Remarkably enhanced energy storage properties of lead-free Ba0.53Sr0.47TiO3 thin films capacitors by optimizing bottom electrode thickness

The lead-free Ba_0.53Sr_0.47TiO₃ (BST) thin films buffered with La_0.67Sr_0.33MnO₃ (LSMO) bottom electrode of different thicknesses were fabricated by pulsed laser deposition method on a (001) SrTiO₃ substrate. It was found that the roughness of electrode decreases and substrate stress relaxes gradually with the increase of LSMO thickness, which is beneficial for weakening local high electric field and achieving higher E_b. Therefore, the recoverable energy density (W_rec) of BST films can be greatly improved up to 67.3 %, that is, from 30.6 J/cm³ for the LSMO thickness of 30 nm up to 51.2 J/cm³ for the LSMO thickness of 140 nm after optimizing the LSMO thickness. Furthermore, the thin film capacitor with a 140 nm LSMO bottom electrode shows an outstanding thermal stability from 20 °C to 160 °C and superior fatigue resistance after 10⁸ electrical cycles with only a slightly decrease of W_rec below 1.6 % and 3.7 %, respectively. Our work demonstrates that optimizing bottom electrodes thickness is a promising way for enhancing energy storage properties of thin-film capacitors.     

Characteristics of tiger nut milk: effects of milling

A standard method for the extraction of tiger nut milk has been introduced. It has been shown that, although milling duration improves the yield of tiger nut milk solids and its nutrient composition, there is a quantifiable loss of nutrient in the pressing residue during milk extraction. Milling duration improved the colloidal stability of the milk against creaming during 16 h of storage. A higher milling intensity resulted in the aggregation of biological polymers which resulted in colloidal destabilisation. Milling improved the lightness and stability and reduced browning rate of the tiger nut milk during storage. This report is important for the production of tiger nut milk of consistent and comparable characteristics. Milling has been introduced as a processing method for the qualitative and quantitative modulation of the properties of tiger nut milk. It is recommended to develop further strategies to improve the colloidal stability of tiger nut milk as a beverage.     

Adaptive actuator failure compensation design for unknown chaotic multi‐input systems

In this paper, an adaptive control approach is designed for compensating the faults in the actuators of chaotic systems and maintaining the acceptable system stability. We propose a state‐feedback model reference adaptive control scheme for unknown chaotic multi‐input systems. Only the dimensions of the chaotic systems are required to be known. Based on Lyapunov stability theory, new adaptive control laws are synthesized to accommodate actuator failures and system nonlinearities. An illustrative example is studied. The simulation results show the effectiveness of the design method. Copyright © 2014 John Wiley & Sons, Ltd.     

浅谈氯碱氢的一种深度脱水工艺

概述了氢的主要工业生产方法和实际应用,详细介绍了氯碱氢三级脱水工艺过程,并运用在线分析手段,准确显示了干燥过程中的氯碱氢水分含量变化规律。     

Modeling the effect of deep traps on the capacitance–voltage characteristics of p-type Si-doped GaAs Schottky diodes grown on high index GaAs substrates

Numerical simulation, using SILVACO-TCAD, is carried out to explain experimentally observed effects of different types of deep levels on the capacitance–voltage characteristics of p-type Si-doped GaAs Schottky diodes grown on high index GaAs substrates. Two diodes were grown on (311)A and (211)A oriented GaAs substrates using Molecular Beam Epitaxy (MBE). Although, deep levels were observed in both structures, the measured capacitance–voltage characteristics show a negative differential capacitance (NDC) for the (311)A diodes, while the (211)A devices display a usual behaviour. The NDC is related to the nature and spatial distribution of the deep levels, which are characterized by the Deep Level Transient Spectroscopy (DLTS) technique. In the (311)A structure only majority deep levels (hole traps) were observed while both majority and minority deep levels were present in the (211)A diodes. The simulation, which calculates the capacitance–voltage characteristics in the absence and presence of different types of deep levels, agrees well with the experimentally observed behaviour.     

Quality and Emulsion Stability of Milk from Ettawah Crossed Bred Goat During Frozen Storage

Goat milk has specific chemical composition and physical properties. The purpose of this study was to investigate the change of milk quality and emulsion stability during 60 d frozen storage. Milk sample was taken from three Ettawah Crossedbred goats that were divided into three groups. Samples were frozen and stored for 0, 30 and 60 days. At the end of each storage periode, milk sample was thawed in the refrigerator and analyzed for total number of bacteria, chemical (acidity, pH, free fatty acids), physical (alcohol test, clot on boiling test) quality, and emulsion stability. The microbiological and chemical data were analyzed statistically using one way ANOVA, whereas physical quality and emulsion stabilty were expressed qualitatively. There were no change in the total bacteria, acidity, pH and free fatty acid (FFA) of milk during storage, whereas the assessment by 70% alcohol showed positive since 0 d. Emulsions stability changed after 30 d of storage. While, the clot on boiling (COB) test of milk was positive at 60 d of storage. Recommendation is frozen storage of goat milk should not longer than 30 d.     

Review on zirconate-cerate-based electrolytes for proton-conducting solid oxide fuel cell

The performance of low-to-intermediate temperature (400–800?°C) solid oxide fuel cells (SOFCs) depends on the properties of electrolyte used. SOFC performance can be enhanced by replacing electrolyte materials from conventional oxide ion (O^2-) conductors with proton (H⁺) conductors because H⁺ conductors have higher ionic conductivity and theoretical electrical efficiency than O^2- conductors within the target temperature range. Electrolytes based on cerate and/or zirconate have been proposed as potential H⁺ conductors. Cerate-based electrolytes have the highest H⁺ conductivity, but they are chemically and thermally unstable during redox cycles, whereas zirconate-based electrolytes exhibit the opposite properties. Thus, tailoring the properties of cerate and/or zirconate electrolytes by doping with rare-earth metals has become a main concern for many researchers to further improve the ionic conductivity and stability of electrolytes. This article provides an overview on the properties of four types of cerate and/or zirconate electrolytes including cerate-based, zirconate-based, single-doped cerate–zirconate and hybrid-doped cerate–zirconate. The properties of the proton electrolytes such as ionic conductivity, chemical stability and sinterability are also systematically discussed. This review further provides a summary of the performance of SOFCs operated with cerate and/or zirconate proton conductors and the actual potential of these materials as alternative electrolytes for proton-conducting SOFC application.     

A new perspective of co-doping and Nd segregation effect on proton stability and transportation in Y and Nd co-doped BaCeO3

Bulk and surface properties of proton stability and transportation in Y and Nd co-doped BaCeO₃ (BCYN), especially the effect of Nd segregation, were investigated by first-principles calculations. Since the structure of doped BaCeO₃ at the operating temperature of proton-conducting has been unclear for a long time, we have summarized the latest experimental results and calculated the structure of the asymmetric BCYN for the first time. The results show that compared with Y, Nd doping promotes oxygen vacancy formation, however reduces proton stability. Our calculation can also provide a possible explanation for the formation of space charge layer at the grain boundary of doped BaCeO₃ in experiment. Unlike the stable Y in BCYN, Nd is calculated to be easily segregated, which can facilitate both proton hydration and proton transportation near the surface. Moreover, Nd segregation at the grain boundary is predicted to be beneficial for proton transportation between grains.     

Microstructural and electrical changes in Ca0.9R0.1CeNbMoO8 (R = Y,Sm, Nd,La) ceramics induced by rare-earth ion doping

Rare-earth ions doped Ca_0.9R_0.1CeNbMoO₈ (R = Y, Sm, Nd, La) ceramics have been successfully prepared by solid-state method, and their modifications to the microstructure and electrical properties are also investigated. The rare-earth ions doped ceramics exhibit the scheelite structure. With the increase in the radius of rare-earth ions, the lattice distortion and bond interaction will be enhanced, and the consistency of grain size will be reduced. The ceramics exhibit negative temperature coefficient (NTC) thermistor characteristics in the temperature range of 473 K-1273 K, and the activation energy decreases with the increase of the radius of rare-earth ions. Rare-earth ions doping can increase the content of Ce³⁺ ions and promote the conductivity of ceramics. Except for Sm³⁺-doped ceramics, the high-temperature aging rate of other ceramics is less than 2%. The existence of some metastable Sm²⁺ ions in Sm³⁺-doped ceramics not only increases the activation energy, but also reduces the high-temperature stability of the ceramics.