Two-step pyrolytic engineering to form porous nitrogen-rich carbons with a 3D network structure for Zn-air battery oxygen reduction electrocatalysis

It is of great urgency to design inexpensive and high-performance oxygen reduction reaction (ORR) electrocatalysts derived from biowastes as substitutes for Pt-based materials in electrochemical energy-conversion devices. Here we propose a strategy to synthesize three-dimensional (3D) porous nitrogen-doped network carbons to catalyze the ORR from two-step pyrolysis engineering of biowaste scale combined with the use of a ZnCl₂ activator and a FeCl₂ promotor. Electrochemical tests show that the synthesized network carbons have exhibited comparable ORR catalytic activity with a half-wave potential (~0.85 V vs. RHE) and outstanding cyclical stability in comparison to the Pt/C catalyst. Beyond that, a high electron transfer number (~3.8) and a low peroxide yield (<7.6%) can be obtained, indicating a four-electron reaction pathway. The maximum power density is ~68 mW cm^?2, but continuous discharge curves (at a constant potential of ~1.30 V) for 12 h are not obviously declined in Zn-air battery tests using synthesized network carbons as the cathodic catalyst. The formation of 3D porous structures with high BET surface area can effectively expose the surface catalytic sites and promote mass transportation to boost the ORR activity. This work may open a new idea to prepare porous carbon-based catalysts for some important reactions in new energy devices.     

Relationship between the adhesion properties of UV-curable alumina suspensions and the functionalities and structures of UV-curable acrylate monomers for DLP-based ceramic stereolithography

Digital light processing (DLP)-based ceramic stereolithography has attracted significant attentions due to the high printing speed and high dimensional accuracy of DLP printers. However, undesired dropping of unfinished ceramic parts during printing, owing to inadequate adhesion between the first cured layer and the substrate of the building platform, still remains a challenge. In this study, the relationship between the adhesion properties of ultraviolet (UV)-curable alumina (α-Al₂O₃) suspensions and the functionalities and structures of UV-curable acrylate monomers was investigated. With an increase in the proportions of monofunctional monomers, the adhesion abilities of UV-curable alumina suspensions enhanced because of reduced volume shrinkage, however, inferior curing performances were observed due to a decrease in the double bond densities. Furthermore, the large-volume branched chain structures in monofunctional monomers and ethyoxyl groups in polyfunctional monomers effectively decreased the volume contraction, improving the adhesion performances of UV-curable alumina suspensions and facilitating the conversion of double bonds to provide excellent curing properties, further guaranteeing strong adhesion of these suspensions to the substrate.     

Rational Designs for Lithium-Sulfur Batteries with Low Electrolyte/Sulfur Ratio

Lithium-sulfur batteries (LSBs) are considered a promising next-generation energy storage device owing to their high theoretical energy density. However, their overall performance is limited by several critical issues such as lithium polysulfide (PS) shuttles, low sulfur utilization, and unstable Li metal anodes. Despite recent huge progress, the electrolyte/sulfur ratio (E/S) used is usually very high (≥20 µL mg⁻¹), which greatly reduces the practical energy density of devices. To push forward LSBs from the lab to the industry, considerable attention is devoted to reducing E/S while ensuring the electrochemical performance. To date, however, few reviews have comprehensively elucidated the possible strategies to achieve that purpose. In this review, recent advances in low E/S cathodes and anodes based on the issues resulting from low E/S and the corresponding solutions are summarized. These will be beneficial for a systematic understanding of the rational design ideas and research trends of low E/S LSBs. In particular, three strategies are proposed for cathodes: preventing PS formation/aggregation to avoid inadequate dissolution, designing multifunctional macroporous networks to address incomplete infiltration, and utilizing an imprison strategy to relieve the adsorption dependence on specific surface area. Finally, the challenges and future prospects for low E/S LSBs are discussed.     

Fabrication of BSCF-based mixed ionic-electronic conducting membrane by electrophoretic deposition for oxygen separation application

Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3-δ (BSCF), which exhibits a high mixed oxide ionic-electronic conduction, was used for the fabrication of an oxygen separation membrane. An asymmetric structure, which was a thin and dense BSCF membrane layer supported on a porous BSCF substrate, was fabricated by the electrophoretic deposition method (EPD). Porous BSCF supports were prepared by the uniaxial pressing method using a powder mixture with BSCF and starch as the pore-forming agent (0–50 wt.%). The sintering behaviors of the porous support and the thin layer were separately characterized by dilatometry to determine the co-fired temperature at which cracking did not occur. A crack-free and thin dense membrane layer, which had about a 15 μm thickness and >95% relative density, was obtained after optimizing the processes of EPD and sintering. The dense/porous interface was well-bonded and the oxygen permeation flux was 2.5 ml (STP) min⁻¹ cm^-2 at 850 °C.     

Performance improvement of conventional and inverted polymer solar cells with hydrophobic fluoropolymer as nonvolatile processing additive

The morphology of the photoactive layer critically affects the performance of the bulk heterojunction polymer solar cells (PSCs). To control the morphology, we introduced a hydrophobic fluoropolymer polyvinylidene fluoride (PVDF) as nonvolatile additive into the P3HT:PCBM active layer. The effect of PVDF on the surface and the bulk morphology were investigated by atomic force microscope and transmission electron microscopy, respectively. Through the repulsive interactions between the hydrophilic PCBM and the hydrophobic PVDF, much more uniform phase separation with good P3HT crystallinity is formed within the active layer, resulting enhanced light harvesting and improved photovoltaic performance in conventional devices. The PCE of the conventional device can improve from 2.40% to 3.07% with PVDF additive. The PVDF distribution within the active layer was investigated by secondary ion mass spectroscopy, confirming a bottom distribution of PVDF. Therefore, inverted device structure was designed, and the PCE can improve from 2.81% to 3.45% with PVDF additive. Our findings suggest that PVDF is a promising nonvolatile processing additive for high performance polymer solar cells.     

Microstructures and mechanical properties of B4C-TiB2-SiC composites fabricated by ball milling and hot pressing

B₄C-TiB₂-SiC composites were fabricated via hot pressing using ball milled B₄C, TiB₂, and SiC powder mixtures as the starting materials. The impact of ball milling on the densification behaviors, mechanical properties, and microstructures of the ceramic composites were investigated. The results showed that the refinement of the powder mixtures and the removal of the oxide impurities played an important role in the improvement of densification and properties. Moreover, the formation of the liquid phases during the sintering was deemed beneficial for densification. The typical values of relative density, hardness, bending strength, and fracture toughness of the composites reached 99.20%, 32.84?GPa, 858?MPa and 8.21?MPa?m^1/2, respectively. Crack deflection, crack bridging, crack branching, and microcracking were considered to be the potential toughening mechanisms in the composites. Furthermore, numerous nano-sized intergranular/intragranular phases and twin structures were observed in the B₄C-TiB₂-SiC composite.     

Effect of grinding-induced cyclic heating on the hardened layer generation in the plunge grinding of a cylindrical component

This paper discusses the effects of the grinding-induced cyclic heating on the properties of the hardened layer in a plunge cylindrical grinding process on the high strength steel EN26. It was found that a multi-pass grinding brings about a uniform and continuous hardened layer along the circumference of the cylindrical workpiece. An increase of the number of grinding passes, leads to a thicker layer of hardening, a larger compressive residual stress and a deeper plastic deformation zone. Within the plastic deformation zone, the martensitic grains are refined by the thermo-mechanical loading, giving rise to a hardness of 12.5% higher than that from a conventional martensitic transformation. The coupled effects of heat accumulation and wheel wear in the multi-pass grinding are the main causes for the thickening of the hardened layer. A too small infeed per workpiece revolution would result in insufficient grinding heat, and in turn, bring about an undesirable tempered hardened layer and a reduction of its hardness.     

应用数字PWM器件SA4828的大功率直流电源

本文介绍一种智能型、高精度PWR控制器SA4828，其控制实行全数字化产生三相脉宽调制波形．本文采用此器件设计大功率直流电源应用于22KW直流电机测试，对感性负载表现出具有纹波小，响应迅速、硬件电路简洁、控制简单易于编写的优点。     

APPLICATION OF COMPUTER NUMERICAL METHOD IN PORE STRUCTURE CALCULATION

This paper compares the results Of calculat-ing pore structure and graphing differential and integralpore size distribution by hand and Computer,and presents thatlagrangian interpolation uesd by calculating pore structure issuitable and reliable.     

一种环氧树脂阻尼灌封胶的热氧加速老化研究

研究了某种环氧树脂阻尼灌封胶在热氧老化的作用下分子结构、硬度、断面形貌以及动态力学性能随时间的变化．傅立叶红外光谱图表明，所制备的样品环氧基团反应比较完全，热氧老化后试样表面由仲胺和环氧基团形成的酯键发生了部分断裂和氧化；邵氏硬度的增加、瓦向高温区移动则表明在老化过程中复杂的固化反应仍然继续进行；最大损耗因子（tanδmax）波动较小表明试样老化后分子结构几乎保持不变；SEM图片显示试样的冲击断裂由老化前的韧性转变为老化后的脆性断裂．