低温球磨制备高热稳定性纳米晶Al-Zn-Mg-Cu合金块体材料

利用液氮球磨和真空热压技术制备纳米晶Al-10Zn-3Mg-1.8Cu(质量分数,%)合金块体材料。采用X射线衍射(XRD)和透射电镜(TEM)对材料在制备过程中的固态相变、晶粒尺寸和热稳定性进行分析。结果表明,材料经过液氮球磨15 h后晶粒尺寸为37 nm,真空热压后材料晶粒保持在100 nm,热挤压后晶粒尺寸约为300 nm,热处理后晶粒尺寸保持不变。材料的高热稳定性原因在于大量合金元素和杂质元素超饱和固溶于Al基体中阻止了晶粒的长大,以及细小析出MgZn2相和Al2O3颗粒对于晶界的钉扎作用。     

Manufacturing a TiAl alloy by high-energy ball milling and subsequent reactive sintering

A TiAl alloy was fabricated by high-energy ball milling and subsequent reactive sintering from the mixed powders of Ti and Al. High-energy ball milling produced a kind of particular composite powders with an extremely fine altemative Ti and Al lamella structure. The composite powders not only possessed good consolidation and densification characteristics, but also resulted in the augment of nucleation rate of α and γ titanium aluminides during solid-phase reactive sintering After a series of processing, pressing, degassing, extrusion, and sintering, the resultant TiAl alloy presented high relative density and refined grain sizes of （α2 ＋ γ） lamella and γ phases. The compressive yield strength of the sintered TiAl reached 600 MPa at 800℃.     

TA15钛合金接头活性剂补焊的组织特征

采用现代测试手段分析TA15钛合金活性剂补焊接头微观组织特征,探讨钛合金焊缝采用活性剂多次补焊的可行性.结果表明:涂有活性剂补焊接头各区域结合良好,热影响区域小且与焊缝区过渡平缓,没有出现明显分界;涂活性剂焊缝区晶内组织并未因补焊次数的增加而粗大;焊缝接头主要元素Ti、Al、Mo、V和Zr均分布均匀,没有因采用活性剂而出现烧损和偏聚的现象;室温下补焊焊缝组织由α-Ti组成;涂活性剂焊缝各补焊区硬度值接近,略低于正常焊缝区硬度.采用活性剂对钛合金可以进行多次补焊并能够获得高质量焊缝.     

镁合金的活性电弧焊接

在不同的电流条件下,研究了9种常见氧化物、氟化物、氯化物活性剂在镁合金交流氩弧焊及变极性等离子焊弧中的行为.结果表明:活性剂TiO2、Cr2O3、AlF3、NiCl2、CdCl2、ZnCl2、MgCl2使镁合金交流氩弧焊焊缝熔深增加;MgF2、SiO2使镁合金交流氩弧焊焊缝熔深减小;TiO2、SiO2、Cr2O3、AlF3、NiCl2、CdCl2使镁合金变极性等离子弧焊焊缝熔深增加;MgF2、ZnCl2、MgCl2使镁合金变极性等离子弧焊焊缝熔深减小;活性剂对镁合金交流氩弧焊焊缝熔深增加的作用大于对镁合金变极性等离子弧焊的;电弧收缩是活性剂使得镁合金电弧焊焊缝熔深增加的原因之一;活性剂的加入使得焊缝的晶粒比未涂敷活性剂时粗大.     

半固态Y112铝合金成形组织与性能

采用近液相线半连续多模铸造法制备出Y112铝合金半固态坯料。分别考察了半固态合金流变成形件、触变成形件和常规压铸件的组织与性能。结果表明：Y112铝合金的半固态流变成形件的组织细小、均匀，硬度为112HV，优于触变成形件和常规压铸件的。     

化学镀Ni-P合金在铝合金剑杆头上的应用

采用化学镀工艺方法在铝合金剑杆头表面镀一层Ni-P合金，代替进口的剑杆头。对铝合金剑杆头的预处理工艺、镀液的配方、施镀工艺以及镀后热处理工艺进行了研究，确定了简便易行的施镀工艺及镀后热处理工艺。所确定的镀液配方，性能稳定，可获得40μm以上厚度的镀层，且镀层与基体的结合力较好，其硬度可达1100HV以上，其 综合性能与进口件相当。     

Effect of grain size on high-temperature oxidation behavior of Cu-80Ni alloy

1　INTRODUCTIONTheoxidationofunalloyedcopperandnickelhasalreadybeenstudiedindetail.Whilethehigh tem peratureoxidationofCu Nialloys ,alsostudiedanumberoftimestodate[13] ,isanexampleofarela tivelysimpleclassofscalingofbinaryalloysbyasin gleoxidant,becausethemetalsformacontinuousse riesofsolidsolutions ,whiletheiroxides ,CuO ,Cu2 OandNiO ,exhibitsmallmutualsolubilitiesandshowsignificantdifferencesinthethermodynamicstabilityandparabolicgrowthrates .Thus ,copper richalloysformexternalscales…     

成形参数对AZ91D镁合金触变成形性与缺陷形成的影响

研究了不同成形工艺参数,如坯料加热温度、加热时间和模具预热温度(模具温度)对AZ91D镁合金触变成形性与缺陷形成的影响。结果表明:成形性、缺陷形成与加工参数紧密相关。合适的成形参数为:坯料加热温度在575～595℃,加热时间超过75min,模具预热温度超过275℃;主要有冷隔、液相偏析、缩松、裂纹和氧化夹杂5种缺陷。其中,裂纹和氧化夹杂是主要的缺陷。     

IN-SITU OBSER VATION OF SINGLE-POINT WEAR OF PM Al-Ti ALLOY

ＩＮＳＩＴＵＯＢＳＥＲＶＡＴＩＯＮＯＦＳＩＮＧＬＥ－ＰＯＩＮＴＷＥＡＲＯＦＰＭＡｌＴｉＡＬＬＯＹ①ＷｕＪｉｎｍｉｎｇ，ＷｕＮｉａｎｑｉａｎｇ，ＷａｎｇＧｕａｎｇｘｉｎ，ＬｉＺｈｉｚｈａｎｇＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａｌｓＳｃｉｅｎｃｅａ...     

超低碳不锈钢冷轧（拔）无缝钢管生产工艺改进

介绍了采用Φ８０ｍｍ超低碳不锈钢轧坯经扒皮、穿孔、冷轧（拔）生产Φ５７ｍｍ以下成品管的工艺改进、新工艺要点，并对新工艺效果进行了浅析。