L12型Al3Ti合金室温变形超位错的分解及计算机图像模拟

利用透射电子显微镜和计算机图像模拟技术研究了ＬＩ２型Ａｌ３Ｔｉ合金室温变形的位错核心结构，结果表明：α（１１０）超位错在｛１１１｝面上分解成两个α／３｛１１２｝型超偏位错，其间为超点阵内禀层错。     

脉冲电流对Zn-42%Al合金定向凝固行为的影响

采用Zn-42%Al合金作为试验材料,研究不同电流强度和脉冲频率下脉冲电流对合金定向凝固组织的影响.结果表明,随着脉冲电流强度的增大,组织得到更加明显的细化;脉冲电流细化组织的作用对脉冲频率存在一个极限响应,当脉冲振荡频率过高,脉冲电流的细化组织效果会被削弱.     

Surface nitridation of titanium metal by means of a gas tunnel type plasma jet

The surface nitridation of titanium was carried out at a low pressure in nitrogen atmosphere using a gas tunnel type plasma jet. The titanium nitride (TiN) film, 10 μm thick and 2000 HV, could be formed in 10 s. The structure of the TiN film was investigated by XRD. The Vickers hardness on the surface of the film was measured. The effects of deposition conditions on the properties of TiN films (TiN thickness,Vickers hardness, etc.) were investigated, and the advantage of this deposition method was identified from those results.     

电脉冲改善金属材料组织的应用现状

综合评述了电脉冲作用下金属凝固过程、非晶结构的纳米晶化以及金属快速再结晶等方面的研究进展,着重介绍了电脉冲在材料加工过程中的作用机理.     

不同参数脉冲电流对不锈钢Cr18Ni9Ti凝固组织的影响

采用储能电容为1200μF的脉冲电源，在不同的脉冲电压下，对奥氏体不锈钢1Crl8Ni9Ti进行脉冲电流处理。实验结果表明：脉冲电流能够细化奥氏体不锈钢的凝固组织，使奥氏体一次枝晶长度缩短，二次枝晶间距减小。在一定范围内，脉冲电压升高和脉冲重复率增大都有利于奥氏体不锈钢凝固组织的细化和改善。     

纳米晶CuCr合金的制备及其截流值研究

通过高能球磨和真空热压技术制备了致密度大于98%的纳米晶CuCr合金,通过XRD,SEM和TEM研究了其显微组织和结构.结果表明,其晶粒尺寸小于50 nm.在模拟电路上研究了其真空电弧稳定性和截流值,纳米晶CuCr合金的真空电弧稳定性好于常规CuCr合金,其截流值为常规CuCr合金的17%～35%.     

孔隙性缺陷修复过程中材料扩散方式研究

孔隙性缺陷修复过程中, 由重结晶充满孔洞所需物质从基体材料中扩散而来, 材料的扩散能力对完成缺陷修复过程所需时间具有重要的影响。本文研究了孔隙性缺陷修复过程中材料扩散特性, 在不同温度条件下, 发现了至少存在着4种材料扩散方式, 其扩散能力相差较大。通过改变温度或加入其它物质, 扩散方式可以转变, 扩散速度能够得到控制, 这对于提高缺陷的修复能力, 有效消除大型锻件内部孔隙性缺陷具有重要作用。     

低压脉冲电场下纯铝的晶粒细化

研究了低压脉冲电场作用下纯铝凝固组织的变化，考察了放电电压和处理时间对纯铝晶粒尺寸的影响。结果表明：低压脉冲电场可以显著地细化纯铝的凝固组织。随着放电电压的提高，纯铝的晶粒尺寸逐渐减小；当放电电压达到400V时，晶粒尺寸略有回弹。随着处理时间的增加，纯铝的晶粒尺寸逐渐减小；当处理时间大于15min时，纯铝的晶粒尺寸随着处理时间的增加而略有增大。     

变阻抗电阻焊机的电流控制

本文根据阻焊过程中影响焊接回路阻抗变化的因素,引入了变阻抗电流控制环节,并建立起阻抗变化的数学模型和对应的变化曲线。还介绍了变阻抗电流控制的电路原理和应用范围。     

开关式TIG焊电源的焊接性能分析

本文建立了开关式ＴＩＧ焊电源的离散时域数学模型，分析了电弧引燃过程、引弧性能、电流波形特点和电弧稳定性。试验表明该电源具有良好的焊接性能。