Study of alinite cement hydration by impedance spectroscopy

Two types of alinite cements, Mg-alinite and Zn-alinite, were synthesized using the reagent grade chemicals. Their hydration behavior was compared with ordinary Portland cement (OPC) using impedance spectroscopy (IS) and ²⁹Si nuclear magnetic resonance (NMR) spectroscopy. The bulk resistance in the IS spectra and the intensity ratio of the hydrous (Q₁ and Q₂) to anhydrous (Q₀) phases in the NMR spectra were estimated as the extent of hydration. The results obtained from both techniques were consistent each other. Mg-alinite had a comparable hydration rate to OPC and Zn-alinite exhibited faster hydration kinetics than Mg-alinite.     

Ru-doped nanostructured carbon films

Pure and Ru-doped carbon films are deposited on Si (100) substrates by electron cyclotron resonance chemical vapor deposition. The films are characterized by transmission electron microscopy, electron energy loss spectroscopy, energy dispersive X-ray spectroscopy and atomic force microscopy. In both the pure and Ru-doped samples, diamond nanocrystallites are formed in amorphous carbon matrices. The Ru-doped film contains much smaller diamond nanocrystallites (approx. 3 nm) than the pure samples (approx. 11 nm). Lower surface roughnesses are observed in both pure and Ru-doped samples as compared to other reported nanocrystalline diamond films. The conductivity of the Ru-doped film is significantly higher than that of the pure film. The results show that Ru-doped nanocrystalline diamond films have unique structures and properties as compared to pure nanocrystalline diamond films or metal doped diamond-like carbon films, which may offer advantages for electrochemical, optical-window, field emission or tribological applications.     

几种光谱方法(FTIR、FT-Raman,NMR)在橡胶分析中的应用

综述了傅里叶变换红外光谱 ,傅里叶变换拉曼光谱以及核磁共振波谱在橡胶结构的定性、定量分析中的应用     

用固体核磁技术分析PE 100管材料的抗熔垂性

用固体核磁技术分析了2种具有不同抗熔垂性能的聚乙烯管材料的凝聚态结构与流变性能。管材树脂的抗熔垂性能与其核磁迟豫特性紧密相关,好的抗熔垂性能对应更长的纵向迟豫时间。抗熔垂性能好的双峰管材料的重均分子量更高,高相对分子质量部分的含量更多。     

Synthesis and characterization of soluble (porphyrinato)iron(II) polymers

The use of (tetrakis(4-hexylphenyl)porphyrinato)Fe(II) in polymerization reactions with bidentate ligands such as 9,10-diisocyanoanthracene and 1,4-diisocyanobenzene led to well-defined stacked polymers1 and2 which are still soluble in common organic solvents such as chloroform, dichloromethane, and tetrahydrofurane. They have been completely characterized by¹H-NMR and UV/vis spectropscopy in solution, even allowing end-group analysis for determination of the average degree of polymerization, yieldingn=10 andn=5 for1 and2, respectively. Mößbauer and IR spectroscopy further established the strong Fe-CN bonding reflected by very small isomer shifts and quadrupole splittings (E _Q0.2 mm s^–1) and a large decrease in the IR stretching frequency (v _CN60 cm^–1). The axially stacked polymers exhibit semiconducting properties only upon doping.Presented at the 5th International Symposium on Macromolecule-Metal Complexes (MMV), Summer 1993 in Bremen, Germany.     

Surface plasmon resonance evaluation of various aminoglycoside-RNA hairpin interactions reveals low degree of selectivity

Aminoglycoside antibiotics, which are able to selectively bind to RNA, are considered to be an important lead in RNA-targeting drug discovery. In this study, surface plasmon resonance (SPR) was employed to explore the interaction of aminoglycosides with known tobramycin-binding RNA hairpins (aptamers) and an unrelated RNA hairpin. It was established that aminoglycosides have multiple interactions with RNA hairpins. Unexpectedly, the different hairpins showed comparable affinity for a set of related aminoglycosides. The observed absence of selectivity presents an extra hurdle in the discovery of novel aminoglycosides as specific drugs that target defined RNA hairpins.     

Chaos in parametric resonance flow at water-mercury interface

In the electrochemical system with liquid-liquid interface, intense local convections by the resonance with potential pulses take place. Therefore, with laser beam scattering, temporal movement of the water-mercury interface was observed. As a result, the scattering efficiency showed non-linear oscillation.

Such non-linear response could be controlled by potential pulse height. As the potential height was increased, new scattering peaks in the oscillation emerged, which was expected of a kind of bifurcation phenomenon. From these results, phase portrait, Poincarè section, correlation dimension of the strange attractor and the largest Lyapunov exponent of the trajectories were obtained. Consequently, it was concluded that all the parameters indicate chaotic behavior of the resonance flow.     

Enhancement in magnetic permeability of Ni-Co-Zn ferrites using CuO doping for RF and microwave devices

Novel soft magnetic ferrite materials will play a crucial role in next-generation trillion-dollar sensor technologies related to 5G communications and internet of things as these materials can achieve improved wireless power/signal transfer efficiency with high operation frequency. In this work, Ni_0.4Co_0.25Zn_0.35Fe₂O₄ ferrites with high permeability and low magnetic loss were prepared for RF and microwave device applications. Composition and microstructure control is crucial to obtain the desired magnetic and loss properties. CuO dopant (x = 0 wt% to 20 wt%) were employed during the synthesis of Ni_0.4Co_0.25Zn_0.35Fe₂O₄ ferrite specimens to modify the microstructures, thus improving the magnetic properties of the ferrites. High value of measured relative permeability (μ’ of 4-10) and relatively low magnetic loss tangent ( of 0.01-0.1) has been achieved at frequency range between 100 and 800 MHz. Addition of CuO, especially up to 3 wt%, can cause a significant increase in permeability. Real part of the permeability of 3.87 and 10.9 has been achieved for undoped and 3 wt% CuO doped specimens, while noticeable reduction in magnetic losses has been observed for the doped sample measured at 400 MHz. The resonance frequency of synthesized ferrites has also been shifted into GHz range, when higher concentration of CuO dopants (>5 wt%) were employed.     

EPR study of hydrogen-related defects in boron-doped p-type CVD homoepitaxial diamond films

Boron-doped p-type single crystalline chemical vapor deposition (CVD) homoepitaxial diamond films were investigated by electron paramagnetic resonance (EPR). Carbon dangling bond defects, which were accompanied by a nearby hydrogen atom, were observed in boron-doped p-type CVD diamond films on a IIa substrate similar to those observed in undoped diamond. This result suggested that the energy level position of the defects is located below the Fermi energy of boron-doped diamond, at around 0.3 eV above the valence-band top. The reason why the Fermi energy could be changed by the incorporation of boron atoms at low density (10¹⁶–10¹⁷/cm³) in the film in spite of the existence of the large defect density of EPR centers (10¹⁸/cm³) is thought to be that the singly occupied electron states of defects are located near the band edge. As for the thermal annealing effect of the defects, it was revealed that the concentration of the defects and the mobility of the p-type film did not change after annealing up to 1200 °C which is much higher than the temperature of boron–hydrogen pair dissociation.     

Variable temperature13C MAS NMR of KFe2Mn(CO)12 in the solid state and as aCatalyst precursor on a carbon support

Variable temperature¹³C MAS NMR spectra are reported for¹³CO-enriched KFe₂Mn(CO)₁₂ as a solid and also as dispersed clusters on a carbon support. The spectrum of KFe₂Mn(CO)₁₂ at 300 K agrees with the proposed structure for this cluster and shows that the cluster is static. Two bridging carbonyl resonances are clearly resolved and, by comparison with¹³C MAS NMR spectra of Mn₂(CO)₁₀ and Fe₂(CO)₉, all terminal resonances for the cluster can be assigned. When the cluster is supported on carbon, two broad resonances are observed at room temperature which are assignable to KFe₂Mn(CO)₁₂ and a decomposition product, Mn₂(CO)₁₀. The carbonyl ligands in both supported clusters are completely averaged, and KFe₂Mn(CO)₁₂ on the carbon surface demonstrates fluxional behavior similar to that observed for the cluster in solution. For this fluxional process, activation energies of 0.6 kcal/mol and 0.5 kcal/mol are estimated for carbon-supported KFe₂Mn(CO)₁₂ and Mn₂(CO)₁₀, respectively.