Corrosion Behavior of 316LN and 316 Stainless Steels During Long-term Exposure to Aerated 0.5 M NaCl Using Electrochemical Noise Technique

In the present work 316LN as well as 316 stainless steel (SS) coupons each of dimensions (0.025 × 0.018 × 0.006 m³) in well-polished condition were used as two nominal electrodes which were immersed in the aerated solution of 0.5 M NaCl. Correlated current and potential electrochemical noise (EN) signals were collected at 1 Hz sampling frequency for 1 h daily over a period of 30 days. The detrended EN data were used to calculate the noise resistance (R _N) as well as the spectral noise resistance at zero frequency (R _SN^o) values and other statistical parameters. To study the nature of pits and distribution of their diameters as well as depths, extensive observations of the pitted and the blank specimens were carried out using Confocal Laser Scanning Microscopy (CLSM). The current and the potential records of the two alloys showed distinct differences in their corrosion behavior. It was observed that within less than 4 h of immersion, 316SS showed signals indicative of unstable pitting and onset of stable pitting was noticed after 48 h of exposure. However, until about 24 h, 316LN showed just the random signals and unstable pitting was observed after 28 h. The signals clearly indicated continuous growth of the stable pits in 316SS as against the repassivation of the unstable pits in 316LN after 7 days exposure. It was observed that R _N values showed a continuous decrease in the case of 316SS, but were quite stable in the case of 316LN over the exposure period. Concurrent to these observations it was observed that 316SS specimen was extensively pitted. The frequency distributions of pit diameters as well pit depths were observed to be highest at 10-20 μm and 5-10 μm, respectively. However, pits with as large as 70-80 μm diameter and as deep as 20-25 μm too were observed. No pits were observed in case of 316LN even after 30 days of exposure, an observation that corroborates well with the stable R _N values. Thus, in the present investigation, the long-term tests using EN technique coupled with CLSM studies conclusively prove that many unstable pits initiated in 316SS turn into stable ones resulting in insidious localized corrosion attack whereas the unstable pits initiated in 316LN get passivated in the simulated coastal environment.     

On-line corrosion monitoring in geothermal district heating systems. II. Localized corrosion

Corrosion monitoring in district heating systems has traditionally been performed by using off-line methods, such as weight loss. The disadvantage is that the method is very slow, especially in low-corrosive environments, and that it only provides information about the past corrosion (accumulated over period of time). The purpose of the work is to test on-line monitoring methods in geothermal hot water in the district heating system in Reykjavik, Iceland. Geothermal water poses certain problems with regards to corrosion monitoring due to low conductivity, high pH and the presence of sulphide. These conditions make the geothermal environment low corrosive. However, a quality control is needed, especially since the sulphide causes the steel pipes to be more vulnerable towards localized corrosion. The methods used in this study were: linear polarization resistance (LPR), harmonic analysis (HA), electrochemical noise (EN) and zero resistance ammetry (ZRA). The Pitting Factor was measured with EN and showed promising results for measuring-localized corrosion on-line. A crevice corrosion cell also gave good results but had a low lifetime. However, the results of a galvanic corrosion cell (Fe/Cu) proved more difficult to interpret since they were dependent both on the dissolved oxygen and the sulphide level.     

真空相变锅炉低排烟温度设计与低温腐蚀

真空相变锅炉是否会明显发生烟气低温腐蚀，一直众说不一。文章从锅炉发生低温腐蚀的机理人手，通过理论分析计算并通过实践检验，提出了真空相变锅炉虽然不能完全避免低温腐蚀问题，但不论排烟温度是否高于烟气露点，低温腐蚀的程度都很弱的观点；给出了真空相变锅炉沿烟气流程金属壁面的腐蚀速度与壁面温度的关系曲线，和烟气温度低于酸露点时金属壁面的腐蚀速度与壁面温度的关系曲线；同时，文章推荐真空相变锅炉的设计排烟温度取130℃左右的低排烟温度。根据上述观点设计的数百台产品已经过多年实际运行，未发现明显     

S135钻杆钢在钻井液中的氧腐蚀行为

基于系统的理论分析和现场腐蚀产物的XRD分析,揭示了S135钻杆钢在3%NaCl溶液中的氧腐蚀机理。为研究腐蚀因素与腐蚀速率的关系,通过室内高压釜动态模拟实验,分别研究了钻井液中含氧量、钻井液温度、钻井液流速和钻井液盐浓度对S135钻杆钢的氧腐蚀速率影响规律。实验研究结果表明(1)3%NaCl盐水钻井液对S135钻杆钢的腐蚀主要是氧去极化作用所致;(2)钻井液含氧量和钻井液流速的增加会加快钻杆钢的氧腐蚀速率,而钻井液温度和含盐量对钻杆钢的氧腐蚀速率具有双重作用。     

浅析露天栈桥改造

结合工程实例，论述了露天栈桥产生裂缝和腐蚀的原因，对栈桥结构进行了评价，提出了加固方案及加固施工中应注意的事项，经使用证明，加固效果良好。     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     

化学镀Ni-P合金/TiO2复合膜的耐蚀性研究

在改进常规制备方法的基础上，提出化学镀/溶胶-凝胶复合法在碳钢表面制备TiO2复合膜的新技术。用衍射研究了复合膜的组织形态，采用环境扫描电镜（ESEM）表征了复合膜的表观和断面形貌，用极化电阻、阳极极化曲线测量等方法研究TiO2复合膜在0.5mol/L硫酸和0.5mol/L氯化钠溶液中的耐蚀性能。结果表明A3钢表面的TiO2复合膜耐蚀性能优良。     

快速评定砂浆配方对钢筋腐蚀的影响

用电化学方法测定砂浆试件中钢筋的极化电阻，并测定了砂浆的孔隙率，结果发现:砂浆的孔隙率、孔径分布与钢筋极化电阻大小有良好的对应关系。电化学方法能可靠、快速测定砂浆配合比、添加剂对钢筋腐蚀速度的影响。     

低压铝箔交流腐蚀研究

在３０Ｈｚ频率下，通过铝箔在ＨＣｌ＋Ｈ２ＳＯ４＋ＨＮＯ３＋Ｈ３ＰＯ４体系中的交流腐蚀，研究腐蚀液组成中腐蚀主体及缓蚀剂对铝箔腐蚀的作用，探讨腐蚀过程中电源频率、腐蚀液温度、电流密度及腐蚀时间对铝箔腐蚀的影响。腐蚀液组成的配比恰当，有利于比容的提高。在特定的频率下采用合适的腐蚀液温度、适宜的电流密度和腐蚀时间可以提高铝箔的静电容量。     

几种高强度钢腐蚀疲劳裂纹扩展行为的研究

本文研究了ＧＣ－４，３０ＣｒＭｎＳｉＮｉ２Ａ和３００Ｍ超高强钢的腐蚀疲劳裂纹扩展行为。考虑了环境，热处理制度，应力比和频率对裂纹扩展的影响。研究结果表明：腐蚀环境和热处理制度对疲劳裂纹扩展有显著影响。在侵蚀性环境中随频率降低，裂纹扩展大幅度上升，随应力比提高，环境影响加剧。利用扫描电镜对试样断口形貌进行了分析，并讨论了高强钢的腐蚀疲劳机理。