稀土La对45Cr2NiMoVSi热作模具钢力学性能的影响

研究了稀土La对45Cr2NiMoVSi钢的强度、硬度、塑性和冲击韧度的影响。在相同的热处理工艺条件下,分别加入3种不同含量的稀土La,与不添加稀土La的45Cr2NiMoVSi钢的力学性能进行对比。结果表明：稀土La加入量在适当的范围内可显著提高45Cr2NiMoVSi的力学性能,稀土La加入量为0.20%（质量分数）时,45Cr2NiMoVSi钢可获得最好的综合力学性能。     

Microstructural Investigation of Protective and Non-Protective Oxides on 11% Chromium Steel

FIB, SEM and STEM/EDX were used to investigate X20 stainless-steel samples exposed to dry O₂, or O₂ containing 40% H₂O, with a flow velocity of 0.5 cm/s or 5 cm/s, for 168 hr or 336 hr at 600°C. Thin protective Cr-rich (Cr,Fe)₂O₃ was maintained on the samples exposed to dry O₂, even after 336 hr, and on the sample exposed to O₂/H₂O mixture with the low-flow velocity (0.5 cm/s) for 168 hr. The oxide scale formed in the latter environment contained less Cr, due to Cr loss through CrO₂(OH)₂ evaporation. Breakaway oxidation occurred on the samples exposed in high-gas-flow velocity for shorter time (168 hr) or in low-gas-flow velocity (0.5 cm/s) for longer time (336 hr). The breakaway scales featured a two-layered structure: an outward-growing oxide “island” consisting of almost pure hematite (α-Fe₂O₃), and an inward-growing oxide “crater” consisting of (Cr,Fe)₃O₄. The transition from a thin protective (Cr,Fe)₂O₃ scale to a non-protective thick scale on this martensitic/ferritic steel originated locally and was followed by rapid oxide growth, resulting in a thick scale that covered the whole sample surface.     

The Effect of Intensity Pulsed Ion Beam Irradiation on Wear Resistance of High-speed Steel

INTENSITY pulsed ion beam(IPIB)technology hasbeen developed over the last two decades primarily fornuclear fusion and high-energy density physicsresearch,which is also named as high-intensity pulsedion beam technology(HPIB)and becomes a newmodification technique of materials surface such as inthe fields of metal materials modification,functionalfilms and nano-powder synthesis[1-5].Directdeposition of a beam into a solid surface results in arapid melt and resolidification with heating and…     

国内外不锈钢精炼剂研究发展现状

分析了精炼剂组元元素的作用能力，讨论并总结了精炼剂组元的复合作用，介绍了几种国内、国外精炼剂产品，提出发展高效复合精炼剂的想法。     

高强钢焊接区“三点弯曲”试验拘束应力的测定

采用“三点弯曲”试验对HQ130高强钢焊接熔合区附近的应力状态进行了试验测定。试验结果表明，外加载荷增大，焊接试样的应力应变值逐渐增大，经过近似直线的弹性范围后，达到塑变区后应变发生突变。外加载荷增加使产生裂纹的可能性增大。尽管应变的公式计算值和实测值之间存在着一定的偏差，但二者的总体趋势是一致的，在要求不太严格或只要求获得应力变化规律的情况下，仍可用公式法估算。     

SLOW PROPAGATION OF FATIGUE CRACK NEAR THRESHOLD

The effect of pearlite interlamellar spacing(d)from 0.31 to 0.77 μm of T8 steel on fatiguecrack propagation near threshold has been investigated at different stress ratios(R).Theclosure stress intensity factor(K_(cl)),the threshold value(ΔK_(th))and crack tip opening dis-placement range(ΔCOD)were measured.The results show that pearlite interlamellar spac-ing in this range has no effect on K_(cl),but has effect on the threshold value in low stress ratio.The threshold value is higher for materials with larger interlamellar spacing.No matter whatthe stress ratio is,during the propagation near threshold,the propagation rate will be thesame,provieded the crack tip opening displacement range is the same.Metallurgical examinations were also carried out to show that the crack propagationpath is sensitive to mierostructure.The crack always propagates along either boundary ofpearlite colony or ferrite lamellar in pearlite.     

热变形对合金钢A_（e3）影响的热力学计算

以超组元（Ｓｕｐｅｒｅｌｅｍｅｎｔ）模型为基础，开发了计算热变形后Ｆｅ－ΣＸ_ｉ－Ｃ（Ｘ_ｉ＝Ｍｎ，Ｓｉ，Ｍｏ，Ａｌ，Ｃｕ，Ｎｉ，Ｃｏ，Ｃｒ等）多组元合金钢的Ａ（ｅ３）的方法，并着重分析了γ相热变形对Ａ（ｅ３）的影响，未变形合金钢Ａ（ｅ３）的计算值，与前人的实测值基本符合．     

321不锈钢点蚀电位影响因素的研究

通过正交设计和对比实验研究了温度、pH值以及Cl-和SO2-4含量对321不锈钢点蚀电位的影响.正交设计表明,温度和Cl-(Cl-≥0.014mol/L)含量对点蚀电位Eb的影响显著,但pH值(6～9)则没有影响.对比实验表明,当Cl-≤0.014 mol/L时,Cl-对Eb没有影响,当Cl-＞0.014 mol/L,则Eb随Cl-浓度对数升高而线性下降.点蚀电位随温度升高而下降.如不含Cl-,则SO2-4对Eb没有影响,当Cl-=0.028 mol/L时,Eb随SO2-4浓度升高而升高,并趋于稳定值.