexural strength of ceramics. Sintering temperature and AlF₃ addition were also key factors influencing the creation of ideal ceramics. The ceramic made from pickled coal fly ash, 6?wt% AlF₃, and sintered at 1200?°C, exhibited the highest flexural strength of 59.1?MPa, and had a bulk density of 1.32?g/cm³ and porosity of 26.8%. The results show that ceramic materials made under these conditions are ideal candidates for manufacturing ceramic proppants for the exploitation of unconventional oil and gas resources.     

Iron-binding peptides from whey protein hydrolysates: Evaluation,isolation and sequencing by LC–MS/MS

Iron–peptide complexes have been considered a promising source of more bioavailable iron, with reduced side effects as compared to iron salts. Whey protein isolate (WPI) hydrolyzed by alcalase, pancreatin or flavourzyme was ultrafiltered (cut off 5 kDa) and their fractions – retentates and filtrates – were evaluated for iron-binding capacity. The Fe–hydrolysate complexation reaction resulted in a dramatic increase in iron solubility at pH 7.0, from 0% to almost 100%. This result was obtained regardless of the molecular mass profile or the enzyme used to obtain the samples. Fractions from hydrolysate obtained with pancreatin (HP) were chosen to continue the study. The complexes formed with both fractions from HP were stable under simulated gastric digestion (50.8–89.4%). To identify the peptides with iron-binding capacity, the HP fractions were isolated by IMAC-Fe^3 +, and the retentate showed higher relative concentrations of iron-binding peptides than the filtrate. Iron-binding peptide sequencing, accomplished by LC–MS/MS, showed Glu and/or Asp in all the sequences, and their carboxylic groups were amongst the main iron-binding sites. WPI hydrolysis with pancreatin yields peptides that can form iron complexes with the potential to increase iron bioavailability and reduce its pro-oxidant effect.     

Fabrication and microwave absorption properties of magnetite nanoparticle–carbon nanotube–hollow carbon fiber composites

Absorbents with “tree-like” structures, which were composed of hollow porous carbon fibers (HPCFs) acting as “trunk” structures, carbon nanotubes (CNTs) as “branch” structures and magnetite (Fe₃O₄) nanoparticles playing the role of “fruit” structures were prepared by chemical vapor deposition technique and chemical reaction. Microwave reflection loss, permittivity and permeability of Fe₃O₄–CNTs–HPCFs composites were investigated in the frequency range of 2–18 GHz. It was proven that prepared absorbents possessed the excellent electromagnetic wave absorbing performances. The bandwidth with a reflection loss less than −15 dB covers a wide frequency range from 10.2 to 18 GHz with the thickness of 1.5–3.0 mm, and the minimum reflection loss is −50.9 dB at 14.03 GHz with a 2.5 mm thick sample layer. Microwave absorbing mechanism of the Fe₃O₄–CNTs–HPCFs composites is concluded as dielectric polarization and the synergetic interactions exist between Fe₃O₄ and CNTs–HPCFs.     

Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Electromagnetic shielding properties of iron oxide impregnated kenaf bast fiberboard

The electromagnetic shielding effectiveness of kenaf fiber based composites with different iron oxide impregnation levels was investigated. The kenaf fibers were retted for removing the lignin and extractives from the fibers and magnetized. Using the unsaturated polyester and the magnetized fibers, kenaf fiber based composites were manufactured by the compression molding process. The transmission energies of the composites were characterized when the composite samples were exposed under the irradiation of electromagnetic (EM) wave with a variable frequency from 9 GHz to 11 GHz. Using the Scanning Electron Microscope (SEM), the iron oxide nanoparticles were observed on the surfaces and inside the micropore structures of single fibers. As the Fe content increased from 0% to 6.8%, 15.9% and 18.0%, the total surface free energy of kenaf fibers with the magnetizing treatments increased from 44.8 mJ/m² to 46.1 mJ/m², 48.8 mJ/m² and 53.0 mJ/m², respectively, while the modulus of elasticity reduced from 2875 MPa to 2729 MPa, 2487 MPa and 2007 MPa, respectively. Meanwhile, the shielding effectiveness was increased from 30–50% to 60–70%, 65–75% and 70–80%, respectively.