New nanocomposite based on poly(lactic-co-glycolic acid) copolymer and magnetite. Synthesis and characterization

The study presents the preparation of the new magnetic nanocomposite based on PLGA and magnetite. The PLGA used to obtain the magnetic nanocomposites was synthesized by the copolymerization of lactic acid with glycolic acid, in the presence of tin octanoate [Sn(Oct)₂] as catalyst, by polycondensation procedure. Magnetite was obtained by co-precipitation from aqueous salt solutions FeCl₂/FeCl₃. The particles size of magnetite was 420 nm, and the saturation magnetization 62.78 emu/g, while the PLGA/magnetite nanocomposite size was 864 nm and the saturation magnetization 39.44 emu/g. The magnetic nanocomposites were characterized by FT-IR, DLS technique, SEM, VSM and simultaneous thermal analyses (TG–FTIR–MS). The polymer matrix PLGA acts as a shell and carrier for the active component, while magnetite is the component which makes targeting possible by external magnetic field manipulation. Based on the gases resulted by thermal degradation of PLGA copolymer, using the simultaneous analysis TG–FTIR–MS, a possible degradation mechanism was proposed.     

Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Electromagnetic shielding properties of iron oxide impregnated kenaf bast fiberboard

The electromagnetic shielding effectiveness of kenaf fiber based composites with different iron oxide impregnation levels was investigated. The kenaf fibers were retted for removing the lignin and extractives from the fibers and magnetized. Using the unsaturated polyester and the magnetized fibers, kenaf fiber based composites were manufactured by the compression molding process. The transmission energies of the composites were characterized when the composite samples were exposed under the irradiation of electromagnetic (EM) wave with a variable frequency from 9 GHz to 11 GHz. Using the Scanning Electron Microscope (SEM), the iron oxide nanoparticles were observed on the surfaces and inside the micropore structures of single fibers. As the Fe content increased from 0% to 6.8%, 15.9% and 18.0%, the total surface free energy of kenaf fibers with the magnetizing treatments increased from 44.8 mJ/m² to 46.1 mJ/m², 48.8 mJ/m² and 53.0 mJ/m², respectively, while the modulus of elasticity reduced from 2875 MPa to 2729 MPa, 2487 MPa and 2007 MPa, respectively. Meanwhile, the shielding effectiveness was increased from 30–50% to 60–70%, 65–75% and 70–80%, respectively.     

Synthesis and characterization of nanostructured magnetoresistive Ni doped ZnO films

We report a method to produce magnetic nanostructured semiconductor films based in ZnO doped with Nickel to control their magnetic properties. The method is based on a combined diffusion–oxidation process within a controlled atmosphere chamber to produce a uniform distribution of Ni ions in the ZnO films (ZnO:Ni). The synthesis of ZnO:Ni films is reported as well as the magnetoresistive characteristics, the used method yields films with reproducible and homogeneous properties. The films were also characterized structurally by X-Ray Diffraction (XRD) and Raman spectroscopy, and by Hall–van der Pauw measurements. The XRD measurements confirm the nanocrystalline films character. The films resulted of n-type conductivity with electron concentrations of ~10²⁰ cm⁻³ in average and carrier mobilities of 5 cm²/V s. The Magnetoresistance (MR) behavior of the films at 300 K shows negative changes of ΔR~0.5% in accordance with the usual literature reports on samples produced by other methods.     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Influences of magnetic fields on current–voltage characteristics of gold-DNA-gold structure with variable gaps

Achieving highly sensitive magnetic sensors by means of Metal-DNA-Metal (MDM) structure is a key issue. DNA, being a genetic information carrier in living cells reveals tunable semiconducting response in the presence of external electric and magnetic fields, which is promising for molecular electronics. The influence of magnetic fields up to 1200 mT on the current–voltage (I–V) behavior of Gold-DNA-Gold (GDG) structure having variable gap sizes from 20–50 μm are reported in this work. These structures were fabricated using UV lithography, DC magnetron sputtering and thermal evaporation techniques. DNA strands were extracted from Boesenbergia rotunda plant via standard protocol. The acquired I–V characteristics display the semiconducting diode nature of DNA in GDG structures. The potential barrier for all the structures exhibit an increasing trend with the increase of externally imposed magnetic field irrespective of variable gap sizes. Furthermore, the potential barrier in GDG junction at higher magnetic field strengths (>1000 mT) is found to be considerably enhanced. This enhancement in the junction barrier height at elevated magnetic fields is attributed to the reduction of carrier mobility and augmentation of resistance. The achieved admirable features of magnetic sensitivity suggest the viability of using these GDG sandwiches as a prospective magnetic sensor.     

Chemical leaching and magnetic properties of non-equilibrium Al(Co–Cu) powders produced by rod milling

We report upon the chemical leaching and magnetic properties of nanoscale crystalline Al_0.6(Co₂₅Cu₇₅)_0.4 alloy powders produced by rod milling. X-Ray diffractometry (XRD), transmission electron microscopy, differential scanning calorimetry, vibrating sample magnetometry, and superconducting quantum interference device magnetometry were used to characterize the as-milled and leached specimens. After 400 h of milling, only the b.c.c. phase of the intermetallic compound γ-Al_3.892Cu_6.10808 was detected by XRD. After annealing the leached specimen at 600 °C for 1 h, the nanoscale crystalline phase was transformed into the f.c.c. Cu phase, and this was accompanied by a change in the magnetic properties. The peaks of the magnetization shifted towards lower temperature with increasing external field. The temperature behavior at T_f (45 K) for direct current (d.c.) magnetic susceptibility measurements was quite different for field cooling and zero-field cooling. After cooling the leached specimen from 800 °C, magnetization increased gradually.     

The enhanced coercivity for the magnetite/silica nanocomposite at room temperature

Magnetite/silica nanocomposite was synthesized by a facile solvothermal processing at 150 °C for about 10 h. X-ray diffraction (XRD) analysis revealed the effect of annealing on the crystallinity of silica. Transmission electron microscopy (TEM) images showed the good dispersion of magnetite in the silica matrix. Magnetic properties of the nanocomposite were characterized by vibration sample magnetometer (VSM), and the enhanced coercivity was explained by the intrinsic anisotropy of the particles enhanced by the interparticle dipolar fields.     