Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Methyltransferase Contingencies in the Pathway of Everninomicin D Antibiotics and Analogues

Everninomicins are orthoester oligosaccharide antibiotics with potent activity against multidrug-resistant bacterial pathogens. Everninomicins act by disrupting ribosomal assembly in a distinct region in comparison to clinically prescribed drugs. We employed microporous intergeneric conjugation with Escherichia coli to manipulate Micromonospora for targeted gene-replacement studies of multiple putative methyltransferases across the octasaccharide scaffold of everninomicin effecting the A₁, C, F, and H rings. Analyses of gene-replacement and genetic complementation mutants established the mutability of the everninomicin scaffold through the generation of 12 previously unreported analogues and, together with previous results, permitted assignment of the ten methyltransferases required for everninomicin biosynthesis. The in vitro activity of A₁- and H-ring-modifying methyltransferases demonstrated the ability to catalyze late-stage modification of the scaffold on an A₁-ring phenol and H-ring C-4’ hydroxy moiety. Together these results establish the potential of the everninomicin scaffold for modification through mutagenesis and in vitro modification of advanced biosynthetic intermediates.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Influence of SiC content on the oxidation of carbon fibre reinforced ZrB2/SiC composites at 1500 and 1650 °C in air

The microstructure and the oxidation resistance in air of continuous carbon fibre reinforced ZrB₂–SiC ceramic composites were investigated. SiC content was varied between 5–20?vol.%, while maintaining fibre content at ～40?vol.%. Short term oxidation tests in air were carried out at 1500 and 1650?°C in a bottom-up loading furnace. The thickness, composition and microstructure of the resulting oxide scale were analysed by SEM-EDS and X-Ray diffraction. The results show that contents above 15?vol.% SiC ensure the formation of a homogeneous protective borosilicate glass that covers the entire sample and minimizes fibre burnout. The scale thickness is ～90?μm for the sample containing 5?vol.% SiC and decreases with increasing SiC content.     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

Studying the effect of organo-modified nanoclay loading on the thermal stability,flame retardant,anti-corrosive and mechanical properties of polyurethane nanocomposite for surface coating

Clay polyurethane nanocomposite (CPN) coating films were fabricated by uniformly dispersing nanoclay, organically modified with 25–30 wt.% octadecylamine in varying concentrations up to 5 wt.%, in a commercial two component, glossy, acrylic aliphatic polyurethane using ultrasonication. Organo-modified nanoclay was characterized by X-ray diffraction (XRD). The dispersion of the nanoclay into the matrix was investigated by scanning electron microscopy (SEM). CPN coating films were characterized by thermogravimetric analysis (TGA), and flame retardant, corrosion resistance and mechanical properties were also investigated. The XRD measurement indicated that, the organo-modified nanoclay particles were mainly constituted of montmorillonite with traces of quartz and calcite also found to be present. The SEM analysis showed that the nanoclay layers were dispersed and intercalated into the polyurethane coating. Thermogravimetric analysis showed that incorporating 5 wt.% organo-nanoclay into polyurethane considerably enhanced the thermal stability and increased the char residue to 14.11 wt.% relative to 4.58 for the sample without organo-nanoclay (blank polyurethane). The limiting oxygen index (LOI) test revealed that incorporation of organo-nanoclay led to a further increase in LOI values, which indicate an improvement in flame retardancy properties. The corrosion resistance also improved and this improvement increases with increase nanoclay wt.%. The mechanical resistance measurements demonstrated that the gloss of the CPN coating films slightly decreased, although hardness, adhesion and impact resistance of the CPN coating films improved with the incorporation of the organo-nanoclay.     

Effect of in-situ formation of columnar mullite and pore structure refinement on high temperature properties of corundum casatbles

The effects of in-situ synthesis columnar mullite and pore structure on the hot modulus of rupture (HMOR), thermal shock resistance and corrosion resistance of corundum castables have been investigated in this paper. When 2% nano silica was added, the pore diameters of castables could be decreased to 15 nm (at 110 °C), 1 μm (1100 °C) and 6 μm (1500 °C), respectively. The corresponding reducing magnitude of pore size is 98.5%, 83.3% and 33.3%. The HMOR of castables fired at 1500 °C increased by 110% to 3.64 MPa. Furthermore, after three thermal shock cycles, the residual strength ratio of castables increased from 5.2% to 15.3%. A large amount of cross-distributed columnar mullite was formed between nano silica and α-Al₂O₃ by the two-dimensional nucleation mechanism, which remarkably enhanced the high temperature properties. The penetration index reduced from 30.86% to 19.88%, suggesting that smaller pore size and higher viscosity had a great influence to the penetration process.     

Effect of focused ion beam sample preparation on the phase composition of zirconia

The investigation of phase transformations in metastable ceramic systems such as zirconia often requires local phase analysis within the areas of interest. Electron backscatter diffraction is a suitable method in combination with focused ion beam sample preparation. The interaction between ion beam and sample has to be carefully considered. In case of metastable Y-PSZ and Mg-PSZ, phase transformations were observed after FIB preparation with 30?kV, 30?nA and 5° incidence angle. Damage was the dominating effect for angles of 72°. The expected local temperature increase due to the ion bombardment with 30?kV and 30?nA is 700?K for ZrO₂. Thus, the observed phase transformations can be explained on the basis of the temperature increase in the corresponding Y-PSZ phase diagram. In case of Mg-PSZ, the transition temperature is 1083?°C. The local temperature increase was obviously lower. The excitation energy for the observed phase transformation was smaller than expected from the phase diagrams of the thermodynamic equilibrium. Using 5?kV, 4.8?nA and 5° incidence angle, no phase transformations and no damage were observed. Thus, these conditions are well suited for the FIB preparation of metastable zirconia.