Ennoblement of stainless steel in natural seawater – A new explanation

The ennoblement of corrosion potential (E_corr) of passive metal immersed in seawater was investigated with electrochemical technology and epifluorescence microscopy. The in situ observation showed that the bacteria number increased on the metal surface according to an exponential law which was in the same way with the ennoblement of E_corr. At the same time, the anodic polarization current of high‐Mo stainless steel decreased in the initial days. According to the mix‐potential theory and the characteristics of polarization curves of high‐Mo steel in natural seawater, the ennoblement of corrosion potential may be induced by the decrease of the passive current density.     

工业纯铝在模拟海水中的电化学腐蚀行为

为研究铝在海水中的腐蚀过程,采用电化学阻抗谱、浸泡试验、扫描电子显微镜研究工业纯铝在模拟海水中的腐蚀行为.结果表明:铝在模拟海水中发生点蚀的区域为富含Fe的晶间化合物处,点蚀半径随时间的增加而扩大.铝在模拟海水中的溶解曲线分为4个区间:活性溶解区、过渡区、过钝化区、钝化区.铝在模拟海水中,极化电位为过钝化区时,转移电阻R t随着电位的升高而变小,铝发生严重的点蚀;而极化电位为钝化区时,铝的转移电阻R t随着电位的升高基本不变,铝的溶解行为受到抑制.工业纯铝在模拟海水中发生点蚀的电位区间是-0.45～-0.65 V,钝化电位区间为-0.75～-0.85 V.     

舰用主汽轮机组在海水温度变化情况下最大工作能力分析

针对舰用主汽轮机组的工作环境特性,基于热力学和流体力学基本理论,建立冷凝器工作特性模型,并运用Matlab/Simulink进行求解,定量分析了海水温度变化对舰用冷凝器压力、主汽轮机组功率和舰船航速的影响。研究成果对如何充分发挥装备的最大使用效能,具有重要的指导意义。     

关于抽水蓄能电站水库优化调度的研究

针对某抽水蓄能电站水库运行的特点，在满足电力系统调度要求的前提下，以整个调度周期内总发电收益现值最大为目标建立了优化调度模型。通过径流描述以及应用动态规划法进行优化计算，求解抽水蓄能电站水库优化调度方案。在求解寻优的过程中，既兼顾了面临时段和余留时期的效益，又考虑上水库的天然来水和下水库的区间来水，通过分析表明，所提模型与计算方法是可行和实用的。     

用于海水反渗透淡化系统的能量回收器的实验研究

介绍了用于海水反渗透淡化系统的余压能量回收器的工作原理，建立了相应的实验装置，研究了能量回收器工作流体的流量和压力的变化规律，分析了其中的变化原因，为今后能量回收器的设计和优化提供可靠的依据．     

反渗透海水淡化技术应用

简要回顾了反渗透技术的发展过程及应用状况．针对国内典型反渗透海水淡化工程实例，分析了一期、二期不同工艺、设备的技术特点，并针对相关海域的海水水质介绍了海水预处理技术以及存在的问题．     

我国海水淡化的现状与钛的应用

海水淡化是解决人类水资源危机的重要途径。重点介绍了蒸发法中的多级闪蒸、多效蒸发,以及膜法中的反渗透海水淡化方法,并分析了各种方法的优缺点、现状和发展方向;总结了世界范围内各种海水淡化装置中钛的应用情况,讨论了与铜管相比,钛管的性能、成本等指标的优劣性,着重分析了今后海水淡化方法及钛在海水淡化中应用的发展方向。分析认为,今后海水淡化产业在世界范围内的发展将更加迅速,中国也将成为海水淡化产业发展的主要市场之一;随着"十二五"规划对今后海水淡化原材料、装备制造自主创新率的明确要求,国产钛材在海水淡化产业中的应用必将迎来新的发展机遇。     

Corrosion behaviour of hot dip zinc and zinc-aluminium coatings on steel in seawater

A comparative investigation of hot dip Zn-25Al alloy, Zn-55Al-Si and Zn coatings on steel was performed with attention to their corrosion performance in seawater. The results of 2-year exposure testing of these at Zhoushan test site are reported here. In tidal and immersion environments, Zn-25Al alloy coating is several times more durable than zinc coating of double thickness. At long exposure times, corrosion rate for the Zn-25Al alloy coating remains indistinguishable from that for the Zn-55Al-Si coating of similar thickness in tidal zone, and is two to three times lower than the latter in immersion zone. The decrease in tensile strength suggested that galvanized and Zn-55Al-Si coated steel suffer intense pitting corrosion in immersion zone. The electrochemical tests showed that all these coatings provide cathodic protection to the substrate metal; the galvanic potentials are equal to −1,050, −1,025 and −880 mV (SCE) for zinc, Zn-25Al alloy and Zn-55Al-Si coating, respectively, which are adequate to keep the steel inside the immunity region. It is believed that the superior performance of the Zn-25Al alloy coating is due to its optimal combination of the uniform corrosion resistance and pitting corrosion resistance. The inferior corrosion performance by comparison of the Zn coating mainly results from its larger dissolution rate, while the failure of the Zn-55Al-Si coating is probably related to its higher susceptibility to pitting corrosion in seawater.     

反渗透海水淡化技术最新研究动态

从降低海水反渗透淡化产水成本和环境友好过程的开发两个方面探讨了国内外海水反渗透淡化技术的最新研究成果和应用情况，包括能量回收器的研究、新型工艺过程的设计、海水反渗透膜的研究和应用、用膜法预处理代替传统化学器预处理以及NF—SWRO—MSF过程集成5个部分．     

氧化锌超疏水薄膜的制备及其耐久性

为了提高氧化锌(ZnO)纳米疏水膜层在实际应用中的耐久性能,采用水热法在铝基底表面制备出微纳米结构的ZnO超疏水薄膜,利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和接触角测量仪对所得ZnO薄膜的成分、微观结构及润湿性能进行分析;利用UMT摩擦磨损试验机对薄膜的摩擦性能和机械疏水耐久度进行研究;并用CHI660E电化学工作站对超疏水试样在海水中的耐腐蚀性能进行测量分析。结果表明:制备的微纳米结构ZnO薄膜具有超疏水性,在未经低表面能物质改性的情况下,对水的静态接触角高达152°,滚动角仅为2°;摩擦磨损测试表明该薄膜在经过2 400磨损周期后仍能保持较高的静态接触角;电化学阻抗谱和Tafel曲线测试表明,该薄膜的确降低了铝在海水中的腐蚀速率,缓蚀率高达93.8%。