水热法制备BiVO_4及其光催化性能研究

采用水热反应法并改变反应条件制备不同形貌和晶体结构的BiVO4可见光催化剂,并探讨不同形貌BiVO4的形成机制及其光催化活性的影响因素。借助X-射线衍射（XRD）、扫描电子显微镜（SEM）及固体紫外-可见漫反射光谱（DRS）对产品进行表征,并在可见光（λ〉420 nm）照射下考察其降解亚甲基蓝（MB）的光催化性能。结果表明,高温更有利于单斜型钒酸铋的生成,反应初始pH值对钒酸铋的形貌影响较大。反应过程中,前驱液中的颗粒通过溶解再结晶、定向聚集自组装、熟化过程最终形成不同形貌的钒酸铋颗粒。钒酸铋的光催化降解速率主要受其晶粒粒径和晶体微观应变的影响,晶粒粒径越大,微观应变越小,结晶度越好,降解速率越高。     

Fe/Bi0.5Sb1.5Te3热电元件高温稳定性研究

热电元件的界面高温稳定性是决定热电器件服役性能和应用前景的重要因素,而阻挡层和热电材料之间的界面扩散和界面电阻则是评价热电元件高温稳定性的主要标准.为了进一步提升P型碲化铋热电器件的界面稳定性,本研究采用高通量筛选的方法选定适用于P型碲化铋的Fe阻挡层材料.通过一步烧结的方法制备了Fe/P-BT的热电元件,并系统研究了...     

Al3+/Bi4Ti3O12薄膜的制备及其光催化性能表征

采用溶胶一凝胶法制备了掺 Al3+ 的Bi4 Ti3 O12 薄膜(Bl-xAlxTi3O12).采用分光光度法研究了薄膜对甲基橙溶液的降解,以及Al3+对薄膜的光催化效果影响.光催化结果表明,Al3+的掺杂量为 2atm% 时,薄膜的光催化效果最好,比未掺杂前提高 57.9%,且吸收边红移量为 36nm.     

掺钇铌酸锌铋陶瓷的介电性能

通过X射线衍射、扫描电镜、精密阻抗分析仪等对A位Y3 取代的Bi(1.5-x)YxZnNb1.5O7介质陶瓷样品的结构和介电性能进行了研究.结果表明:当Y3 取代量较少时(x≤0.2),样品保持立方焦绿石结构;当Y3 取代较多时(x≥0.4),样品出现第二相.随着取代量的增加,样品的致密化温度升高,表观密度减小,晶粒尺寸减小,介电常数减小,介电损耗增加.Y3 取代后(x≤0.8),样品的温度系数得到优化,且具有良好的高频稳定性.低温的介电弛豫现象随着Y3 取代的增加发生有规律的变化,表现为介电常数下降,介电常数峰宽化和平坦.     

钛酸铋钠基无铅压电陶瓷研究近期进展

钛酸铋钠(分子式是Bi0.5Na0.5TiO3,简写为BNT)基无铅压电陶瓷性能优良,但与铅基陶瓷相比还有相当的差距,其性能有待进一步提高.从BNT基陶瓷改性、陶瓷新体系以及陶瓷制备技术等多方面,分析了提高BNT基陶瓷性能的原理、途径和方法,指出了发明陶瓷新体系的有关思路,讨论了陶瓷制备技术与陶瓷性能的关系.同时,列举了近期在BNT基陶瓷性能改善研究中的若干新进展和新结果、性能良好的BNT基陶瓷新体系及制备工艺和制备新技术对陶瓷性能的影响,并对今后的相关研究进行了展望.     

热处理对氧化铋在8μm～14μm波段内的发射率的影响

本文通过设计正交实验,采用不同的热处理工艺对着色颜料氧化铋粉末进行热处理,随后测量样品在8μm～14μm波段的平均法向发射率,并得出优化的热处理工艺路线;对各个影响因素进行的分析表明,温度是热处理过程中影响样品发射率变化的主要因素,并通过XRD、SEM、EDS等多种表征手段,分析了红外发射率变化的内在机理.结果表明,晶格畸变是引起发射率变化的主要因素,而由气体分子吸附引起的表面成分变化对发射率也有一定的影响.     

Effect of wall wettability condition on drift-flux parameters in lead–bismuth two-phase flow in circular and annular bubble columns

Lead–bismuth two-phase flow in a cylindrical vessel and annulus was experimentally investigated by varying the surface wettability of the vessel wall. The test section used in this study was a cylindrical stainless vessel with/without inner sleeve to change the hydraulic diameter. Volume-averaged void fraction was measured by varying the surface wettability of the test section, which was enhanced by using a soldering flux. Measured void fraction was compared with existing two-phase flow correlations and with one-dimensional theoretical simulations assuming one-dimensional drift-flux model. From experimental results, measured distribution parameters of the lead–bismuth two-phase flow are much larger than that of ordinary two-phase flow regardless of the surface wettability. In the present work, the one-dimensional analysis was carried out for the cylindrical vessel to reproduce the distribution parameter. From the simulation results, predicted value for the cylindrical vessel showed good agreement with experimental results. However, in annulus, the distribution parameters in annulus were underestimated by the present model. It was suggested that, in case of annulus, steeper void fraction profile might be formed near the inner surface for poor wettability condition.     

化学复合镀法制备多孔光催化材料及其光催化性能

以多孔泡沫镍为载体,采用化学复合镀法制备了性能优良的多孔光催化材料,以产品对水中罗丹明B的降解性能为评价指标,对产品的光催化性能进行评价. 产品对水中罗丹明B的光催化降解反应严格符合零级动力学规律. 化学复合镀制备多孔光催化材料的最佳工艺条件为：镀液中硫酸镍浓度20 g/L,次亚磷酸钠浓度20 g/L,施镀过程中纳米TiO2投加量0.28 g/L,镀液温度90℃,镀液pH值4.6. 各因素影响产品性能的顺序为硫酸镍浓度>次亚磷酸钠浓度>镀液温度>镀液pH值>纳米TiO2投加量. 纳米Bi2O3复合使产品的光催化性能下降,随着纳米Bi2O3复合量增加,产品的光催化性能提高. ZnO复合使产品的光催化性能有明显改善,随着纳米ZnO复合量的增加,产品的光催化性能提高. Ag修饰导致Bi2O3复合光催化材料的光催化性能下降、ZnO复合光催化材料的光催化性能提高.     

Pb、Bi连续测定综合实验设计

对Pb、Bi连续测定中的Pb、Bi废液采用Na2S沉淀,HNO3溶解后配制成分析溶液,将原来的分析实验设计成集回收和测定于一体的综合实验,使Pb、Bi溶液可以循环利用,解决了废液排放造成的Pb污染和试剂消耗,实现了化学实验的绿色化,达到了综合训练的目的。     

2,4-二羟基苯甲酸铋对双基推进剂燃烧的催化作用

为了考察2,4-二羟基苯甲酸铋对双基推进剂燃烧的催化效果以及探索其催化作用机理,用螺压工艺制备了含2,4-二羟基苯甲酸铋的推进剂样品,研究了2,4-二羟基苯甲酸铋对双基推进剂燃烧的催化性能。结果表明,2,4-二羟基苯甲酸铋对双基系推进剂的燃烧具有良好的催化作用,能显著提高推进剂的燃速,并大大降低压力指数,与少量碳黑复合后,对提高推进剂的燃速效果更明显,铋盐、铜盐与碳黑三元复合后,催化效果更优。用快速热裂解固相原位池／傅里叶变换红外光谱（RSFT-IR）联用装置研究了2,4-二羟基苯甲酸铋的热分解机理,发现2,4-二羟基苯甲酸铋在催化推进剂燃烧过程中的活性组分为Bi2O3。