Physical characteristics of AFEX-pretreated and densified switchgrass,prairie cord grass,and corn stover

The goal of the study was to evaluate and compare the physical properties of control, pretreated and densified corn stover, switchgrass, and prairie cord grass samples. Ammonia Fiber Expansion (AFEX) pretreated switchgrass, corn stover, and prairie cord grass samples were densified by using the comPAKco device developed by Federal Machine Company of Fargo, ND. The densified biomass were referred as “PAKs” in this study. All feedstocks were ground into three different grind size of 2, 4 and 8 mm prior to AFEX pretreatment and the impact of grinding on pellet properties was studied. The results showed that the physical properties of AFEX-PAKed material were not influenced by the initial grind size of the feedstocks. The bulk density of the AFEX-PAKed biomass increased by 1.2–6 fold as compared to untreated and AFEX-pretreated materials. The durability of the AFEX-PAKed materials were between 78.25 and 95.2%, indicating that the AFEX-PAKed biomass can be transported easily. To understand the effect of storage on the physical properties of these materials, samples were stored in the ambient condition (20 ± 2 °C and 70 ± 5% relative humidity) for six months. After storage, thermal properties of the biomass did not change but glass transition temperature decreased. The water absorption index and water solubility index of AFEX-treated and AFEX-PAKed biomass showed mixed trends after storage. Moisture content decreased and durability increased upon storage.     

HSDPA部署策略及覆盖、容量规划

本文介绍了HSDPA的发展背景,针对HSDPA的主要技术特点,依据市场发展规划、用户需求等方面对HSDPA部署进行探讨,并对HSDPA的覆盖与容量方面进行规划分析.     

Mesopore development in PAN-ACF resulting from non-metal additives

The narrow pore-size distribution of activated carbon fibres (ACF) limits their application in the fields concerning larger molecules, such as liquid adsorption and catalyst support. On the addition of carbon particles and organic materials to polyacrylonitrile fibres, and after stabilizing and activating, the mesoporosity in the resultant ACF has been obviously increased. Among these additives, carbon black gives the best effect. With 1 wt% carbon black I in precursor and on activating at 880°C for 30 min, a mesoporosity of 48.2% (total pore volume 0.704 ml g-1, mesopore volume 0.340 ml g-1) has been obtained. The mechanism of mesopore formation is also discussed. This revised version was published online in November 2006 with corrections to the Cover Date.     

Fischer-Tropsch synthesis on Fe-Mn ultrafine catalysts

The Fischer-Tropsch (FT) synthesis on Fe-Mn ultrafine catalysts prepared by a special degradation method of Fe-Mn complexes is presented. The effects of preparation method and Mn content on the FT performance are examined and the active phases and the role of Mn are elucidated.     

三相电压不平衡情况下电机车整流技术的研究

针对煤矿井下直流电机车变流系统中存在三相电压不平衡而使传统的PWM整流器的交流侧出现负序电流分量的问题,提出了一种在三相电压不平衡情况下抑制PWM整流器交流侧负序电流分量的控制策略;详细介绍了该控制策略的具体实现。仿真及现场实验结果表明,采用该控制策略后,PWM整流器的交流侧电流波形基本接近正弦波形,实现了单位功率因数运行。     

Efficient photodegradation of phenol assisted by persulfate under visible light irradiation via a nitrogen-doped titanium-carbon composite

To realize the utilization of visible light and improve the photocatalytic efficiency of organic pollutant degradation in wastewater, a nitrogen-doped titanium-carbon composite (N-TiO₂/AC) prepared by sol-gel methods was applied in the photodegradation of phenol assisted by persulfate under visible light irradiation (named N-TiO₂/AC/PS/VIS). The results show that a synergistic effect exists between visible-light photocatalysis and persulfate activation. Compared with TiO₂/PS/VIS, the phenol degradation rate was found to be observably improved by 65% in the N-TiO₂/AC/PS/VIS system. This significant increase in degradation rate was mainly attributed to the following two factors: 1) The N and C doping can change the crystal structure of TiO₂, which extends the TiO₂ absorption wavelength range to the visible light region. 2) As an electron acceptor, PS can not only prevent electrons and holes from recombining with each other but can also generate strong oxidizing radicals such as ∙SO₄^– and ∙OH to accelerate the reaction dynamics. The process of phenol degradation was found to be consistent with the Langmuir pseudo-first-order kinetic model with an apparent rate constant k of 1.73 min^–1. The N-TiO₂/AC/PS/VIS process was proven to be a facile method for pollutant degradation with high pH adaptability, excellent visible-light utilization and good application prospects.     

软段含离子基团的阴离子型水性聚氨酯胶粘剂的研究(Ⅱ)——硬段结构的影响

以含有不同离子基团的聚酯多元醇为软段,采用丙酮法合成了一系列水性聚氨酯乳液。研究了不同硬段结构和硬段含量和扩链剂对其干膜物理机械性能和吸水率的影响。     

煤与粘结剂的相互作用和型煤抗压强度的关系

煤的润湿性与型煤抗压强度相关。用于表征煤的润湿性方法有煤与淀粉粘结剂的接触角、粘合功、煤的润湿临界表面张力等。研究证明,随着煤化程度的升高,煤与淀粉粘结剂接触角变小,粘合功增加,粉煤的润湿性改善,型煤抗压强度得以提高。另外,煤的润湿临界表面张力越大,煤的润湿性越好,型煤抗压强度也就越高。     

Effect of preparation conditions on the properties of a coal-derived activated carbon honeycomb monolith

Activated carbon honeycomb (ACH) monoliths were prepared by extruding of a mixture of bituminous coal and organic additives and subsequent carbonization and steam activation. Preparation parameters that were varied were carbonization temperature and activation time. The carbonization conditions were 500, 650 and 800 °C for 1 h and the steam activation conditions were 850 °C for 2, 4 and 6 h. The monoliths at various states were characterized by SEM, XRD, nitrogen adsorption and compression test. It was found that carbonization temperature has significant effects on pore size distribution and mechanical strength of ACH monoliths. The ACH monoliths prepared from high carbonization temperatures exhibited lower values of the BET surface area and total pore volume and higher value of the mechanical strength than those of the ACH monoliths prepared from low carbonization temperatures. This was attributed to the effect of high temperature carbonization that results in the formation of relatively less defective structures.     

Role of La2O3 in Pd-Supported Catalysts for Methanol Decomposition

Systems of Pd supported on various La₂O₃-modified -Al₂O₃ and CeO₂–Al₂O₃ catalysts were tested for catalytic methanol decomposition and characterized by means of XRD, BET, TPR, H₂-chemisorption and CO–FTIR. The addition of lanthanum significantly improved the selectivity of CO and H₂ for all the catalysts but showed a different influence on the catalytic activity in two systems. Methanol conversion decreased on La₂O₃-modified Pd/-Al₂O₃ catalysts, in line with the reduction of Pd dispersion, while the addition of La₂O₃ improved the dispersion of Pd and reinforced Pd–CeO₂ interaction for La₂O₃-modified Pd/CeO₂–Al₂O₃ catalysts, which resulted in a high production rate of CO and H₂. Thus, a synergistic effect between CeO₂ and La₂O₃ was observed on -Al₂O₃-supported Pd catalyst for methanol decomposition.